CN103205052A - 一种耐高低温的机油滤清器用密封垫 - Google Patents
一种耐高低温的机油滤清器用密封垫 Download PDFInfo
- Publication number
- CN103205052A CN103205052A CN2013101112349A CN201310111234A CN103205052A CN 103205052 A CN103205052 A CN 103205052A CN 2013101112349 A CN2013101112349 A CN 2013101112349A CN 201310111234 A CN201310111234 A CN 201310111234A CN 103205052 A CN103205052 A CN 103205052A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- gasket
- low temperature
- sealing gasket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种耐高低温的机油滤清器用密封垫,按重量份含有以下组分:Vamac G100、防老剂0.5~4、硬脂酸0.5~3、VAM0.2~2。本发明所提供的密封垫具有优良的耐低温和高温性能,并具有优异的物理机械性能。
Description
技术领域
本发明涉及一种滤清器密封垫,尤其涉及一种耐高低温的汽车机油用的滤清器密封垫。
背景技术
机油滤清器位于发动机润滑系统中。它的上游是机油泵,下游是发动机中需要润滑的各零部件。其作用是对来自油底壳的机油中有害杂质进行滤除,以洁净的机油供给曲轴、连杆、凸轮轴、增压器、活塞环等运动副,起到润滑、冷却、清洗作用,从而延长这些零部件的寿命。密封垫是由一个或几个零件组成的罩,固定在轴承的一个套圈或垫圈上并与另一套圈或垫圈接触或形成窄的迷宫间隙,防止润滑油漏出及外物侵入。
在机油滤清器中,密封垫一般用的有选用氟胶做主体材料,其耐高温能达到200度,耐低温能到-20度。但在北方严寒地区,氟胶则会失去其使用性能。造成滤清器漏油。或者用HNBR氢化丁腈橡胶密封垫,如CN102942723A公开了一种用于滤清器底壳与上盖的密封圈,它是由下述原料组成:氯丁橡胶CR121、氢化丁腈橡胶ZP2020(日本瑞翁)、硬酯酸锌、古马隆、2-硫醇基苯骈咪唑、氯化石蜡、半补强炭黑SRF、蒙脱石粉、己二酸酯、促进剂PZ、促进剂TETD、交联剂TAC、防老剂RD、抗氧剂1010、改性硅藻土。或用丁晴橡胶密封垫,如CN102952299A公开的橡胶密封圈的主料包括:28~36重量份的丁晴橡胶2865;辅料包括:10~18重量份的炭黑330、10~18重量份的半补强、1~6重量份的二辛酯、0.35~0.65重量份的氧化锌、0.02~0.05重量份的硫磺、0.2~0.7重量份的硬酸酯、0.3~0.7重量份的防老剂4010NA、0.3~0.7重量份的防老剂RD、0.15~0.3重量份的促进剂T.T.C、2~7重量份的碳酸钙、0.8~1.2重量份的EN-100和0.15~0.25重量份的促进剂DM。
发明内容
本发明的目的在于提供一种能耐高低温的机油滤清器用的橡胶密封垫。本发明所提供的密封垫选取杜邦公司Vamac G为主体材料,耐高温能达到175℃,高温200℃浸泡机油中能短时间工作,耐低温则能达到-40℃。满足北方市场的需求,其价格也远远低于氟胶。
本发明所提供的机油滤清器用密封垫,其特征在于,按重量份含有以下组分:Vamac G100、防老剂0.5~4,例如为0.7份、1.1份、1.5份、2份、2.5份、3.2份、3.8份等、硬脂酸0.5~3,例如为0.7份、0.9份、1.2份、1.6份、2份、2.3份、2.8份等、VAM0.2~2,例如为0.4份、0.6份、0.8份、1.0份、1.3份、1.6份、1.9份等。
Vamac G是一种由乙烯、甲基丙烯酸酯及硫化单体组成的三元共聚物,它的硫化采用的是以胺为基础的橡胶硫化体系。Vamac G共聚物有极佳的抗臭氧、氧气和紫外线的作用。同时,乙烯和甲基丙烯酸酯单体为Vamac G共聚物带来了良好的高温稳定性,乙烯单体还提供了优异的低温柔性;而具有极性的甲基丙烯酸酯和硫化单元则提供了良好的耐油性能。通过乙烯和甲基丙烯酸酯比例的最佳化,可以使产品耐高温性和耐油性得到良好的平衡,从而取得最好的综合性能。Vamac G聚合物的存放期较长,可达几年。
防老剂能防止或抑制诸如氧、热、光、臭氧、机械应力、重金属离子等因素破坏制品性能、延长密封垫储存和使用寿命的配合剂。
硬脂酸即十八烷酸,含18个碳原子的饱和脂肪酸。在本发明中作为硫化活性剂,也可用作增塑剂和软化剂,同时还有脱模剂的作用。
Vam为有机磷酸酯类加工助剂,VAM作为丙烯酸脂中的一种加工助剂,主要起防粘,内脱模剂等作用。
