CN103304675A - 一种淀粉黄糊精的简易制备方法 - Google Patents
一种淀粉黄糊精的简易制备方法 Download PDFInfo
- Publication number
- CN103304675A CN103304675A CN2013102759619A CN201310275961A CN103304675A CN 103304675 A CN103304675 A CN 103304675A CN 2013102759619 A CN2013102759619 A CN 2013102759619A CN 201310275961 A CN201310275961 A CN 201310275961A CN 103304675 A CN103304675 A CN 103304675A
- Authority
- CN
- China
- Prior art keywords
- starch
- yellow
- quality
- stir
- preparing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种淀粉黄糊精的简易制备方法,其主要工艺过程是将一定量的马铃薯淀粉倒入盛有相同质量的去离子水中,然后滴入质量为马铃薯淀粉质量0.35%的36%的盐酸和质量为马铃薯淀粉质量0.28%的65%的硝酸,搅拌均匀,自然晾干,在铁锅中翻炒,控制温度在1200C-1300C,直到混合物的颜色变为深黄色,自然冷却,包装即得产品,该产品制备工艺简单,成本很低。
Description
技术领域
本发明涉及一种淀粉黄糊精的简易制备方法,特别指以马铃薯淀粉、浓盐酸和浓硝酸为原料,来制备适用于纸面石膏板粘合剂用的黄糊精的简易方法。
背景技术
黄糊精是重要的淀粉变性产物,其低廉的价格及优越的粘合性能使其具有广泛的应用,特别是在纸面石膏板生产中作为主要的粘合剂。由于黄糊精价格较低,因此开发一种简易的制备方法,对于降低企业的流动资金占有率及减少运输成本具有重要意义。
发明内容
本发明要解决的技术问题是提供一种淀粉黄糊精的简易制备方法,这种制备方法以马铃薯淀粉、浓盐酸和浓硝酸为原料,经合理配比,通过一定的工艺过程而制得黄糊精。
本发明要解决的技术问题是由如下方案解决的:一种淀粉黄糊精的简易制备方法,其特征是:首先将一定量马铃薯淀粉在搅拌的条件下加入到盛有相同质量的去离子水中,然后滴入质量为马铃薯淀粉质量0.35%的36%的盐酸和质量为马铃薯淀粉质量0.28%的65%的硝酸搅拌均匀,自然晾干,在铁锅中翻炒,温度控制在1200C -1300C,直到混合物的颜色变为深黄色,自然冷却,包装即得产品。
本发明的优点是:1、本方法的生产工艺和设备简单,制备的黄糊精性能很好,成本很低。2、本方法适合企业自产自用,可节约运输环节的成本,减少流动资金的占用。
附图说明
图1是本发明的制备工艺流程图。
具体实施方式
首先将10公斤马铃薯淀粉加入到质量为10公斤的去离子水中,然后分别滴入35g质量分数为36%的盐酸和28g质量分数为65%的硝酸,搅拌均匀,自然晾干,在铁锅中翻炒,温度控制在1200C -1300C,直到混合物的颜色变为深黄色后自然冷却,包装即得产品。
Claims (4)
1.一种淀粉黄糊精的简易制备方法,其特征是:首先将一定量马铃薯淀粉加入到盛有相同质量的去离子水中,然后滴入质量为马铃薯淀粉质量0.35%的36%的盐酸和质量为马铃薯淀粉质量0.28%的65%的硝酸,搅拌均匀,自然晾干,在铁锅中翻炒,直到混合物的颜色变为深黄色,自然冷却,包装即得产品。
2.根据权利要求1所述一种淀粉黄糊精的简易制备方法,其原料为马铃薯淀粉、浓盐酸和浓硝酸。
3.根据权利要求1所述一种淀粉黄糊精的简易制备方法,其主要工艺过程为在铁锅中翻炒。
4.一种淀粉黄糊精的简易制备方法,其特征是:反应混合物在铁锅中的翻炒温度为120 0C -1300C。