CN103224412A - Producing method of meteor shower glaze - Google Patents
Producing method of meteor shower glaze Download PDFInfo
- Publication number
- CN103224412A CN103224412A CN2013101158696A CN201310115869A CN103224412A CN 103224412 A CN103224412 A CN 103224412A CN 2013101158696 A CN2013101158696 A CN 2013101158696A CN 201310115869 A CN201310115869 A CN 201310115869A CN 103224412 A CN103224412 A CN 103224412A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- raw materials
- particulate material
- meteor shower
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a producing method of meteor shower glaze. The method comprises: (1) preparing materials according to the following components by weight parts: 30-40 parts of low-temperature frits, 25-30 parts of feldspar powder, 15-18 parts of quartz powder, 12-15 parts of calcite, 6-10 parts of kaolin, 10-15 parts of zinc oxide and 3-6 parts of talcum powder; (2) performing wet milling for 6-8 hours according to a proportion of the materials : ball : water being 1 : 1.5 : 0.5; (3) sieving the milled glaze with a 160-mesh sieve, adding 1-2 % of particle materials into 100 % of sieved glaze, uniformly stirring, mixing into a glaze slurry of 50-60 Baume degrees, wherein the particle materials is prepared by granulating the following components by weight parts: 60-70 parts of titanium dioxide and 30-40 parts of tannin extract and then sieved with a sieve of 40-100 meshes; and (4) spraying the glaze slurry onto a green body with a smooth surface, drying, and firing to obtain the finish product under an oxidizing atmosphere of 1160-1200 DEG C. The glaze of enamel produced by the method looks like the meteor shower, and thus is close to the nature and relatively strong in appeal.
Description
Technical field
The present invention relates to a kind of making method of meteor shower glaze.
Background technology
At present, in ceramic industry, the moulding of porcelain base is that the allotment of the basic glaze of quality products makes porcelain more dazzling brilliant, the porcelain base of same moulding, often because of the glaze difference, and the vision of crossing the human consumer produces different influences, and the sort of glaze that exactly likes meteor shower makes the porcelain base more lively, press close to the Nature more, product when this also is current porcelain industry a kind of.
Summary of the invention
Technical problem to be solved by this invention provides a kind of glaze that can make and exactly likes meteor shower, makes product press close to the Nature, has the making method of the meteor shower glaze of strong infectivity.
The present invention solves the problems of the technologies described above the technical scheme of being taked: a kind of making method of meteor shower glaze, and the step of this method is as follows: get the raw materials ready according to following component and each component weight part (1): 30 parts ~ 40 parts of low temperature frits; 25 parts ~ 30 parts of Feldspar Powders; 15 parts ~ 18 parts of silica powders; 12 parts ~ 15 parts in calcite; 6 parts ~ 10 parts of kaolin; 10 parts ~ 15 parts in zinc oxide; 3 parts ~ 6 parts of talcum powder; 2) are Aned Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours; (3) glaze behind the ball milling is crossed 160 mesh sieves, adds 1% ~ 2% particulate material in addition and stir in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume; Wherein, particulate material is got the raw materials ready by following component and each component weight part: 60 parts ~ 70 parts of titanium dioxide; 30 parts ~ 40 parts of tannin extracts, particle are got the raw materials ready and are passed through granulation, obtain particulate material behind 40 ~ 100 mesh sieves excessively; (4) get the bright and clean base substrate of appearance and spray this glaze slip drying after, under 1160 ℃ ~ 1200 ℃ oxidizing atmosphere, fire finished product.
After having adopted technique scheme, the present invention has following beneficial effect: by this method experiment repeatedly with found that gained finished product glaze face is mobile strong, wherein the stream grain has flow trace, like meteor shower, allow the people feel the sensation that the various constellation palms are held in the hand, attractive in appearance, lively, make finished product press close to the Nature, have stronger infectivity.
Embodiment
Content of the present invention is easier to be expressly understood that below according to specific embodiment, the present invention is further detailed explanation in order to make,
Embodiment one
A kind of making method of meteor shower glaze, the step of this method is as follows: get the raw materials ready according to following component and each component weight part (1): 30 parts of low temperature frits; 25 parts of Feldspar Powders; 15 parts of silica powders; 12 parts in calcite; 6 parts of kaolin; 10 parts in zinc oxide; 3 parts of talcum powder; (2) are Aned Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours; (3) glaze behind the ball milling is crossed 160 mesh sieves, adds 1% particulate material in addition and stir in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume; Wherein, particulate material is got the raw materials ready by following component and each component weight part: 60 parts of titanium dioxide; 30 parts of tannin extracts, particle are got the raw materials ready and are passed through granulation, obtain particulate material behind 40 ~ 100 mesh sieves excessively; (4) get the bright and clean base substrate of appearance and spray this glaze slip drying after, under 1160 ℃ ~ 1200 ℃ oxidizing atmosphere, fire finished product.
