CN104441354B - A kind of processing technology of electric candle mould - Google Patents
A kind of processing technology of electric candle mould Download PDFInfo
- Publication number
- CN104441354B CN104441354B CN201410628887.9A CN201410628887A CN104441354B CN 104441354 B CN104441354 B CN 104441354B CN 201410628887 A CN201410628887 A CN 201410628887A CN 104441354 B CN104441354 B CN 104441354B
- Authority
- CN
- China
- Prior art keywords
- candle
- rubber
- mold
- mold core
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of processing technology of electric candle mould, specifically includes and is fabricated to candle mold core of different shapes from metal, and carries out decorative pattern engraving on the surface of mold core；Frozen glue processing is carried out to silicon rubber at 150 DEG C from frozen glue machine, forms blob of viscose；Blob of viscose in step b is put into step a mold core, the die cast under 170 ~ 200 DEG C of high temperature, forms the rubber mold that thickness is 2 ~ 3mm；Rubber mold is taken out, wax liquor is poured into rubber mold at 120 DEG C, molding after 5 ~ 12h, so as to prepare the candle body of electric candle.
Description
Technical field
The present invention relates to a kind of processing technology, more particularly to a kind of processing technology of electric candle mould.
Background technology
Electric candle is a kind of new class candle, and it uses the candle body of candle and the candle wick of electronics, shaken with candle
Drag and while feel, reduce danger coefficient caused by candle, electric candle progressively turns into be adjusted in people's life
The essential article of atmosphere.
The candle body of in general electric candle is process by the way that wax liquor is poured into mould, and candle candle body is prepared good
The bad mould for being heavily dependent on processing.
Existing candle body die processing method is：The mold core of candle candle body shape is produced with mud, then outside
Painting is covered with silica gel, binds gypsum after air-drying in outside, forms candle mould, when processing candle candle body, takes out internal mud and makes
Mold core, wax liquor is poured into mould, formed candle.
Although this method can prepare candle candle body, but its candle candle body surface detail lines is unintelligible, does not allow
Easy molding, easy damaged candle body during taking-up so that yield rate is low, simultaneously for the candle of spheroid class, candle prepared by this mould
Body is yielding, and cost is high, while mould just has breakage, short life after using 40~50 times.
The content of the invention
The defects of it is an object of the invention to overcome prior art, there is provided a kind of processing technology of electric candle mould, can
Easily to prepare candle candle body, and candle body lines is clear, and without bubble, product is unlikely to deform, and candle does not need deburring.
To achieve the above object, the present invention proposes following technical scheme：
A kind of processing technology of electric candle mould, specifically comprises the following steps：
A. it is fabricated to candle mold core of different shapes from hard material；
B. refining glue processing is carried out to silicon rubber at 150 DEG C from rubber mixing machine, forms blob of viscose；
C. the blob of viscose in step b is coated on outside step a mold core, the die cast under 170~200 DEG C of high temperature,
Form the rubber mold that thickness is 2~3mm；
D. rubber mold is taken out, wax liquor is poured into rubber mold at 120 DEG C, molding after 5~12h, so as to prepare
The candle body of electric candle.
Hard material in the step a is metal, timber or ceramics.
Metal in the step a is aluminium, iron or copper.
The surface of the mold core carries out smooth treatment, wire drawing process or carving processing.
Compared with prior art, the processing technology for a kind of electric candle mould that the present invention discloses, whole mould process letter
It is single, and the mould prepared can be used effectively more than 200 times, cost is low, long lifespan, while the candle candle body surface of its processing
Lines is clear, without bubble, and can prepare any shape, seamless among the ball of preparation especially for ball candle body.
Embodiment
Clear, complete description will be carried out to the technical scheme of the utility model embodiment below.
A kind of processing technology for electric candle mould that the present invention discloses, it is mainly used in processing the processing of electric candle candle wick
Mould, specifically comprise the following steps：
A. candle mold core of different shapes is fabricated to from hard material, and is carried out as needed on the surface of mold core
Smooth treatment, either wire drawing process or carving processing；
B. refining glue processing is carried out to silicon rubber at 150 DEG C from rubber mixing machine, forms blob of viscose；
Blob of viscose in step b is coated on outside step a mold core, the die cast under 170~200 DEG C of high temperature, shape
Into the rubber mold that thickness is 2~3mm；
D. rubber mold is taken out, wax liquor is poured into rubber mold at 120 DEG C, molding after 5~12h, so as to prepare
The candle body of electric candle.
Hard material in the step a is metal, timber, the material of all hard such as ceramics, if from metal,
It is preferred that the material of aluminium, iron or copper as mold core.
The technology contents and technical characteristic of the present invention have revealed that as above, but those skilled in the art still may base
Make a variety of replacements and modification without departing substantially from spirit of the present invention, therefore, the scope of the present invention in teachings of the present invention and announcement
The content disclosed in embodiment should be not limited to, and should be included various without departing substantially from replacement of the present utility model and modification and special for this
Profit application claim is covered.
Claims (1)
- A kind of 1. processing technology of electric candle mould, it is characterised in that：Specifically comprise the following steps：A. iron block is fabricated to candle mold core of different shapes, the surface of the mold core carries out smooth treatment, wire drawing process Or carving processing；B. refining glue processing is carried out to silicon rubber at 150 DEG C from rubber mixing machine, forms blob of viscose；C. the blob of viscose in step b is coated on outside step a mold core, the die cast under 170~200 DEG C of high temperature, formed Thickness is 2~3mm rubber mold；D. rubber mold is taken out, wax liquor is poured into rubber mold at 120 DEG C, molding after 5~12h, so as to prepare electronics The candle body of candle.