CN103172971A - 一种预压用脲醛树脂及其合成工艺 - Google Patents

一种预压用脲醛树脂及其合成工艺 Download PDF

Info

Publication number
CN103172971A
CN103172971A CN2013101005169A CN201310100516A CN103172971A CN 103172971 A CN103172971 A CN 103172971A CN 2013101005169 A CN2013101005169 A CN 2013101005169A CN 201310100516 A CN201310100516 A CN 201310100516A CN 103172971 A CN103172971 A CN 103172971A
Authority
CN
China
Prior art keywords
urea
value
formaldehyde resin
sodium hydroxide
prepressing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101005169A
Other languages
English (en)
Inventor
刘建新
陈东辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HUNAN FUXIANG WOOD INDUSTRY Co Ltd
Original Assignee
HUNAN FUXIANG WOOD INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HUNAN FUXIANG WOOD INDUSTRY Co Ltd filed Critical HUNAN FUXIANG WOOD INDUSTRY Co Ltd
Priority to CN2013101005169A priority Critical patent/CN103172971A/zh
Publication of CN103172971A publication Critical patent/CN103172971A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种预压用脲醛树脂及其合成工艺，包括以下组分：尿素、甲醛、聚乙烯醇、氢氧化钠、氨水和醋酸，所述一种预压用脲醛树脂的合成工艺是：将甲醛加入反应釜内，开启搅拌机，用氢氧化钠调节PH值，然后加入第一批尿素和聚乙烯醇，加热至45-50℃；在40-50min内使温度均匀升至90-95℃，保持30-40min，并且保持PH值为6.0-7.0；用醋酸调节PH值为4.8-5.0，取样测定粘度，当测定值为2.4-2.6秒时，加入第二批尿素，继续反应至粘度达到3.6-3.8秒时，加入氢氧化钠和氨水调节PH值至7.2-7.5，冷却至40-45℃放料，本方法得到的预压用脲醛树脂具有初粘性高、游离醛含量低、毒性小的特点。

Description

一种预压用脲醛树脂及其合成工艺
技术领域
本发明涉及一种预压用脲醛树脂及合成工艺。
背景技术
在人造板的加工过程中，为了提供人造板的质量，预压是必不可少的工艺之一，预压胶大多采用普通的脲醛树脂，现有的脲醛树脂初粘性较低，并且游离醛含量较高，对环境污染较为严重。
发明内容
本发明的目的在于解决现有技术存在的问题，从而提供一种初粘性较高，游离醛含量低，毒性较小的预压用脲醛树脂及其合成工艺。
本发明所解决的技术问题采用以下技术方案来实现：一种预压用脲醛树脂，其特征在于：它由以下重量比的原料配制而成：
尿素           100
甲醛           80-90
聚乙烯醇       15-20
氢氧化钠       2-2.5
氨水           2-2.5
醋酸           2-2.5。
一种预压用脲醛树脂的合成工艺，其特征在于：包括以下步骤：
第一步：将甲醛加入反应釜内，开启搅拌机，用氢氧化钠调节PH值至8.2-8.4，然后加入第一批尿素和聚乙烯醇，加热至45-50℃；
第二步：在40-50min内使温度均匀升至90-95℃，保持30-40min，并且保持PH值为6.0-7.0；
第三步：用醋酸调节PH值为4.8-5.0，取样测定粘度，当测定值为2.4-2.6秒时，加入第二批尿素，继续反应至粘度达到3.6-3.8秒时，立即加入氢氧化钠和氨水调节PH值至7.2-7.5，冷却至40-45℃放料。
本发明采用分批加入尿素的工艺，有利于二羟甲脲的生成，减缓反应速度，使反应完全，达到降低游离醛、提高树脂贮存稳定性的目的，此外，氨水是弱碱，用它作催化剂可以使树脂游离醛降低，并能提高树脂的溶水性能，最后，聚乙烯醇可以增加树酯的初粘性，满足预压要求。
本发明制成的脲醛树脂初粘性高，游离醛含量低，毒性较小。
具体实施方式
下面根据具体实例对本发明作进一步说明：
实施例1
取甲醛80g，加入反应釜内，开启搅拌机，用氢氧化钠调节PH值至8.2，然后加入第一批尿素50g和聚乙烯醇15g，加热至45℃；在40min内使温度均匀升至90℃，保持30min，并且保持PH值为6.0；用醋酸调节PH值至4.8，取样测定粘度，当测定值为2.4秒时，加入第二批尿素50g，继续反应至粘度达到3.6秒时，立即加入氢氧化钠和氨水调节PH值至7.2，冷却至40℃放料。
实施例2
取甲醛85g，加入反应釜内，开启搅拌机，用氢氧化钠调节PH值至8.3，然后加入第一批尿素50g和聚乙烯醇17g，加热至47℃；在47min内使温度均匀升至92℃，保持35min，并且保持PH值为6.5；用醋酸调节PH值至4.9，取样测定粘度，当测定值为2.5秒时，加入第二批尿素50g，继续反应至粘度达到3.7秒时，立即加入氢氧化钠和氨水调节PH值至7.3，冷却至42℃放料。
实施例3
取甲醛90g，加入反应釜内，开启搅拌机，用氢氧化钠调节PH值至8.4，然后加入第一批尿素50g和聚乙烯醇20g，加热至50℃；在50min内使温度均匀升至95℃，保持40min，并且保持PH值为7.0；用醋酸调节PH值至5.0，取样测定粘度，当测定值为2.6秒时，加入第二批尿素50g，继续反应至粘度达到3.8秒时，立即加入氢氧化钠和氨水调节PH值至7.5，冷却至45℃放料。
以上显示和描述了本发明的基本原理和主要特征及本发明的优点，本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内，本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (2)

1.一种预压用脲醛树脂，其特征在于：它由以下重量比的原料配制而成：
尿素           100
甲醛           80-90
聚乙烯醇       15-20
氢氧化钠       2-2.5
氨水           2-2.5
醋酸           2-2.5。
2.一种预压用脲醛树脂的合成工艺，其特征在于：包括以下步骤：
第一步：将甲醛加入反应釜内，开启搅拌机，用氢氧化钠调节PH值至8.2-8.4，然后加入第一批尿素和聚乙烯醇，加热至45-50℃；
第二步：在40-50min内使温度均匀升至90-95℃，保持30-40min，并且保持PH值为6.0-7.0；
第三步：用醋酸调节PH值为4.8-5.0，取样测定粘度，当测定值为2.4-2.6秒时，加入第二批尿素，继续反应至粘度达到3.6-3.8秒时，立即加入氢氧化钠和氨水调节PH值至7.2-7.5，冷却至40-45℃放料。
CN2013101005169A 2013-03-27 2013-03-27 一种预压用脲醛树脂及其合成工艺 Pending CN103172971A (zh)