Mobile strong by this method gained finished product glaze face, wherein the stream grain has flow trace, like meteor shower, allows the people feel the sensation that the various constellation palms are held in the hand, and is attractive in appearance, lively, makes finished product press close to the Nature, has stronger infectivity.
Embodiment two
A kind of making method of meteor shower glaze, the step of this method is as follows: get the raw materials ready according to following component and each component weight part (1): 40 parts of low temperature frits; 30 parts of Feldspar Powders; 17 parts of silica powders; 15 parts in calcite; 10 parts of kaolin; 15 parts in zinc oxide; 6 parts of talcum powder; (2) are Aned Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours; (3) glaze behind the ball milling is crossed 160 mesh sieves, adds 2% particulate material in addition and stir in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume; Wherein, particulate material is got the raw materials ready by following component and each component weight part: 70 parts of titanium dioxide; 40 parts of tannin extracts, particle are got the raw materials ready and are passed through granulation, obtain particulate material behind 40 ~ 100 mesh sieves excessively; (4) get the bright and clean base substrate of appearance and spray this glaze slip drying after, under 1160 ℃ ~ 1200 ℃ oxidizing atmosphere, fire finished product.
Mobile strong by this method gained finished product glaze face, wherein the stream grain has flow trace, like meteor shower, allows the people feel the sensation that the various constellation palms are held in the hand, and is attractive in appearance, lively, makes finished product press close to the Nature, has stronger infectivity.
Embodiment three
A kind of making method of meteor shower glaze, the step of this method is as follows: get the raw materials ready according to following component and each component weight part (1): 30 parts ~ 40 parts of low temperature frits; 28 parts of Feldspar Powders; 16 parts of silica powders; 14 parts in calcite; 8 parts of kaolin; 12 parts in zinc oxide; 4 parts of talcum powder; (2) are Aned Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours; (3) glaze behind the ball milling is crossed 160 mesh sieves, adds 1% particulate material in addition and stir in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume; Wherein, particulate material is got the raw materials ready by following component and each component weight part: 65 parts of titanium dioxide; 35 parts of tannin extracts, particle are got the raw materials ready and are passed through granulation, obtain particulate material behind 40 ~ 100 mesh sieves excessively; (4) get the bright and clean base substrate of appearance and spray this glaze slip drying after, under 1160 ℃ ~ 1200 ℃ oxidizing atmosphere, fire finished product.
Mobile strong by this method gained finished product glaze face, wherein the stream grain has flow trace, like meteor shower, allows the people feel the sensation that the various constellation palms are held in the hand, and is attractive in appearance, lively, makes finished product press close to the Nature, has stronger infectivity.
Above-mentioned three embodiment, the value of having got three scopes in upper, middle and lower of each component weight part respectively detects, can draw preparation repeatedly through the experimenter, gained finished product glaze still flowability is very strong, and wherein the stream grain has flow trace, like meteor shower, allow the people feel the sensation that the various constellation palms are held in the hand, attractive in appearance, lively, make finished product press close to the Nature, have stronger infectivity.
Above-described specific embodiment; purpose of the present invention, technical scheme and beneficial effect are further described; institute is understood that; the above only is specific embodiments of the invention; be not limited to the present invention; within the spirit and principles in the present invention all, any modification of being made, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (1)
1. the making method of a meteor shower glaze is characterized in that the step of this method is as follows:
(1) get the raw materials ready according to following component and each component weight part:
30 parts ~ 40 parts of low temperature frits; 25 parts ~ 30 parts of Feldspar Powders;
15 parts ~ 18 parts of silica powders; 12 parts ~ 15 parts in calcite;
6 parts ~ 10 parts of kaolin; 10 parts ~ 15 parts in zinc oxide;
3 parts ~ 6 parts of talcum powder;
(2) are Aned Liao ︰ Qiu ︰ water=1 ︰, 1.5 ︰ 0.5, wet ball grinding 6 ~ 8 hours;
(3) glaze behind the ball milling is crossed 160 mesh sieves, adds 1% ~ 2% particulate material in addition and stir in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume; Wherein, particulate material is got the raw materials ready by following component and each component weight part: 60 parts ~ 70 parts of titanium dioxide; 30 parts ~ 40 parts of tannin extracts, particle are got the raw materials ready and are passed through granulation, obtain particulate material behind 40 ~ 100 mesh sieves excessively;
(4) get the bright and clean base substrate of appearance and spray this glaze slip drying after, under 1160 ℃ ~ 1200 ℃ oxidizing atmosphere, fire finished product.