CN102633535B - Method for preparing gemstone fancy glaze - Google Patents
Method for preparing gemstone fancy glaze Download PDFInfo
- Publication number
- CN102633535B CN102633535B CN 201210081599 CN201210081599A CN102633535B CN 102633535 B CN102633535 B CN 102633535B CN 201210081599 CN201210081599 CN 201210081599 CN 201210081599 A CN201210081599 A CN 201210081599A CN 102633535 B CN102633535 B CN 102633535B
- Authority
- CN
- China
- Prior art keywords
- glaze
- parts
- coat enamel
- ground
- cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A method for preparing gemstone fancy glaze is characterized in that the method includes steps: preparing ground glaze by components including, by weight, from 30 to 40 parts of potassium feldspar, from 15 to 20 parts of quartz, from 12 to 18 parts of calcite, from 16 to 20 parts of clinker, from 10 to 15 parts of iron oxide red, and preparing cover glaze by components including, by weight, from 35 to 40 parts of clinker, from 15 to 20 parts of calcite, from 10 to 20 parts of iron oxide, from 8 to 15 parts of titanium oxide, from 6 to 15 parts of clay and from 0.3 to 0.5 part of cobalt oxide;and realizing wet-method ball milling for the ground glaze and the cover glaze, sieving, preparing glaze slip with the baume degree ranging from 45 to 50, applying the ground glaze on a mud blank, naturally drying the mud blank with the ground glaze, brushing the cover glaze slip onto the mud blank applied with the ground glaze, firing the mud blank at the temperature ranging from 1180 DEG C to 1200 DEG C, and obtaining the gemstone fancy glaze with colors like a gemstone. The gemstone fancy glaze is colorful and is glittering and translucent in texture and brilliant in glossiness.
Description
Technical field
The making method that the present invention relates to ceramic glaze is particularly related to a kind of making method of jewel fancy glaze.
Background technology
Color of gemstones is bright-coloured, and quality is sparkling and crystal-clear, and gloss is magnificent, and rare, is signifying wealth, and the color and luster of jewel is used for the porcelain industry, and the glaze that the Gem flower-shaped three-dimensional jig-saw puzzle color and luster is made on the porcelain surface is difficulty relatively always.
Summary of the invention
Purpose of the present invention provides a kind of making method of jewel fancy glaze, makes porcelain have bright-colored as the jewel and sparkling and crystal-clear quality.
Jewel fancy glaze of the present invention is characterized in that:
(1) by following component and weight percent preparation
A, ground-coat enamel
Potassium felspar sand 30～40 quartz 15～20
Calcite 12～18 frits 16～20
Red iron oxide 10～15
B, cover-coat enamel
Frit 35～40 calcites 15～20
Ferric oxide 10～20 titanium oxide 8～15
Clay 6～15 cobalt oxides 0.3～0.5
(2) ground-coat enamel is by expecting: ball: water equals 1: 2: 0.6, wet ball grinding 18 hours, and the glaze behind the ball milling is crossed 180 mesh sieves, and the glaze slip of furnishing 45～50 degree Beaume is applied on the moulded pottery not yet put in a kiln to bake, and is stand-by after the seasoning;
(3) cover-coat enamel is by expecting: ball: water equals 1: 2: 0.6, wet ball grinding 18 hours, and the glaze behind the ball milling is crossed 180 mesh sieves, and the glaze slip of furnishing 35～40 degree Beaume plots point-like with the cover-coat enamel slurry at the moulded pottery not yet put in a kiln to bake of going up ground-coat enamel, and 1180～1200 ℃ of temperature are fired finished product.
According to this jewel fancy glaze that above technical scheme proposes, color is glittering and translucent, and gloss is bright-coloured, and the people is so fond that will not let out of one's hand, can be used for various tablewares, tea set and porcelain artwork.
