CN104788837A - 一种pps导热绝缘塑料 - Google Patents
一种pps导热绝缘塑料 Download PDFInfo
- Publication number
- CN104788837A CN104788837A CN201510146668.1A CN201510146668A CN104788837A CN 104788837 A CN104788837 A CN 104788837A CN 201510146668 A CN201510146668 A CN 201510146668A CN 104788837 A CN104788837 A CN 104788837A
- Authority
- CN
- China
- Prior art keywords
- pps
- percent
- conductive insulated
- polystyrene
- moulded heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种PPS导热绝缘塑料,由以下成分按重量比组成:聚苯乙烯85%~90%、聚酰胺树脂10%~15%、氧化镁45~55%、高岭陶土5%~8%、二氧化钛2%~4.5%、抗氧剂1.5%~3.5%、复合热稳定剂2.5%~4.5%、偶联剂5%~10%、高效润滑剂5%~7.5%,本发明还公开了PPS导热绝缘塑料的制作方法。通过上述方式,本发明一种PPS导热绝缘塑料,PPS复合材料的导热率为4.5W/(m K),同时具有良好的机械加工性能及电绝缘性能,极大的增强了PPS的应用范围。
Description
技术领域
本发明涉及塑料,特别是涉及一种PPS导热绝缘塑料。
背景技术
我国电子电器用的导热绝缘复合材料多为胶粘剂、橡胶材料,对于塑料导热绝缘材料的应用少之又少,而国外对于导热绝缘塑料的应用已成为系列化商品。
PPS塑料电绝缘性(尤其高频绝缘性)优良,白色硬而脆,跌落于地上有金属响声,透光率仅次于有机玻璃,着色性耐水性,化学稳定性良好。有优良的阻燃性,为不燃塑料。但PPS强度一般,质脆,易产生应力脆裂;不耐苯、汽油等有机溶剂;长期使用温度可达260度,在400度的空气或氮气中保持稳定。通过添加增强材料改性后,可以使冲击强度大为提高,耐热性和其它机械性能也有所提高。
发明内容
本发明主要解决的技术问题是提供一种PPS导热绝缘塑料的制作方法。通过上述方式,本发明一种PPS导热绝缘塑料,PPS复合材料的导热率为4.5W/(m K),同时具有良好的机械加工性能及电绝缘性能,极大的增强了PPS的应用范围。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种PPS导热绝缘塑料,由以下成分按重量比组成:聚苯乙烯85%~90%、聚酰胺树脂10%~15%、氧化镁45%~55%、高岭陶土5%~8%、二氧化钛2%~4.5%、抗氧剂1.5%~3.5%、复合热稳定剂2.5%~4.5%、偶联剂5%~10%、高效润滑剂5%~7.5%。
在本发明一个较佳实例中,所述抗氧剂为L-维生素C及苹果酚的混合物。
在本发明一个较佳实例中,所述复合热稳定剂为无毒液体钙锌稳定剂。
在本发明一个较佳实例中,所述偶联剂为2,3环氧丙基三乙氧硅烷。
在本发明一个较佳实例中,包括以下步骤:
步骤一、将聚苯乙烯充分干燥,然后按照聚苯乙烯88%~90%、高岭陶土6~8%、二氧化钛3%~4.5%、氧化镁50%~55%、L-维生素C1%~1.5%、苹果酚1.5%~2%、无毒液体钙锌稳定剂2.5%~3.5%、2,3环氧丙基三乙氧硅烷8%~10%、高效润滑剂6%~7.5%的比例进行称取;
步骤二、将称取好的料依次放入高速混合机中进行混合5~8min,待混合均匀后取出备用;