作为优选技术方案,所述的密封垫,按重量份含有以下组分:
作为优选技术方案,所述的密封垫,按重量份含有以下组分:
作为优选技术方案,所述的密封垫,还含有1#硫化剂、促进剂DOTG、填充体系N774、填充体系N550、增塑剂TP-759、防焦剂18D中的一种或两种以上的混合物。优选含有1#硫化剂、促进剂DOTG、填充体系N774、填充体系N550、增塑剂TP-759和防焦剂18D所有的组分。上述助剂的用量本领域技术人员可根据现有知识进行常规选择。
1#硫化剂是六亚甲基二胺氨基甲酸盐,可使橡胶产品保持原来的鲜艳色彩;促进剂DOTG即N,N'-二邻甲苯胍,可提高橡胶制品的硬度并兼具防老化和塑解作用;填充体系选择N774、N550,既保证生胶优异的物理机械性能,同时回弹较好;增塑剂选择TP-759具有优良的耐低温性能;18D为防焦剂,延长混炼胶焦烧时间;本发明所提供的密封垫的组分保证混炼胶一定的含胶率,具有较低的压缩永久变形率,满足使用性能的需求。
作为优选技术方案,所述的密封垫,所述的1#硫化剂的重量份为0.5~3,例如为0.7、1.1、1.6、1.9、2.3、2.6、2.8等,优选为1~2,进一步优选为1.5。
优选地,所述的促进剂DOTG的重量份为1~8,例如为1.5、2、2.6、3.4、4.5、5.6、6.1、6.8、7.5等,优选为2~5,进一步优选为4。
优选地,所述的填充体系N774的重量份为20~60,例如为25、31、35、39、45、52、58等,优选为20~50,进一步优选为30~40。
优选地,所述的填充体系N550的重量份为20~60,例如为25、31、35、39、45、52、58等,20~50,进一步优选为30~40。
优选地,所述的增塑剂TP-759的重量份为1~25,例如为3、6、10、15、19、23等,优选为3~20,进一步优选为5~15。
优选地,所述的防焦剂18D重量份为0.1~2,例如为0.2份、0.4份、0.7份、0.9份、1.3份、1.6份、1.8份等,优选为0.5~1.5,进一步优选为0.5。
作为优选技术方案,所述的密封垫,按重量份含有以下组分:
作为优选技术方案,所述的密封垫,按重量份含有以下组分:
作为优选技术方案,所述的密封垫,按重量份含有以下组分:
本发明所提供的密封垫的制备方法可用常规方法进行制备,如采用CN102952299A公开的方法进行制备。制品硫化后,增加二道硫化工序,可以确保制品充分硫化,具有更优异的物理机械性能。
本发明所提供的橡胶密封垫具有良好的耐低温、高温性能,较好的满足北方市场的需求,回弹性好,具有较低的压缩永久变形率,同时具有优异的物理机械性能。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。
实施例一
按重量份数含有:
实施例二
按重量份数含有:
实施例三
按重量份数含有:
实施例四
按重量份数含有:
实施例五
按重量份数含有:
实施例六
按重量份数含有:
使用性能
对实施例一~六得到的密封垫进行性能测试,测试结果见下表1。
表1
按GB/T1682进行低温试验:-40℃保持3min,观察无龟裂。
从表1及低温性能试验可以看出,本发明的密封垫经过高温、耐油试验后,仍具有优良的物理机械性能,并能经受住较低温而无龟裂。
申请人声明,本发明通过上述实施例来说明本发明的详细工艺设备和工艺流程,但本发明并不局限于上述详细工艺设备和工艺流程,即不意味着本发明必须依赖上述详细工艺设备和工艺流程才能实施。所属技术领域的技术人员应该明了,对本发明的任何改进,对本发明产品各原料的等效替换及辅助成分的添加、具体方式的选择等,均落在本发明的保护范围和公开范围之内。
Claims (8)
3.如权利要求1或2所述的密封垫,其特征在于,按重量份含有以下组分:
4.如权利要求1~3任一项所述的密封垫,其特征在于,还含有1#硫化剂、促进剂DOTG、填充体系N774、填充体系N550、增塑剂TP-759、防焦剂18D中的一种或两种以上的混合物。
5.如权利要求4所述的密封垫,其特征在于,所述的1#硫化剂的重量份为0.5~3,优选为1~2,进一步优选为1.5;
优选地,所述的促进剂DOTG的重量份为1~8,优选为2~5,进一步优选为4;
优选地,所述的填充体系N774的重量份为20~60,优选为20~50,进一步 优选为30~40;
优选地,所述的填充体系N550的重量份为20~60,20~50,进一步优选为30~40;
优选地,所述的增塑剂TP-759的重量份为1~25,优选为3~20,进一步优选为5~15;
优选地,所述的防焦剂18D重量份为0.1~2,优选为0.5~1.5,进一步优选为0.5。
6.如权利要求1~5任一项所述的密封垫,其特征在于,按重量份含有以下组分:
8.如权利要求1~7任一项所述的密封垫,其特征在于,按重量份含有以下组分: