CN103193985A - 一种有机硅平滑剂的制备方法 - Google Patents
一种有机硅平滑剂的制备方法 Download PDFInfo
- Publication number
- CN103193985A CN103193985A CN2012100024280A CN201210002428A CN103193985A CN 103193985 A CN103193985 A CN 103193985A CN 2012100024280 A CN2012100024280 A CN 2012100024280A CN 201210002428 A CN201210002428 A CN 201210002428A CN 103193985 A CN103193985 A CN 103193985A
- Authority
- CN
- China
- Prior art keywords
- preparation
- agent
- reaction
- silicon oil
- carry out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种有机硅平滑剂的制备方法,首先制备超高摩尔质量的羟基硅油,然后通过聚合反应和平衡化反应以及脱低分子处理后,得到羟氨基改性硅油,本发明加工过程简单,所使原料叫少,成本较低,且可使织物具有很好的柔软性、回弹性、蓬松性,且效果明显,具有广阔的市场前景。
Description
技术领域
本发明涉及一种柔软平滑剂技术领域,尤指一种有机硅平滑剂的制备方法。
背景技术
为了使织物具有柔软、滑润或丰满的手感,除了采用机械整理外,还可在纺织品生产的后整理工序中加入柔软平滑剂进行整理。早期的有机硅柔软剂是二甲基硅油与含氢硅油的机械混合物,这种有机硅不含活性基因,与织物结合不够牢固,容易脱落并且手感差。目前市面上的平滑剂多属有机硅柔软平滑剂,此类平滑剂应用效果一般,其柔软性、回弹性、蓬松性都较差,而国内解决这一问题大都采用复配方式,但其较复杂,且效果不明显。
发明内容
为了解决上述问题,本发明提供一种有机硅平滑剂的制备方法,其目的在于使织物具有很好的柔软性、回弹性、蓬松性,且效果明显。
为解决上述技术问题,本发明的技术方案为:一种有机硅平滑剂的制备方法,包括以下步骤:
(1)超高摩尔质量的羟基硅油制备
将含氧基化合物和封头剂按100∶0.2比例混合后,加入催化剂在180℃进行聚合反应10小时后,保持恒温进行平衡化反应,对反应物进行脱低分子处理,最后进行出料,得到超高摩尔质量的羟基硅油;
(2)羟氨基改性硅油制备
将含氧基化合物和封头剂按100∶0.5比例混合后,加入催化剂在180℃进行聚合反应8小时后,加入投料总量的5%比例的硅烷偶联剂进行平衡化反应,在反应物中加入20%比例的上步制得的超高摩尔质量的羟基硅油,在进行平衡化反应后进行中和,后对反应物进行脱低分子处理,制得羟氨基改性硅油,最后进行出料并包装入库。
所述含氧基化合物为D4或DMC。
所述封头剂为MM。
所述催化剂为强碱性无机物。
所述平衡化反应参数为:应温度170-180℃,反应时间8-10小时,反应压力常压。
本发明制备的有机硅平滑剂,加工过程简单,所使原料叫少,成本较低,且可使织物具有很好的柔软性、回弹性、蓬松性,且效果明显,通过该工艺建立新的乳液平衡体系性能稳定,使用操作简单,有效地全面提高了纺织品的服用性和附加值。
具体实施例
实施例1
将DMC和MM按100∶0.2的比例混合后,加入氢氧化钠在180℃进行聚合反应10个小时后,保持恒温进行平衡化反应,对反应物进行脱低分子处理,最后进行出料,得超高摩尔质量的羟基硅油;
将DMC和MM按100∶0.5的比例混合后,加入氢氧化钠在170℃进行聚合反应8个小时后,保持加入投料总量的5%比例的甲基三甲基硅烷进行平衡化反应,在反应物中加入20%比例的上步制得的超高摩尔质量的羟基硅油,在反应温度180℃、反应时间10小时、反应压力常压的条件下进行平衡化反应后,进行中和,后对反应物进行脱低分子处理,得羟氨基改性硅油,最后进行出料并包装入库。
实施例2
将DMC和MM按100∶0.2的比例混合后,加入氢氧化钠在180℃进行聚合反应10个小时后,保持恒温进行平衡化反应,对反应物进行脱低分子处理,最后进行出料,得超高摩尔质量的羟基硅油;
将DMC和MM按100∶0.5的比例混合后,加入氢氧化钠在170℃进行聚合反应8个小时后,保持加入投料总量的5%比例的甲基三甲基硅烷进行平衡化反应,在反应物中加入20%比例的上步制得的超高摩尔质量的羟基硅油,在反应温度170℃、反应时间8小时、反应压力常压的条件下进行平衡化反应后,进行中和,后对反应物进行脱低分子处理,得羟氨基改性硅油,最后进行出料并包装入库。
该产品能够使织物产生超级柔软、平滑、蓬松等手感,尤其能对化学纤维如仿毛、仿丝等织物手感类似于羊毛、蚕丝等手感。
Claims (5)
1.一种有机硅平滑剂的制备方法,包括以下步骤:
(1)超高摩尔质量的羟基硅油制备
将含氧基化合物和封头剂按100∶0.2比例混合后,加入催化剂在180℃进行聚合反应10小时后,保持恒温进行平衡化反应,对反应物进行脱低分子处理,最后进行出料,得到超高摩尔质量的羟基硅油;
(2)羟氨基改性硅油制备
将含氧基化合物和封头剂按100∶0.5比例混合后,加入催化剂在180℃进行聚合反应8小时后,加入投料总量的5%比例的硅烷偶联剂进行平衡化反应,在反应物中加入20%比例的上步制得的超高摩尔质量的羟基硅油,在进行平衡化反应后进行中和,后对反应物进行脱低分子处理,制得羟氨基改性硅油,最后进行出料并包装入库。
2.根据权利要求1所述一种有机硅平滑剂的制备方法,其特征在于:所述含氧基化合物为D4或DMC。
3.根据权利要求1所述一种有机硅平滑剂的制备方法,其特征在于:所述封头剂为MM。
4.根据权利要求1所述一种有机硅平滑剂的制备方法,其特征在于:所述催化剂为强碱性无机物。
5.根据权利要求1所述一种有机硅平滑剂的制备方法,其特征在于:所述平衡化反应参数为反应温度170-180℃反应时间8-10小时,反应压力常压。