CN103194565A - 一种对含钒铁水同时进行脱磷和提钒的方法 - Google Patents
一种对含钒铁水同时进行脱磷和提钒的方法 Download PDFInfo
- Publication number
- CN103194565A CN103194565A CN2013101538642A CN201310153864A CN103194565A CN 103194565 A CN103194565 A CN 103194565A CN 2013101538642 A CN2013101538642 A CN 2013101538642A CN 201310153864 A CN201310153864 A CN 201310153864A CN 103194565 A CN103194565 A CN 103194565A
- Authority
- CN
- China
- Prior art keywords
- vanadium
- blowing
- hot metal
- dephosphorization
- tfe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (7)