CN103289628A - 一种用于板材的聚乙烯热熔胶及其制备方法 - Google Patents
一种用于板材的聚乙烯热熔胶及其制备方法 Download PDFInfo
- Publication number
- CN103289628A CN103289628A CN2013102525866A CN201310252586A CN103289628A CN 103289628 A CN103289628 A CN 103289628A CN 2013102525866 A CN2013102525866 A CN 2013102525866A CN 201310252586 A CN201310252586 A CN 201310252586A CN 103289628 A CN103289628 A CN 103289628A
- Authority
- CN
- China
- Prior art keywords
- melt adhesive
- hot melt
- parts
- polyethylene
- polyethylene hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于板材的聚乙烯热熔胶，包括以下重量份计的组分：对苯二甲酸聚酯80-100份、聚乙烯蜡PE2010-20份、氧化烯烃30-40份、聚丙烯酸钠10-15份、钛酸四丁酯1-7份、异佛尔酮二胺1.3-2.5份、5-钠磺基间苯二甲酸二甲酯15-20份、聚己二酸丁二醇酯二元醇20-30份。本发明的聚乙烯热熔胶对不同的板材的剥离强度均高于一般的热熔胶，尤其对于硬质聚氯乙烯薄板和软质聚氯乙烯薄板，粘结强度很强；而且本发明的产品容易得到，降低生产成本，各组分之间易分散均匀，有利于提高热熔胶的稳定性。
Description
技术领域
本发明涉及塑胶领域，尤其涉及一种用于板材的聚乙烯热熔胶及其制备方法。
背景技术
热熔胶粘合是利用热熔胶机通过热力把热熔胶熔解，熔胶后的胶成为一种液体，通过热熔胶机的热熔胶管和热熔胶枪，送到被粘合物表面，热熔胶冷却后即完成了粘合。热熔胶通常是指在室温下呈固态，加热熔融成液态，涂布，润湿被粘物后，经压合、冷却，在几秒钟内完成粘结的粘接剂。热熔胶一般分为天然热熔胶，如石蜡、松香、沥青等；合成热熔胶，如共聚烯烃、聚酰胺、聚酯、聚氨酯；按化学组成分可以分为聚烯类热熔胶粘剂，乙烯及其共聚物类热熔胶粘剂、聚酯类热熔胶粘剂、聚酰胺类热熔胶粘剂，其中，聚烯类热熔胶粘剂中的聚乙烯热熔胶由乙烯与少量的烯烃或其他单体聚合而成的热熔胶，比较容易粘接多孔性的表面；但是现有技术的聚乙烯热熔胶的粘接性能不是很好、容易分离。热熔胶可以通过掺混、接枝等办法对现有品种进行改性以提高热熔胶的性能。例如稳定剂用于防止氧化；增粘剂改善粘接强度；石蜡降低粘度改变表面性质；各种填料可提高粘度、熔点和粘接强度等。研究各种配合剂的品种、用量，并进行配方优化以满足不同需求。
发明内容
本发明提供了一种用于板材的聚乙烯热熔胶及其制备方法，粘接强度较强，不易剥离。
本发明采用以下技术方案：
一种用于板材的聚乙烯热熔胶，包括以下重量份计的组分：
对苯二甲酸聚酯80-100份、聚乙烯蜡PE20 10-20份、氧化烯烃30-40份、聚丙烯酸钠10-15份、钛酸四丁酯1-7份、异佛尔酮二胺1.3-2.5份、5-钠磺基间苯二甲酸二甲酯15-20份、聚己二酸丁二醇酯二元醇20-30份。
作为优选，聚乙烯蜡PE20的相对分子质量300-600.
