CN103936260A - Double-layer colored glaze blowing method - Google Patents
Double-layer colored glaze blowing method Download PDFInfo
- Publication number
- CN103936260A CN103936260A CN201410160762.8A CN201410160762A CN103936260A CN 103936260 A CN103936260 A CN 103936260A CN 201410160762 A CN201410160762 A CN 201410160762A CN 103936260 A CN103936260 A CN 103936260A
- Authority
- CN
- China
- Prior art keywords
- coloured glaze
- double
- blowing
- colored glaze
- blowing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a double-layer colored glaze blowing method. The double-layer colored glaze blowing method comprises the steps of manufacturing outer colored glaze and blowing inner glass, wherein the outer colored glaze manufacturing step comprises shape design, manufacturing of a silica gel mold, manufacturing of a wax mold, renovation of a plaster mold, firing of the colored glaze, finishing and polishing, and the inner glass blowing step comprises firing of glass, preparation of small bubbles, inner-side blowing, cooling, finishing and checking. Therefore, the double-layer colored glaze blowing method has the advantages of high reliability, simple manufacturing technology, high production speed, exquisite finished products, good practicability, suitability for cavities in different shapes, low cost, non-pollution of the finished products and the like and meanwhile has broad market prospect in the colored glaze production field.
Description
Technical field
The present invention relates to coloured glaze and manufacture field, particularly relate to a kind of double-deck coloured glaze blowing method.
Background technology
Coloured glaze, is one of China Han traditional handicraft product, with versicolor synthetic quartz be raw material, adopt the Ancient Bronze lost wax casting method high temperature crystal works that form that dewax.Its color stream cloud drench coloured silk, Meron U.S., quality is glittering and translucent, bright and glittering, but the material lead tolerance of using due to manufacture coloured glaze is high, in colour, be mixed with other toxic substances, at high temperature easily distribute, make coloured glaze be commonly used for artwork, the sight of the water tumbler of its manufacture, bowl basin is good but lack practicality, and existing double-deck manufacturing process of coloured glaze is not suitable for the manufacture of the kettle class vessel of internal cavity bulging.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of double-deck coloured glaze blowing method, by designing double-deck coloured glaze and glass, effectively isolates poisonous coloured glaze, ensures the practicality of coloured glaze; Mode by blowing is manufactured inner bag, adapts to various difform internal surfaces, and adaptability is good; Manufacture coloured glaze shell, various shapes by liquid condition shaping mode; Have that reliability is high, manufacturing process is simple, production rate is fast, finished product is exquisite, have good practicality, be applicable to the cavity of different shape, the advantage such as cheap, finished product is pollution-free, has market outlook widely at colored glaze product production field simultaneously.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of double-deck coloured glaze blowing method is provided, comprise: 1) design outline manufacture silica gel mould, 2) utilize silica gel mould make wax-pattern and turn over gypsum mold processed, 3) gypsum mold steam dewaxing is left to gypsum former, 4) select stained glass burning coloured glaze by design, 5) cooling rear finishing is polished and is completed the outer manufacture of coloured glaze, 6) from the crown glass solution of firing, take out glass basis and utilize blowpipe to make vesicle, 7) blowpipe is goed deep into the inner chamber of outer mould, blow in inner side, crown glass and coloured glaze shell are thoroughly fitted, 8) remove blowpipe and make it cooling, afterwards whole coloured glaze vessel are repaired to inspection.
In a preferred embodiment of the present invention, described glass basis temperature is 1000 DEG C, and described blowing temperature is 900 DEG C.
In a preferred embodiment of the present invention, the firing temperature of described burning coloured glaze is 1400 DEG C, and the described firing time is 3-10 days.
In a preferred embodiment of the present invention, described coloured glaze superficies are designed with blowing hole.
In a preferred embodiment of the present invention, described finishing inspection comprises for the filling up and finally polishing of the excision of unnecessary coloured glaze, blowing hole, and it is synthetic resins that the filling up of described blowing hole used material.
