CN103304938A - Ptc热敏电阻基材及其制备方法 - Google Patents
Ptc热敏电阻基材及其制备方法 Download PDFInfo
- Publication number
- CN103304938A CN103304938A CN2013101974919A CN201310197491A CN103304938A CN 103304938 A CN103304938 A CN 103304938A CN 2013101974919 A CN2013101974919 A CN 2013101974919A CN 201310197491 A CN201310197491 A CN 201310197491A CN 103304938 A CN103304938 A CN 103304938A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- ptc
- base material
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种PTC热敏电阻基材,由下列重量份的原料制成:聚偏氟乙烯50-55、线性低密度聚乙烯30-35、碳黑20-25、铝粉18-24、氮化铝12-16、麦饭石粉20-25、氢氧化铝粉16-18、氧化镁6-8、海泡石12-14、交联剂TAC3-5、交联剂TAIC1-2、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷5-8、二甲基二巯基乙酸异辛酯锡2-3、环氧化甘油三酸酯8-10。大大提高了本发明的PTC强度和高的PTC稳定性,电阻稳定、温度均匀、PTC特性稳定、增加材料的使用寿命。
Description
技术领域
本发明属于高分子材料领域,具体涉及一种高分子基PTC 热敏电阻基材及其制备方法。
背景技术
PTC 高分子发热材料作为过热、过流保护和自控温加热材料广泛应用于通信、计算机、汽车、工业控制、家用电器等众多领域中。目前的有机PTC 材料主要以石墨和炭黑为导电填料,主要存在室温电阻分布较宽,PTC 强度小、稳定性较低等问题。
发明内容
本发明的目的是提供一种PTC热敏电阻基材及其制备方法,具备低的室温电阻率、长期通流稳定的性能、高的PTC 强度和高的PTC 稳定性。
本发明技术方案如下:
一种PTC热敏电阻基材,其特征在于:由下列重量份的原料制成:聚偏氟乙烯50-55、线性低密度聚乙烯30-35、碳黑20-25、铝粉18-24、氮化铝12-16、麦饭石粉20-25、氢氧化铝粉16-18、氧化镁6-8、海泡石12-14、交联剂 TAC 3-5、交联剂 TAIC 1-2、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷5-8、二甲基二巯基乙酸异辛酯锡2-3、环氧化甘油三酸酯8-10。
所述的PTC热敏电阻基材的制备方法,其特征在于:包括以下步骤:将氢氧化铝粉加水搅拌制成悬浮液,再加入铝粉、麦饭石粉,高速分散10-20分钟后,加热至80-95℃,再加交联剂 TAC、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷,搅拌均匀后,再加入氧化镁粉,研磨2-3小时,到浆料,喷雾干燥,得到粉末;将线性低密度聚乙烯、碳黑、氮化铝、环氧化甘油三酸酯在80-120℃下混炼15-25分钟,得到混合料;将聚偏氟乙烯、所得粉末与混合料及其它剩余原料混合,加热至130-185℃,混炼15-25分钟,挤出造粒得到。
将本发明PTC 高分子发热材料压制成片材,再在片材表面压制导线,即得到PTC发热片。
本发明采用碳黑、铝粉作为导电复合材料,铝粉、麦饭石粉加入交联剂 TAC、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷进行研磨,增加其之间的分子网格结构,具有加强耐热、耐流、耐压和提高电阻变化稳定性的作用;本发明线性低密度聚乙烯、碳黑、氮化铝、环氧化甘油三酸酯实行一次混料,增加了各原料组成分散性,经过二次混料后,增加了各原料成分之间的兼容性,导电网络结构的更加稳固,大大提高了本发明的PTC 强度和高的PTC 稳定性,电阻稳定、温度均匀、PTC特性稳定、增加材料的使用寿命。
具体实施方式
一种PTC热敏电阻基材,由下列重量份(公斤)的原料制成:聚偏氟乙烯50、线性低密度聚乙烯30、碳黑25、铝粉24、氮化铝16、麦饭石粉20、氢氧化铝粉16、氧化镁6、海泡石14、交联剂 TAC 5、交联剂 TAIC 2、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷5、二甲基二巯基乙酸异辛酯锡3、环氧化甘油三酸酯8-。
所述的PTC热敏电阻基材的制备方法,包括以下步骤:将氢氧化铝粉加水搅拌制成悬浮液,再加入铝粉、麦饭石粉,高速分散10-20分钟后,加热至80-95℃,再加交联剂 TAC、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷,搅拌均匀后,再加入氧化镁粉,研磨2-3小时,到浆料,喷雾干燥,得到粉末;将线性低密度聚乙烯、碳黑、氮化铝、环氧化甘油三酸酯在80-120℃下混炼15-25分钟,得到混合料;将聚偏氟乙烯、所得粉末与混合料及其它剩余原料混合,加热至130-185℃,混炼15-25分钟,挤出造粒得到
将本发明PTC 高分子发热材料压制成片材,制备长100mm、宽6.5mm、厚2mm 的条形样品,再在片材表面压制导线,即得到PTC发热片。
检测性能:
室温(25℃ ) 零功率电阻为12mΩ,PTC 强度达到8.1 以上,将其在-20℃和140℃之间热循环200 次后其室温电阻仍在30mΩ以下,并且在热循环中电阻的变化情况稳定,具有长期通流大于100A 的通流能力。在200下连续发热36小时,无烧焦现象。PTC高分子发热材料寿命:15分钟通电一次,15分钟断电一次,30分钟一个循环,通断5000次,功率变化率94%,温度变化率98%。
Claims (2)
1.一种PTC热敏电阻基材,其特征在于:由下列重量份的原料制成:聚偏氟乙烯50-55、线性低密度聚乙烯30-35、碳黑20-25、铝粉18-24、氮化铝12-16、麦饭石粉20-25、氢氧化铝粉16-18、氧化镁6-8、海泡石12-14、交联剂 TAC 3-5、交联剂 TAIC 1-2、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷5-8、二甲基二巯基乙酸异辛酯锡2-3、环氧化甘油三酸酯8-10。
2.根据权利要求1所述的PTC热敏电阻基材的制备方法,其特征在于:包括以下步骤:将氢氧化铝粉加水搅拌制成悬浮液,再加入铝粉、麦饭石粉,高速分散10-20分钟后,加热至80-95℃,再加交联剂 TAC、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷,搅拌均匀后,再加入氧化镁粉,研磨2-3小时,到浆料,喷雾干燥,得到粉末;将线性低密度聚乙烯、碳黑、氮化铝、环氧化甘油三酸酯在80-120℃下混炼15-25分钟,得到混合料;将聚偏氟乙烯、所得粉末与混合料及其它剩余原料混合,加热至130-185℃,混炼15-25分钟,挤出造粒得到。