Embodiment
Embodiment one
(1) by following component and weight percent preparation
A, ground-coat enamel
Potassium felspar sand 35 quartz 17
Calcite 15 frits 20
Red iron oxide 13
B, cover-coat enamel
Frit 38 calcites 20
Ferric oxide 12 titanium oxide 15
Clay 14.5 cobalt oxides 0.5
(2) ground-coat enamel is by expecting: ball: water equals 1: 2: 0.6, wet ball grinding 18 hours, and the glaze behind the ball milling is crossed 180 mesh sieves, and the glaze slip of furnishing 50 degree Beaume is applied on the moulded pottery not yet put in a kiln to bake, and is stand-by after the seasoning;
(3) cover-coat enamel is by expecting: ball: water equals 1: 2: 0.6, wet ball grinding 18 hours, and the glaze behind the ball milling is crossed 180 mesh sieves, and the glaze slip of furnishing 35～40 degree Beaume plots point-like with the cover-coat enamel slurry at the moulded pottery not yet put in a kiln to bake of going up ground-coat enamel, and 1180～1200 ℃ of temperature are fired finished product.
Embodiment two
(1) by following component and weight percent preparation
A, ground-coat enamel
Potassium felspar sand 40 quartz 16
Calcite 12 frits 17
Red iron oxide 15
B, cover-coat enamel
Frit 40 calcites 20
Ferric oxide 20 titanium oxide 13.7
Clay 6 cobalt oxides 0.3
(2) ground-coat enamel is by expecting: ball: water equals 1: 2: 0.6, wet ball grinding 18 hours, and the glaze behind the ball milling is crossed 180 mesh sieves, and the glaze slip of furnishing 45 degree Beaume is applied on the moulded pottery not yet put in a kiln to bake, and is stand-by after the seasoning;
(3) cover-coat enamel is by expecting: ball: water equals 1: 2: 0.6, wet ball grinding 18 hours, and the glaze behind the ball milling is crossed 180 mesh sieves, and the glaze slip of furnishing 35～40 degree Beaume plots point-like with the cover-coat enamel slurry at the moulded pottery not yet put in a kiln to bake of going up ground-coat enamel, and 1180～1200 ℃ of temperature are fired finished product.
Frit among the present invention program is the general a kind of material of the industry, and from professional production producer, its constitutive material is: silicon-dioxide 50%, potassium felspar sand 20%, lithium lime stone 15%, zinc oxide 10%, quartzy 5%.
Claims (1)
1. the making method of a jewel fancy glaze is characterized in that:
(1) by following component and weight percent preparation
A, ground-coat enamel
Potassium felspar sand 30 ~ 40 quartz 15 ~ 20
Calcite 12 ~ 18 frits 16 ~ 20
Red iron oxide 10 ~ 15
Wherein the component of above-mentioned frit and weight percent are as follows:
Silicon-dioxide 50 potassium felspar sands 20
Lithium lime stone 15 zinc oxide 10
Quartzy 5;
B, cover-coat enamel
Frit 35 ~ 40 calcites 15 ~ 20
Ferric oxide 10 ~ 20 titanium oxide 8 ~ 15
Clay 6 ~ 15 cobalt oxides 0.3 ~ 0.5
Wherein the component of above-mentioned frit and weight percent are as follows:
Silicon-dioxide 50 potassium felspar sands 20
Lithium lime stone 15 zinc oxide 10
Quartzy 5;
(2) ground-coat enamel is by expecting: ball: water equals 1:2:0.6, wet ball grinding 18 hours, and the glaze behind the ball milling is crossed 180 mesh sieves, and the glaze slip of furnishing 45 ~ 50 degree Beaume is applied on the moulded pottery not yet put in a kiln to bake, and is stand-by after the seasoning;
(3) cover-coat enamel is by expecting: ball: water equals 1:2:0.6, wet ball grinding 18 hours, and the glaze behind the ball milling is crossed 180 mesh sieves, and the glaze slip of furnishing 35 ~ 40 degree Beaume plots point-like with the cover-coat enamel slurry at the moulded pottery not yet put in a kiln to bake of going up ground-coat enamel, and 1180 ~ 1200 ℃ of temperature are fired finished product.