CN102173871A - Preparation method of crackle glaze ceramic body-exposing pattern ceramic bottle - Google Patents
Preparation method of crackle glaze ceramic body-exposing pattern ceramic bottle Download PDFInfo
- Publication number
- CN102173871A CN102173871A CN201110023868XA CN201110023868A CN102173871A CN 102173871 A CN102173871 A CN 102173871A CN 201110023868X A CN201110023868X A CN 201110023868XA CN 201110023868 A CN201110023868 A CN 201110023868A CN 102173871 A CN102173871 A CN 102173871A
- Authority
- CN
- China
- Prior art keywords
- glaze
- crackle
- reveals
- crackle glaze
- ceramic bottle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a crackle glaze ceramic body-exposing pattern ceramic bottle. The preparation method comprises the following steps of: preparing a body; spraying or brushing one layer of interlayer on the part, requiring the crackle glaze, of the body; performing bisque firing; adhering paper to or drawing glue on patterns, decorative patterns or words on the body; glazing the crackle glaze; modifying the patterns; firing the glaze; and crackling. In the production process of a crackle glaze ceramic wine bottle, the method for adhering paper or drawing removable glue is adopted, paster is removed after the patterns, decorative patterns and words are covered and glazed, and the clear body-exposed crackle glaze ceramic wine bottle with three-dimensional and strong-embossment-feeling patterns, decorative patters and words is obtained after modifying, scraping, mending and decorating.
Description
Technical field
The invention belongs to the Production of Ceramics field, be specifically related to the preparation method of ceramic bottle of having of a kind of clear dew tire crackle glazes three-dimensional and the pattern printed words that the embossment sense is strong.
Background technology
Traditional and existing ceramic wine bottle all is no glaze or full glaze product, the pattern that no glaze product can obtain requiring, decorative pattern and printed words, but product surface does not have glaze, colour generation is exactly the carcass true qualities of bottle, the colour generation dullness, bottle mattness and crude sense is arranged, be generally low grade products, price is also on the low side, full glaze product pattern is covered by the glaze layer, because the glaze layer has thickness and color, make pattern particularly as dragon and phoenix, birds and flowers, the details of scenery with hills and waters pattern, the level of embossment can thicken unclear, and the glazing ceramic wine bottle should embody the glaze effect, make pattern again, decorative pattern, the details of printed words, level embodies, and just must have a kind of new production technique to reach our required product.
Summary of the invention
The objective of the invention is in order to overcome the problems referred to above, provide a kind of crackle glaze pottery to reveal tire pattern ceramic bottle preparation method.This method in crackle glaze ceramic wine bottle production process by retouch the method that is coated with the method for paster or with tearable glue, make that pattern, printed words place are covered, reject paster after the glazing, by obtaining the crackle glaze ceramic wine bottle with the strong pattern printed words of solid and embossment sense of clear dew tire after repairing, scrape, mend, decorating.
Purpose of the present invention can reach by following measure:
A kind of crackle glaze pottery reveals tire pattern ceramic bottle (particularly ceramic wine bottle) preparation method, it comprises the steps: preparation blank earlier, required position spray or brushing one deck middle layer of executing crackle glaze on blank, carry out biscuiting then, pattern after the biscuiting on base substrate, decorative pattern or printed words place carry out paster or retouch glue, paster or retouch glue after carry out glazing with crackle glaze, through after the pattern finishing, carry out glaze firing, hack at last.
In the required position spray of crackle glaze or the middle layer that brushing one deck is different from blank material of executing of blank, help crackle glaze and produce the line sheet, prevent simultaneously when the crackle glaze streakline from producing to blank pull or cause stress, make product in use because the effect of stress causes a bottle carcass to crack and seepage.The quality group of this intermediate layer material becomes: Suzhou soil 45～55%, talcum powder 12～18%, feldspar 18～22%, Changxing white clay 13～17%, bubble flower alkali 0.2～0.3%, soda ash 0.4～0.6% (each component sum is 100%).Most preferred consisting of: Suzhou soil 50%, talcum powder 15%, feldspar 20%, Changxing white clay 15%, bubble flower alkali 0.25%, soda ash 0.5%.
Crackle glaze of the present invention comprises basic glaze and pigment, wherein the quality composition of basic glaze is: feldspar 64～68wt.%, quartzy 7～9wt.%, Suzhou soil 8～12wt.%, glass 10～14wt.% (each component sum is 100%), preferred group becomes: feldspar 66%, quartzy 8%, Suzhou soil 10%, glass 12%.In basic glaze, add respectively pigment praseodymium yellow, chromium titanium merimee's yellow, vanadium orchid or antimony sunset ash, then can form the crackle glaze of orange, orange, blue look, celadon respectively.
Make objectionable impurities volatilizations such as mechanical water, planar water, organism by biscuiting, help the raising of quality product, increased the water-intake rate of base substrate simultaneously, help the adsorption strength and the thickness of glaze layer.The unglazed temperature is 800～1000 ℃.
Paster is: special-purpose cotton rice paper is cut into and bottle pattern, the consistent shape of printed words, uses water as bondingly, pattern etc. is covered.Retouch glue for pattern etc. being retouched the glue covering with tearable glue.Paster speed is fast but the pattern edge details is poor in two kinds of modes, and it is slow but edge details such as pattern are good to retouch glue speed, can select to use according to two kinds of modes of practical situation.The glue of retouching in the glue adopts waterproof glue.
