CN103255539A - 一种含有聚酮纤维的抗拉伸防菌面料及其制备工艺 - Google Patents

一种含有聚酮纤维的抗拉伸防菌面料及其制备工艺 Download PDF

Info

Publication number
CN103255539A
CN103255539A CN2013101365535A CN201310136553A CN103255539A CN 103255539 A CN103255539 A CN 103255539A CN 2013101365535 A CN2013101365535 A CN 2013101365535A CN 201310136553 A CN201310136553 A CN 201310136553A CN 103255539 A CN103255539 A CN 103255539A
Authority
CN
China
Prior art keywords
fiber
bismuth
cutting steel
stretch
proof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101365535A
Other languages
English (en)
Other versions
CN103255539B (zh
Inventor
杨小波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Wanqian Clothing Co., Ltd.
Original Assignee
Jinjiang Mingao Textile Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jinjiang Mingao Textile Science & Technology Co Ltd filed Critical Jinjiang Mingao Textile Science & Technology Co Ltd
Priority to CN201310136553.5A priority Critical patent/CN103255539B/zh
Publication of CN103255539A publication Critical patent/CN103255539A/zh
Application granted granted Critical
Publication of CN103255539B publication Critical patent/CN103255539B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种含有聚酮纤维的抗拉伸防菌面料及其制备方法，面料包括以下重量份的原料：5-8份细旦粘胶纤维、22-24份聚乳酸纤维、10-20份纳米竹碳纤维、16-22份聚酮纤维、2-5份纳米二氧化钛、3-8份吸汗速干加工剂、12-18份粘结剂、2-4份的分散剂、3-5份的柔软剂、60-75份涤纶棉纤维。聚酮纤维的加入使得面料具有高拉伸强度、高弹性,该面料可应用于服装、家纺用品、体育用品、卫生用品织物上。

Description

一种含有聚酮纤维的抗拉伸防菌面料及其制备工艺
技术领域
本发明涉及一种含有聚酮纤维的抗拉伸防菌面料及其制备工艺。   
背景技术
近年来，人们对服装面料的舒适性、健康性、安全性和环保性等要求越来越高，对安全高效拉伸强度高的服饰需求越来越多；然而目前高拉伸强度材料添加的成分比较单一，具有的功能也比较单一，没有统一解决舒适、抗拉伸、杀虫、吸汗、保暖等功能。
发明内容
本发明主要解决的技术问题是提供一种含有聚酮纤维的抗拉伸防菌面料，这种面料具有舒适、抗拉伸、杀虫、吸汗、保暖等功能；并且提供了一种该含有聚酮纤维的抗拉伸防菌面料的加工方法，简单、方便、易操作。
一种含有聚酮纤维的抗拉伸防菌面料，包括以下重量份的原料：5-8份细旦粘胶纤维、22-24份聚乳酸纤维、10-20份纳米竹碳纤维、16-22份聚酮纤维、2-5份纳米二氧化钛、3-8份吸汗速干加工剂、12-18份粘结剂、2-4份的分散剂、3-5份的柔软剂、60-75份涤纶棉纤维。
所述纳米二氧化钛的粒径为20-100nm；所述纳米竹碳纤维的长度为200-300nm。
所述的吸汗速干加工剂是由水分散性聚酯、聚氨基甲酸酯、有机硅组成，三者的重量百分比为2：2：1。
含有聚酮纤维的抗拉伸防菌面料的制备工艺，包括以下步骤：
（1）将细旦粘胶纤维、聚乳酸纤维、纳米竹碳纤维、聚酮纤维、纳米二氧化钛、涤纶棉纤维在40-45℃下，加入分散剂、粘结剂、柔软剂，加入100-120份水，混合搅拌均匀，然后晾晒成型；
（2）将上述混合物经过清花、开棉、并条、粗纱、细纱制成功能性纱线条；
（3）将上述功能性纱线条采用针织或机织工艺布匹； 
（4）退浆、水洗、烘干：首先将布匹在0.8-1.2G/L的退浆酶BF-7658中堆置40-50分钟，温度控制在42-44℃，然后使用清水冲洗半小时，最后在烘干机内烘干，温度控制在100-120℃；
（5）吸汗速干加工剂浸渍经过步骤（4）处理过的布匹30-70分钟，然后再在70-80℃下焙烤，最后定型处理。
有益效果
本发明的有益效果是：
（1）    在面料中首次加入聚酮纤维，使面料更加结实耐拉伸；
（2）    加入的纳米二氧化钛无机成分，无毒、无味、无刺激性，热稳定性与耐热性好，不燃烧，且自身为白色。纳米二氧化钛通过与淀粉的完美结合，提高纱线的综合织造性能，减少PVA的用量，煮浆时间短，降低了浆料成本，提高浆纱效益，也解决了PVA浆料不易退浆、环境污染等诸多问题。
（3）    加入吸汗速干加工剂，可以快速吸干身体产生的汗液，减少不适感，并且可以预防潮湿环境下细菌的滋生。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
实施例1
将按照重量份的原料为5份细旦粘胶纤维、22份聚乳酸纤维、10份纳米竹碳纤维、16份聚酮纤维、2份纳米二氧化钛、60份涤纶棉纤维在40℃下，加入2份分散剂、12份粘结剂、3份柔软剂，加入100份水，混合搅拌均匀，然后晾晒成型。纳米二氧化钛的粒径为20nm；纳米竹碳纤维的长度为200nm；。吸汗速干加工剂是由水分散性聚酯、聚氨基甲酸酯、有机硅组成，三者的重量百分比为2：2：1。
然后将上述混合物经过清花、开棉、并条、粗纱、细纱制成功能性纱线条；将成型的功能性纱线条采用针织或机织工艺布匹； 然后将布匹在0.8-1.2G/L的退浆酶BF-7658中堆置40分钟，温度控制在42℃，然后使用清水冲洗半小时，最后在烘干机内烘干，温度控制在100℃；
然后将吸汗速干加工剂浸渍经过步骤（4）处理过的布匹30分钟，然后再在70℃下焙烤，最后定型处理，得到成品面料。
 
