CN103289003B - 一种hpvc树脂材料及其制备方法 - Google Patents

一种hpvc树脂材料及其制备方法 Download PDF

Info

Publication number
CN103289003B
CN103289003B CN201310192983.9A CN201310192983A CN103289003B CN 103289003 B CN103289003 B CN 103289003B CN 201310192983 A CN201310192983 A CN 201310192983A CN 103289003 B CN103289003 B CN 103289003B
Authority
CN
China
Prior art keywords
hpvc
ester
resin material
stearate
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310192983.9A
Other languages
English (en)
Other versions
CN103289003A (zh
Inventor
陈健
张建光
杨文乾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Futong New Material and High Tech Co Ltd
Original Assignee
Wujiang Fengshang Shoe Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wujiang Fengshang Shoe Factory filed Critical Wujiang Fengshang Shoe Factory
Priority to CN201310192983.9A priority Critical patent/CN103289003B/zh
Publication of CN103289003A publication Critical patent/CN103289003A/zh
Application granted granted Critical
Publication of CN103289003B publication Critical patent/CN103289003B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种HPVC树脂材料，由如下重量份的原料组成：PVC单体100份、聚乙二醇二丙烯酸酯0.01～0.02份、马来酸二烯丙酯0.01～0.02份、过氧化二碳酸二（2-乙基己基）酯0.25～0.35份、过氧化二异丁酰0.15～0.32份、聚乙烯醇0.02～0.08份、羟丙基甲基纤维素0.04～0.06份、邻苯二甲酸二辛脂0.01～0.03份、硬脂酸0.02～0.05份、硬脂酸铅0.01～0.02份、硬脂酸钡0.01～0.03份、水15-25份。本发明采用扩链法合成HPVC，可以在比低温法高的聚合温度下生产HPVC，通过实验选择了合适的扩链剂，在70m3聚合装置上生产HPVC树脂并获得成功。聚合配方及生产工艺条件选择合理，生产过程安全，操作方便，产品质量优良。

Description

一种HPVC树脂材料及其制备方法
技术领域
本发明涉及高分子材料领域，具体是一种HPVC树脂材料。
背景技术
聚氯乙烯是我国发展较早、产量最大、应用最广的通用塑料品种之一。普通聚氯乙烯软制品存在力学强度偏低，耐热性、耐寒性差，增塑剂易迁移等缺陷，制约了聚氯乙烯在高档产品中的应用。高聚合度聚氯乙烯(HPVC)通常是指平均聚合度大于1700的聚氯乙烯树脂，HPVC增塑剂吸收量大，其软制品大大改进了普通软PVC制品的力学性能、压缩永久形变、回弹性、耐热性、耐寒性等，因此，其应用更加广泛。
目前，HPVC的合成常用方法为低温法，受到环境温度限制，只能在每年的10月至次年的4月份生产。为满足市场需要，需开发出适合高温季节生产HPVC的生产技术。
发明内容
本发明的目的是提供一种HPVC生产技术，该方法不需要考虑环境温度，可以广泛使用。
一种HPVC树脂材料，其特征在于，由如下重量份的原料组成：PVC单体100份、聚乙二醇二丙烯酸酯0.01～0.02份、马来酸二烯丙酯0.01～0.02份、过氧化二碳酸二(2-乙基己基)酯0.25～0.35份、过氧化二异丁酰0.15～0.32份、聚乙烯醇0.02～0.08份、羟丙基甲基纤维素0.04～0.06份、邻苯二甲酸二辛脂0.01～0.03份、硬脂酸0.02～0.05份、硬脂酸铅0.01～0.02份、硬脂酸钡0.01～0.03份、水15-25份。
上述HPVC树脂材料的制备方法为：HPVC树脂材料的制备方法，其特征在于，将PVC单体、马来酸二烯丙酯、过氧化二碳酸二(2-乙基己基)酯、过氧化二异丁酰、聚乙烯醇、羟丙基甲基纤维素、邻苯二甲酸二辛脂、硬脂酸、硬脂酸铅、硬脂酸钡、水分别加入聚合釜中，经冷搅升温至35～45℃，边搅拌边加入聚乙二醇二丙烯酸酯，2小时后加入丙酮缩氨基硫脲，结束反应，10～15分钟后出料至沉析槽，汽提脱除未反应的PVC单体后，离心干燥、筛分，得HPVC。
本发明采用扩链法合成HPVC，可以在比低温法高的聚合温度下生产HPVC，通过实验选择了合适的扩链剂，在70m3聚合装置上生产HPVC树脂并获得成功。聚合配方及生产工艺条件选择合理，生产过程安全，操作方便，产品质量优良。
具体实施方式
实施例所用原料重量配比如下表：
实施例1 实施例2 实施例3 实施例4 实施例5
PVC单体(份) 100 100 100 100 100
聚乙二醇二丙烯酸酯(份) 0.01 0.02 0.014 0.015 0.08
马来酸二烯丙酯(份) 0.01 0.02 0.013 0.02 0.019
过氧化二碳酸二(2-乙基己基)酯(份) 0.025 0.035 0.027 0.028 0.032
过氧化二异丁酰(份) 0.15 0.32 0.25 0.3 0.18
聚乙烯醇(份) 0.02 0.08 0.04 0.05 0.07
羟丙基甲基纤维素(份) 0.04 0.06 0.05 0.047 0.056
邻苯二甲酸二辛脂(份) 0.01 0.03 0.02 0.015 0.025
硬脂酸(份) 0.02 0.05 0.03 0.04 0.036
硬脂酸铅(份) 0.01 0.02 0.015 0.013 0.018
硬脂酸钡(份) 0.01 0.02 0.012 0.016 0.019
将PVC单体、马来酸二烯丙酯、过氧化二碳酸二(2-乙基己基)酯、过氧化二异丁酰、聚乙烯醇、羟丙基甲基纤维素、邻苯二甲酸二辛脂、硬脂酸、硬脂酸铅、硬脂酸钡、水分别加入聚合釜中，经冷搅升温至35～45℃，边搅拌边加入聚乙二醇二丙烯酸酯，2小时后加入丙酮缩氨基硫脲，结束反应，10～15分钟后出料至沉析槽，汽提脱除未反应的PVC单体后，离心干燥、筛分，得HPVC。
将上述实施例所得样品与低温法生产样品做对比检测，结果如下：
与低温法生产的HPVC树脂相比，链剂法生产的HPVC树脂的增塑剂吸收量和表观密度均更高，这保证了树脂的加工性能；挥发物含量、筛余物、残留氯乙烯含量、白度水平相当，“鱼眼”数更少。

Claims (1)

1.一种HPVC树脂材料，其特征在于：由以下方法制备得到：以重量份计，将氯乙烯单体100份、马来酸二烯丙酯0.02份、过氧化二碳酸二（2-乙基己基）酯0.028份、过氧化二异丁酰0.3份、聚乙烯醇0.05份、羟丙基甲基纤维素0.047份、邻苯二甲酸二辛酯0.015份、硬脂酸0.04份、硬脂酸铅0.013份、硬脂酸钡0.016份、水分别加入聚合釜中，经冷搅升温至35～45℃，边搅拌边加入聚乙二醇二丙烯酸酯0.015份，2小时后加入丙酮缩氨基硫脲，结束反应，10～15分钟后出料至沉析槽，汽提脱除未反应的氯乙烯单体后，离心干燥、筛分，得HPVC。
CN201310192983.9A 2013-05-23 2013-05-23 一种hpvc树脂材料及其制备方法 Expired - Fee Related CN103289003B (zh)