步骤三、将混合料及聚酰胺树脂10%~15%送入双螺杆挤出机进行造粒得到PPS塑料粒子。
本发明的有益效果是:本发明一种PPS导热绝缘塑料的制作方法。通过上述方式,本发明一种PPS导热绝缘塑料,PPS复合材料的导热率为4.5W/(m K),同时具有良好的机械加工性能及电绝缘性能,极大的增强了PPS的应用范围。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
实施例1
一种PPS导热绝缘塑料,由以下成分按重量比组成:聚苯乙烯85%~90%、聚酰胺树脂10%~15%、氧化镁45%~55%、高岭陶土5%~8%、二氧化钛2%~4.5%、抗氧剂1.5%~3.5%、复合热稳定剂2.5%~4.5%、偶联剂5%~10%、高效润滑剂5%~7.5%。
进一步,所述抗氧剂为L-维生素C及苹果酚的混合物。
进一步,所述复合热稳定剂为无毒液体钙锌稳定剂。
进一步,所述偶联剂为2,3环氧丙基三乙氧硅烷。
一种PPS导热绝缘塑料,包括以下步骤:
步骤一、将聚苯乙烯充分干燥,然后按照聚苯乙烯90%、高岭陶土8%、二氧化钛3.5%、氧化镁50%、L-维生素C1.5%、苹果酚1.5%、无毒液体钙锌稳定剂2.5%、2,3环氧丙基三乙氧硅烷10%、高效润滑剂7.5%的比例进行称取;
步骤二、将称取好的料依次放入高速混合机中进行混合5~8min,待混合均匀后取出备用;
步骤三、将混合料及聚酰胺树脂10%~15%送入双螺杆挤出机进行造粒得到PPS塑料粒子。
实施例2
一种PPS导热绝缘塑料,包括以下步骤:
将聚苯乙烯充分干燥,然后按照聚苯乙烯90%、高岭陶土8%、二氧化钛3.5%、氧化镁55%、L-维生素C1.5%、苹果酚1.5%、无毒液体钙锌稳定剂2.5%、2,3环氧丙基三乙氧硅烷10%、高效润滑剂7.5%的比例进行称取;
将称取好的料依次放入高速混合机中进行混合5~8min,待混合均匀后取出备用;
将混合料及聚酰胺树脂10%~15%送入双螺杆挤出机进行造粒得到PPS塑料粒子。
所不同的是添加氧化镁比例不同。
本发明的有益效果是:本发明一种PPS导热绝缘塑料的制作方法。通过上述方式,本发明一种PPS导热绝缘塑料,PPS复合材料的导热率为4.5W/(m K),同时具有良好的机械加工性能及电绝缘性能,极大的增强了PPS的应用范围。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围。
Claims (5)
1.一种PPS导热绝缘塑料,其特征在于,由以下成分按重量比组成:聚苯乙烯85%~90%、聚酰胺树脂10%~15%、氧化镁45%~55%、高岭陶土5%~8%、二氧化钛2%~4.5%、抗氧剂1.5%~3.5%、复合热稳定剂2.5%~4.5%、偶联剂5%~10%、高效润滑剂5%~7.5%。
2.根据权利要求1所述的PPS导热绝缘塑料,其特征在于,所述抗氧剂为L-维生素C及苹果酚的混合物。
3.根据权利要求1所述的PPS导热绝缘塑料,其特征在于,所述复合热稳定剂为无毒液体钙锌稳定剂。
4.根据权利要求1所述的PPS导热绝缘塑料,其特征在于,所述偶联剂为2,3环氧丙基三乙氧硅烷。
5.一种PPS导热绝缘塑料的制备方法,其特征在于,包括以下步骤:
步骤一、将聚苯乙烯充分干燥,然后按照聚苯乙烯88%~90%、高岭陶土6%~8%、二氧化钛3%~4.5%、氧化镁50%~55%、L-维生素C1%~1.5%、苹果酚1.5%~2%、无毒液体钙锌稳定剂2.5%~3.5%、2,3环氧丙基三乙氧硅烷8%~10%、高效润滑剂6%~7.5%的比例进行称取;
步骤二、将称取好的料依次放入高速混合机中进行混合5~8min,待混合均匀后取出备用;
步骤三、将混合料及聚酰胺树脂10%~15%送入双螺杆挤出机进行造粒得到PPS塑料粒子。