实施例2
将按照重量份的原料为8份细旦粘胶纤维、24份聚乳酸纤维、20份纳米竹碳纤维、22份聚酮纤维、3份纳米二氧化钛、75份涤纶棉纤维在42℃下，加入3份分散剂、15份粘结剂、4份柔软剂，加入110份水，混合搅拌均匀，然后晾晒成型。纳米二氧化钛的粒径为60nm；纳米竹碳纤维的长度为250nm。吸汗速干加工剂是由水分散性聚酯、聚氨基甲酸酯、有机硅组成，三者的重量百分比为2：2：1。
然后将上述混合物经过清花、开棉、并条、粗纱、细纱制成功能性纱线条；将成型的功能性纱线条采用针织或机织工艺布匹；然后将布匹在0.8-1.2G/L的退浆酶BF-7658中堆置45分钟，温度控制在43℃，然后使用清水冲洗半小时，最后在烘干机内烘干，温度控制在110℃。
然后将吸汗速干加工剂浸渍经过步骤（4）处理过的布匹50分钟，然后再在75℃下焙烤，最后定型处理，得到成品面料。
实施例3
5-8份细旦粘胶纤维、22-24份聚乳酸纤维、10-20份纳米竹碳纤维、16-22份聚酮纤维、2-5份纳米二氧化钛、3-8份吸汗速干加工剂、12-18份粘结剂、2-4份的分散剂、3-5份的柔软剂、60-75份涤纶棉纤维。
将按照重量份的原料为6份细旦粘胶纤维、23份聚乳酸纤维、15份纳米竹碳纤维、19份聚酮纤维、5份纳米二氧化钛、68份涤纶棉纤维在42℃下，加入4份分散剂、18份粘结剂、5份柔软剂，加入120份水，混合搅拌均匀，然后晾晒成型。其中纳米二氧化钛的粒径为100nm；纳米竹碳纤维的长度为300nm。吸汗速干加工剂是由水分散性聚酯、聚氨基甲酸酯、有机硅组成，三者的重量百分比为2：2：1。
然后将上述混合物经过清花、开棉、并条、粗纱、细纱制成功能性纱线条；将成型的功能性纱线条采用针织或机织工艺布匹； 然后将布匹在0.8-1.2G/L的退浆酶BF-7658中堆置50分钟，温度控制在44℃，然后使用清水冲洗半小时，最后在烘干机内烘干，温度控制在120℃；
然后将吸汗速干加工剂浸渍经过步骤（4）处理过的布匹70分钟，然后再在80℃下焙烤，最后定型处理，得到成品面料。
将制成的成品面料与普通的涤纶棉纤维面料进行比较，分别从表1几个方面进行比较：
表1 制成面料与普通的涤纶棉纤维面料进行比较
比较 柔软度提高率（%） 拉伸度提高率（%） 透气性增加率（%）
实施例1 32 42 56
实施例2 38 43 60
实施例3 35 45 62

Claims (4)

1.一种含有聚酮纤维的抗拉伸防菌面料，其特征在于包括以下重量份的原料：5-8份细旦粘胶纤维、22-24份聚乳酸纤维、10-20份纳米竹碳纤维、16-22份聚酮纤维、2-5份纳米二氧化钛、3-8份吸汗速干加工剂、12-18份粘结剂、2-4份的分散剂、3-5份的柔软剂、60-75份涤纶棉纤维。
2.如权利要求1所述的含有聚酮纤维的抗拉伸防菌面料，所述纳米二氧化钛的粒径为20-100nm；所述纳米竹碳纤维的长度为200-300nm。
3.如权利要求2所述的含有聚酮纤维的抗拉伸防菌面料，所述的吸汗速干加工剂是由水分散性聚酯、聚氨基甲酸酯、有机硅组成，三者的重量百分比为2：2：1。
4.如权利要求1-3任一项所述的含有聚酮纤维的抗拉伸防菌面料的制备工艺，包括以下步骤：
（1）将细旦粘胶纤维、聚乳酸纤维、纳米竹碳纤维、聚酮纤维、纳米二氧化钛、涤纶棉纤维在40-45℃下，加入分散剂、粘结剂、柔软剂，加入100-120份水，混合搅拌均匀，然后晾晒成型；
（2）将上述混合物经过清花、开棉、并条、粗纱、细纱制成功能性纱线条；
（3）将上述功能性纱线条采用针织或机织工艺布匹； 
（4）退浆、水洗、烘干：首先将布匹在0.8-1.2G/L的退浆酶BF-7658中堆置40-50分钟，温度控制在42-44℃，然后使用清水冲洗半小时，最后在烘干机内烘干，温度控制在100-120℃；
（5）吸汗速干加工剂浸渍经过步骤（4）处理过的布匹30-70分钟，然后再在70-80℃下焙烤，最后定型处理。
CN201310136553.5A 2013-04-19 2013-04-19 一种含有聚酮纤维的抗拉伸防菌面料 Active CN103255539B (zh)