Glazing adopts the method for soaking glaze or glaze spraying to carry out.The temperature of glaze firing is 1150～1200 ℃.
Beneficial effect of the present invention: paster or retouch gluing method and in the Production of Ceramics field of routine, also have and use but early stage production technique is generally carried out on device shape surface, the poor effect that forms, do not have gradation sense, artistry is not strong yet, and the market requirement is also low, and the present invention carries out process innovation on the embossment figure on the bottle, and being equipped with crackle glaze of all kinds, the pattern levels are rich has more artistic characteristics, particularly be applied to obtain numerous clients' favor on the ceramic wine bottle of red-purple carcass.
Description of drawings
Fig. 1 is the process flow sheet of the embodiment of the invention 1.
Fig. 2 is the external view of embodiment 1 products obtained therefrom.
Embodiment
Embodiment 1
1, blank: the blank that obtains required moulding by slip casting or mechanical-moulded mode.
2, middle layer: do not have pattern, decorative pattern, printed words place to spray or brush to the bottle appearance with intermediate layer material.Intermediate layer material consists of Suzhou soil 50%, talcum powder 15%, feldspar 20%, Changxing white clay 15%, bubble flower alkali 0.25%, soda ash 0.5%.
3, biscuiting: after the middle layer forms, burn till by 800-1000 ℃.
4, paster, retouch glue: pattern, decorative pattern, printed words place by the unglazed blank are carried out paster or retouch glue (glue refers to waterproof glue).
5, execute crackle glaze: paster, retouch behind the glue with crackle glaze (basic glaze quality consists of: feldspar 66%, quartzy 8%, Suzhou soil 10%, glass 12%; In basic glaze, add respectively pigment praseodymium yellow, chromium titanium merimee's yellow, vanadium orchid or antimony sunset ash, then can form the crackle glaze of orange, orange, blue look, celadon respectively) carry out glazing with the method for soaking glaze or glaze spraying.
6, pattern finishing.After executing outer glaze, remove paster and retouch glue, pattern, decorative pattern, printed words place are repaired, just be meant unnecessary glaze is repaiied, damaged glaze is filled a vacancy, make details, the clear layer of pattern, decorative pattern, printed words.
7, glaze firing: after burning till by 1150-1200 ℃ high temperature, obtain the product that line sheet mechanism is revealed the tire pattern effect.
8, hack: carry out after glaze handles with the inorganic color that need hack line, it is distinct to obtain glaze laminated striation sheet mechanism, embodies the ceramic wine bottle that pattern, decorative pattern, printed words are the tire chromatic effect simultaneously again.
9, test package: the salable product by inspection are packed warehouse-in.
The bottle of different pattern, literal or decorative pattern is carried out above-mentioned processing, obtain product shown in Figure 2 respectively.
Claims (10)
1. a crackle glaze pottery reveals tire pattern ceramic bottle preparation method, it is characterized in that comprising the steps: preparation blank earlier, required position spray or brushing one deck middle layer of executing crackle glaze on blank, carry out biscuiting then, pattern after the biscuiting on base substrate, decorative pattern or printed words place carry out paster or retouch glue, paster or retouch glue after carry out glazing with crackle glaze, through after the pattern finishing, carry out glaze firing, hack at last.
2. crackle glaze pottery according to claim 1 reveals tire pattern ceramic bottle preparation method, it is characterized in that the material in described middle layer is different from blank material.
3. crackle glaze pottery according to claim 1 and 2 reveals tire pattern ceramic bottle preparation method, the quality group that it is characterized in that described intermediate layer material becomes: Suzhou soil 45～55%, talcum powder 12～18%, feldspar 18～22%, Changxing white clay 13～17%, bubble flower alkali 0.2～0.3%, soda ash 0.4～0.6%.
4. crackle glaze pottery according to claim 3 reveals tire pattern ceramic bottle preparation method, the quality group that it is characterized in that described intermediate layer material becomes: Suzhou soil 50%, talcum powder 15%, feldspar 20%, Changxing white clay 15%, bubble flower alkali 0.25%, soda ash 0.5%.
5. crackle glaze pottery according to claim 1 reveals tire pattern ceramic bottle preparation method, it is characterized in that described crackle glaze comprises basic glaze and pigment, wherein the quality group of basic glaze becomes: feldspar 64～68%, quartzy 7～9%, Suzhou soil 8～12%, glass 10～14%.
6. crackle glaze pottery according to claim 5 reveals tire pattern ceramic bottle preparation method, it is characterized in that the composition of described crackle glaze base glaze is: feldspar 66%, quartz 8%, Suzhou soil 10%, glass 12%.
7. crackle glaze pottery according to claim 1 reveals tire pattern ceramic bottle preparation method, it is characterized in that the unglazed temperature is 800～1000 ℃.
8. crackle glaze pottery according to claim 1 reveals tire pattern ceramic bottle preparation method, it is characterized in that the described glue of retouching in the glue is waterproof glue.
9. crackle glaze according to claim 1 pottery reveals tire pattern ceramic bottle preparation method, it is characterized in that described glazing adopts the method for soaking glaze or glaze spraying to carry out.
10. crackle glaze pottery according to claim 1 reveals tire pattern ceramic bottle preparation method, and the temperature that it is characterized in that described glaze firing is 1150～1200 ℃.