作为优选，氧化烯烃是氧化乙烯或氧化丙烯。
上述热熔胶的制备方法包括以下步骤：将各组分放入捏合机在200-220℃混合20-25min，然后造粒，粒子直径为8-10mm，长度为10-20mm。
作为改进，捏合机的温度控制在210℃混合22min。
在热熔胶中添加聚乙烯，可以降低熔融粘度，改善操作性能，本发明的聚乙烯热熔胶对不同的板材的剥离强度均高于一般的热熔胶，尤其对于硬质聚氯乙烯薄板和软质聚氯乙烯薄板，粘结强度很强,高达80N/CM；对于软质聚氯乙烯板和软质聚氯乙烯板的剥离强度需450N/CM左右；对于丙烯酸树脂板和软质聚氯乙烯薄板的剥离强度需350N/CM左右；可见，本发明的热熔胶的粘度比较强，明显高于现有技术的热熔胶；而且本发明的产品容易得到，降低生产成本，各组分之间易分散均匀，有利于提高热熔胶的稳定性。
具体实施方式
下面结合具体实施例对本发明作进一步详细介绍。
实施例1
一种用于板材的聚乙烯热熔胶，包括以下重量份计的组分：对苯二甲酸聚酯80份、聚乙烯蜡PE20 （相对分子质量300）10份、氧化乙烯30份、聚丙烯酸钠10份、钛酸四丁酯1份、异佛尔酮二胺1.3份、5-钠磺基间苯二甲酸二甲酯15份、聚己二酸丁二醇酯二元醇20份。
上述热熔胶的制备方法，包括以下步骤：将各组分放入捏合机在200℃混合20min，然后造粒，粒子直径为8mm，长度为10mm。
实施例2
一种用于板材的聚乙烯热熔胶，包括以下重量份计的组分：对苯二甲酸聚酯100份、聚乙烯蜡PE20 （相对分子质量600）20份、氧化丙烯40份、聚丙烯酸钠15份、钛酸四丁酯7份、异佛尔酮二胺2.5份、5-钠磺基间苯二甲酸二甲酯20份、聚己二酸丁二醇酯二元醇30份。
上述热熔胶的制备方法，包括以下步骤：将各组分放入捏合机在220℃混合25min，然后造粒，粒子直径为10mm，长度为20mm。
实施例3
一种用于板材的聚乙烯热熔胶，包括以下重量份计的组分：对苯二甲酸聚酯90份、聚乙烯蜡PE20 （相对分子质量400）15份、氧化乙烯35份、聚丙烯酸钠13份、钛酸四丁酯5份、异佛尔酮二胺1.9份、5-钠磺基间苯二甲酸二甲酯18份、聚己二酸丁二醇酯二元醇25份。
上述热熔胶的制备方法，包括以下步骤：将各组分放入捏合机在210℃混合23min，然后造粒，粒子直径为9mm，长度为15mm。
下面通过试验测试实施例1、2、3制得的产品的性能：将制得的热熔胶喷涂在板材上，用100℃的热辊压紧，冷却后在20℃测定剥离强度T，单位N/CM。
| 板材类型 | 实施例1 | 实施例2 | 实施例3 |
| 软质聚氯乙烯板和软质聚氯乙烯板 | 45.2 | 46.3 | 43.5 |
| 镀锌铁皮板和软质聚氯乙烯板 | 30.8 | 32.4 | 29.8 |
| 软钢板和软聚氯乙烯板 | 8.0 | 8.3 | 8.9 |
| 硬质聚氯乙烯薄板和软质聚氯乙烯薄板 | 80.8 | 81.6 | 80.9 |
| 丙烯酸树脂板和软质聚氯乙烯薄板 | 35.4 | 35.8 | 35.6 |
| 软铝板和软铝板 | 26.6 | 27.6 | 28.4 |
| 硬铝板和硬铝板 | 23.4 | 24.5 | 24.3 |
| 不锈钢板和软质聚氯乙烯板 | 15.1 | 16.1 | 15.8 |
Claims (3)
1. 一种用于板材的聚乙烯热熔胶，其特征在于包括以下重量份计的组分：对苯二甲酸聚酯80-100份、聚乙烯蜡PE20 10-20份、氧化烯烃30-40份、聚丙烯酸钠10-15份、钛酸四丁酯1-7份、异佛尔酮二胺1.3-2.5份、5-钠磺基间苯二甲酸二甲酯15-20份、聚己二酸丁二醇酯二元醇20-30份。
2. 根据权利要求1所述的用于板材的聚乙烯热熔胶，其特征在于：聚乙烯蜡PE20的相对分子质量300-600.
根据权利要求1所述的用于板材的聚乙烯热熔胶，其特征在于：氧化烯烃是氧化乙烯或氧化丙烯。
3. 基于权利要求1所述的用于板材的聚乙烯热熔胶的制备方法，包括以下步骤：将各组分放入捏合机在200-220℃混合20-25min，然后造粒，粒子直径为8-10mm，长度为10-20mm。