CN103289335A - 一种耐水解增强型pbt - Google Patents
一种耐水解增强型pbt Download PDFInfo
- Publication number
- CN103289335A CN103289335A CN2013102518985A CN201310251898A CN103289335A CN 103289335 A CN103289335 A CN 103289335A CN 2013102518985 A CN2013102518985 A CN 2013102518985A CN 201310251898 A CN201310251898 A CN 201310251898A CN 103289335 A CN103289335 A CN 103289335A
- Authority
- CN
- China
- Prior art keywords
- parts
- hydrolysis
- pbt
- reinforced pbt
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种耐水解增强型PBT，属于高分子材料技术领域，其特征在于包括按照重量份数计的如下原料：PBT树脂90~110份、玻璃纤维10~15份、碳化硅晶须2~4份、复合耐水解剂0.3~0.8份、纳米氧化锌0.5~2份、硬脂酸甘油酯0.5~2份、抗氧剂5650.4~0.7份、抗氧剂6260.6~0.8份、亚磷酸三苯酯0.4~0.6份、热稳定剂0.5~2份、增韧剂3~7份。本发明产品机械性能优异，稳定性好，且具有良好的耐水性，大大拓宽了PBT材料的使用范围。本发明中添加了纳米氧化锌，不仅提高了本发明产品的稳定性，还使得本发明产品具有一定的抗菌力。
Description
技术领域
本发明属于高分子材料技术领域，具体涉及一种耐水解增强型PBT。
背景技术
PBT是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性，且吸湿性很弱。但是，PBT的缺口冲击强度低，成型收缩率大，很难满足人们的需求。
由于PBT中含有酯基，在湿热环境中会发生水解反应，大分子链断裂，分子量下降，产品的机械性能也随之下降，严重时材料完全不能使用，这一缺点大大限制了PBT的使用范围。
因此，如何克服现有技术的不足，制造出是一种耐水解增强型PBT是高分子材料技术领域亟需解决的问题。
发明内容
本发明的目的是为了解决现有技术的不足，提供一种耐水解增强型PBT，该发明产品不仅具有优异的机械性能，还具有良好的耐水解性。
本发明采用的技术方案如下：
一种耐水解增强型PBT，其特征在于包括按照重量份数计的如下原料：PBT树脂90~110份、玻璃纤维10~15份、碳化硅晶须2~4份、复合耐水解剂0.3~0.8份、纳米氧化锌0.5~2份、硬脂酸甘油酯0.5~2份、抗氧剂565 0.4~0.7份、抗氧剂626 0.6~0.8份、亚磷酸三苯酯0.4~0.6份、热稳定剂0.5~2份、增韧剂3~7份。
进一步其优化方案为所述的玻璃纤维为无碱玻璃纤维。
进一步其优化方案为复合耐水解剂为质量比为2:1~3:1的聚碳化二亚胺和氯化铜的混合物。
进一步其优化方案为热稳定剂为二甲基二巯基乙酸异辛酯锡。
进一步其优化方案为所述的增韧剂为乙烯-醋酸乙烯酯共聚物。
本发明的制备方法：首先按照上述比例称取各原料，然后将它们加入高速搅拌机中混合均匀，再送至双螺杆挤出机熔融、混炼、挤出，挤出机温度控制在220-240℃，经冷却、切粒、干燥，最后包装，即得本发明产品。
本发明与现有技术相比，其有益效果为：（1）本发明产品机械性能优异，稳定性好；（2）采用复合耐水解剂，使得本发明产品具有良好的耐水性，拓宽了PBT材料的使用范围；（3）添加了纳米氧化锌，不仅提高了本发明产品的稳定性，还使得本发明产品具有一定的抗菌力。
具体实施例
下面结合实施例对本发明作进一步的详细描述。
实施例1
一种耐水解增强型PBT，包括按照重量份数计的如下原料：PBT树脂90份、无碱玻璃纤维10份、碳化硅晶须2份、聚碳化二亚胺0.2份、氯化铜0.1份、纳米氧化锌0.5份、硬脂酸甘油酯0.5份、抗氧剂565 0.4份、抗氧剂626 0.6份、亚磷酸三苯酯0.4份、二甲基二巯基乙酸异辛酯锡0.5份、乙烯-醋酸乙烯酯共聚物3份。
实施例2
一种耐水解增强型PBT，包括按照重量份数计的如下原料：PBT树脂110份、无碱玻璃纤维15份、碳化硅晶须4份、聚碳化二亚胺0.6份、氯化铜0.2份、纳米氧化锌2份、硬脂酸甘油酯2份、抗氧剂565 0.7份、抗氧剂626 0.8份、亚磷酸三苯酯0.6份、二甲基二巯基乙酸异辛酯锡2份、乙烯-醋酸乙烯酯共聚物7份。
实施例3
一种耐水解增强型PBT，包括按照重量份数计的如下原料：PBT树脂100份、无碱玻璃纤维12份、碳化硅晶须3份、聚碳化二亚胺0.5份、氯化铜0.2份、纳米氧化锌1份、硬脂酸甘油酯1.2份、抗氧剂565 0.6份、抗氧剂626 0.7份、亚磷酸三苯酯0.48份、二甲基二巯基乙酸异辛酯锡1.3份、乙烯-醋酸乙烯酯共聚物6份。
对本实施例的产品采用常规微生物杀菌效果检测，其杀菌力结果为：金黄色葡萄球菌75%，大肠杆菌72%，白色念珠菌73%。
对本发明实施例1~3产品性能检测及耐水解性检测，检测结果如表1所示。其中，耐水解性能测试条件为在PCT高速老化试验机，120℃，湿度为100%R.H.，168h冷却后测得。
表1 本实施例1~3产品性能检测数据
Claims (5)
1.一种耐水解增强型PBT，其特征在于包括按照重量份数计的如下原料：PBT树脂90~110份、玻璃纤维10~15份、碳化硅晶须2~4份、复合耐水解剂0.3~0.8份、纳米氧化锌0.5~2份、硬脂酸甘油酯0.5~2份、抗氧剂565 0.4~0.7份、抗氧剂626 0.6~0.8份、亚磷酸三苯酯0.4~0.6份、热稳定剂0.5~2份、增韧剂3~7份。
2.根据权利要求1所述的耐水解增强型PBT，其特征在于所述的玻璃纤维为无碱玻璃纤维。
3.根据权利要求1所述的耐水解增强型PBT，其特征在于所述的复合耐水解剂为质量比为2:1~3:1的聚碳化二亚胺和氯化铜的混合物。
4.根据权利要求1所述的耐水解增强型PBT，其特征在于所述的热稳定剂为二甲基二巯基乙酸异辛酯锡。
5.根据权利要求1所述的耐水解增强型PBT，其特征在于所述的增韧剂为乙烯-醋酸乙烯酯共聚物。