CN103922569A - Glass pouring and forming method - Google Patents
Glass pouring and forming method Download PDFInfo
- Publication number
- CN103922569A CN103922569A CN201410161077.7A CN201410161077A CN103922569A CN 103922569 A CN103922569 A CN 103922569A CN 201410161077 A CN201410161077 A CN 201410161077A CN 103922569 A CN103922569 A CN 103922569A
- Authority
- CN
- China
- Prior art keywords
- coloured glaze
- forming method
- built
- froth breaking
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass pouring and forming method, which comprises the following steps: designing an appearance, manufacturing a silica gel mold, producing a wax mold, duplicating a plaster mold, preheating the molds, pouring glass, insulating and defoaming, cooling and demolding and polishing and checking. Through the mode, the glass pouring and forming method has the advantages of high reliability, fast machining speed, high finished product quality, low manufacturing price, good ornamental values and the like, is easy to automate and suitable for assembling of line production, and has wide market prospects on the glass manufacturing market.
Description
Technical field
The present invention relates to coloured glaze and manufacture field, particularly relate to a kind of coloured glaze and build forming method.
Background technology
Coloured glaze, is one of China Han traditional handicraft product, with versicolor synthetic quartz be raw material, adopt the Ancient Bronze lost wax casting method high temperature crystal works that form that dewax.Its color stream cloud drench coloured silk, Meron U.S., quality is glittering and translucent, bright and glittering, existing manufacturing process of coloured glaze, for stained glass is stacked according to processing requirement, is sent in kiln and is fired afterwards, and coloured glaze color is glass flow self-assembling formation, because coloured glaze is amorphous material, and melt temperature is higher, for coloured glaze material thoroughly being melted and being packed in mould, often need firing for a long time, expend the energy, and it is not high to manufacture efficiency.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of coloured glaze and builds forming method, realizes the manufacture of coloured glaze by the mode of building, simple and quick; By mould and die preheating is incubated, mobility when raising coloured glaze is built, avoids bubble formation; After building, carry out froth breaking, improve coloured glaze quality; There is the advantages such as reliability is high, process velocity fast, be easy to automatization, be applicable to streamline production, final product quality is high, and manufacturing price is cheap, sight is good, on coloured glaze manufacturing market, have market outlook widely simultaneously.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of coloured glaze to build forming method, comprise: 1) carry out device configuration design and manufacture silica gel mould, 2) utilize silica gel mould make wax-pattern and turn over gypsum mold processed, 3) gypsum mold steam dewaxing is left to gypsum former, 4) gypsum mold is sent into holding furnace, and be heated to build temperature, 5) coloured glaze is built in gypsum mold, afterwards mould is sent into insulation froth breaking stove froth breaking, 6) coolingly rear coloured glaze is removed to mould, 7) remove unnecessary coloured glaze material and otch is polished and eliminated manufacturing defect simultaneously.
In a preferred embodiment of the present invention, described holding furnace temperature is 1000-1200 DEG C.
In a preferred embodiment of the present invention, described froth breaking stove froth breaking temperature is 1400 DEG C of left and right, and described foam time is 2-4 hour.
In a preferred embodiment of the present invention, it is 1400-1450 DEG C that described coloured glaze is built temperature.
In a preferred embodiment of the present invention, described elimination manufacturing defect comprises to be removed the gypsum material embedding and transparent resin is filled in cavity.
The invention has the beneficial effects as follows: coloured glaze of the present invention is built forming method and realize by the mode of building the manufacture of coloured glaze, simple and quick; By mould and die preheating is incubated, mobility when raising coloured glaze is built, avoids bubble formation; After building, carry out froth breaking, improve coloured glaze quality; There is the advantages such as reliability is high, process velocity fast, be easy to automatization, be applicable to streamline production, final product quality is high, and manufacturing price is cheap, sight is good, on coloured glaze manufacturing market, have market outlook widely simultaneously.
Embodiment
To the technical scheme in the embodiment of the present invention be clearly and completely described below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiment.Based on the embodiment in the present invention, those of ordinary skill in the art, not making all other embodiment that obtain under creative work prerequisite, belong to the scope of protection of the invention.
The embodiment of the present invention comprises:
A kind of coloured glaze is built forming method, comprise: 1) carry out device configuration design and manufacture silica gel mould, 2) utilize silica gel mould make wax-pattern and turn over gypsum mold processed, 3) gypsum mold steam dewaxing is left to gypsum former, 4) gypsum mold is sent into holding furnace, and be heated to build temperature, 5) coloured glaze is built in gypsum mold, afterwards mould is sent into insulation froth breaking stove froth breaking, 6) coolingly coloured glaze is removed to mould, 7 afterwards) remove unnecessary coloured glaze material and otch is polished and eliminated manufacturing defect simultaneously.
Described holding furnace temperature is 1000-1200 DEG C, makes the effective preheating of mould, crosses quick setting while avoiding building.
Described froth breaking stove froth breaking temperature is 1400 DEG C of left and right, and described foam time is 2-4 hour, can effectively remove bubble, improves coloured glaze quality.
It is 1400-1450 DEG C that described coloured glaze is built temperature, makes coloured glaze liquid have good mobility, conveniently builds normally and carries out.
Described elimination manufacturing defect comprises to be removed the gypsum material embedding and transparent resin is filled in cavity, improves final product quality.
The beneficial effect that coloured glaze of the present invention is built forming method is:
One, realize the manufacture of coloured glaze by the mode of building, simple and quick;
Two,, by mould and die preheating is incubated, mobility when raising coloured glaze is built, avoids bubble formation;
Three, carry out froth breaking after building, improve coloured glaze quality;
Four, there is the advantages such as reliability is high, process velocity fast, be easy to automatization, be applicable to streamline production, final product quality is high, and manufacturing price is cheap, sight is good, on coloured glaze manufacturing market, have market outlook widely simultaneously.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes description of the present invention to do; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. a coloured glaze is built forming method, it is characterized in that, comprise: 1) carry out device configuration design and manufacture silica gel mould, 2) utilize silica gel mould make wax-pattern and turn over gypsum mold processed, 3) gypsum mold steam dewaxing is left to gypsum former, 4) gypsum mold is sent into holding furnace, and be heated to build temperature, 5) coloured glaze is built in gypsum mold, afterwards mould is sent into insulation froth breaking stove froth breaking, 6) coolingly coloured glaze is removed to mould, 7 afterwards) remove unnecessary coloured glaze material and otch is polished and eliminated manufacturing defect simultaneously.
2. coloured glaze according to claim 1 is built forming method, it is characterized in that, described holding furnace temperature is 1000-1200 DEG C.
3. coloured glaze according to claim 1 is built forming method, it is characterized in that, described froth breaking stove froth breaking temperature is 1400 DEG C of left and right, and described foam time is 2-4 hour.
4. coloured glaze according to claim 1 is built forming method, it is characterized in that, it is 1400-1450 DEG C that described coloured glaze is built temperature.
5. coloured glaze according to claim 1 is built forming method, it is characterized in that, described elimination manufacturing defect comprises to be removed the gypsum material embedding and transparent resin is filled in cavity.