The invention has the beneficial effects as follows: the double-deck coloured glaze blowing method of the present invention, by design double-deck coloured glaze and glass, is effectively isolated poisonous coloured glaze, ensures the practicality of coloured glaze; Mode by blowing is manufactured inner bag, adapts to various difform internal surfaces, and adaptability is good; Manufacture coloured glaze shell, various shapes by liquid condition shaping mode; Have that reliability is high, manufacturing process is simple, production rate is fast, finished product is exquisite, have good practicality, be applicable to the cavity of different shape, the advantage such as cheap, finished product is pollution-free, has market outlook widely at colored glaze product production field simultaneously.
Embodiment
To the technical scheme in the embodiment of the present invention be clearly and completely described below, obviously, described embodiment is only a part of embodiment of the present invention, instead of whole embodiment.Based on the embodiment in the present invention, those of ordinary skill in the art, not making all other embodiment that obtain under creative work prerequisite, belong to the scope of protection of the invention.
The embodiment of the present invention comprises:
A kind of double-deck coloured glaze blowing method, comprise: a kind of double-deck coloured glaze blowing method is provided, comprise: 1) design outline manufacture silica gel mould, 2) utilize silica gel mould make wax-pattern and turn over gypsum mold processed, 3) gypsum mold steam dewaxing is left to gypsum former, 4) select stained glass burning coloured glaze by design, 5) cooling rear finishing is polished and is completed the outer manufacture of coloured glaze, 6) from the crown glass solution of firing, take out glass basis and utilize blowpipe to make vesicle, 7) blowpipe is goed deep into the inner chamber of outer mould, blow in inner side, crown glass and coloured glaze shell are thoroughly fitted, 8) remove blowpipe and make it cooling, excise unnecessary coloured glaze, and utilize resin to fill up blowing hole, afterwards whole coloured glaze vessel are repaired to inspection.
Described glass basis temperature is 1000 DEG C, and described blowing temperature is 900 DEG C, can well blow sizing, can effectively fit with shell.
The firing temperature of described burning coloured glaze is 1400 DEG C, and the described firing time is 3-10 days, ensures the well moulding of coloured glaze, reduces bubble.
Described coloured glaze superficies are designed with blowing hole, and convenient blowing, makes inner layer glass can be close to coloured glaze shell.
The beneficial effect of the double-deck coloured glaze blowing method of the present invention is:
One, by design double-deck coloured glaze and glass, effectively isolate poisonous coloured glaze, ensure the practicality of coloured glaze;
Two, manufacture inner bag by the mode of blowing, adapt to various difform internal surfaces, adaptability is good;
Three, manufacture coloured glaze shell, various shapes by liquid condition shaping mode;
Four, have that reliability is high, manufacturing process is simple, production rate is fast, finished product is exquisite, have good practicality, be applicable to the cavity of different shape, the advantage such as cheap, finished product is pollution-free, has market outlook widely at colored glaze product production field simultaneously.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or conversion of equivalent flow process that utilizes description of the present invention to do; or be directly or indirectly used in other relevant technical field, be all in like manner included in scope of patent protection of the present invention.
Claims (5)
1. a double-deck coloured glaze blowing method, it is characterized in that, comprise: 1) design outline manufacture silica gel mould, 2) utilize silica gel mould make wax-pattern and turn over gypsum mold processed, 3) gypsum mold steam dewaxing is left to gypsum former, 4) select stained glass burning coloured glaze by design, 5) cooling rear finishing is polished and is completed the outer manufacture of coloured glaze, 6) from the crown glass solution of firing, take out glass basis and utilize blowpipe to make vesicle, 7) blowpipe is goed deep into the inner chamber of outer mould, blow in inner side, crown glass and coloured glaze shell are thoroughly fitted, 8) remove blowpipe and make it cooling, afterwards whole coloured glaze vessel are repaired to inspection.
2. double-deck coloured glaze blowing method according to claim 1, is characterized in that, described glass basis temperature is 1000 DEG C, and described blowing temperature is 900 DEG C.
3. double-deck coloured glaze blowing method according to claim 1, is characterized in that, the firing temperature of described burning coloured glaze is 1400 DEG C, and the described firing time is 3-10 days.
4. double-deck coloured glaze blowing method according to claim 1, is characterized in that, described coloured glaze superficies are designed with blowing hole.
5. double-deck coloured glaze blowing method according to claim 1, is characterized in that, described finishing inspection comprises for the filling up and finally polishing of the excision of unnecessary coloured glaze, blowing hole, and it is synthetic resins that the filling up of described blowing hole used material.