CN103107331A - 铅酸蓄电池负极板铅膏 - Google Patents

铅酸蓄电池负极板铅膏 Download PDF

Info

Publication number
CN103107331A
CN103107331A CN2012104467593A CN201210446759A CN103107331A CN 103107331 A CN103107331 A CN 103107331A CN 2012104467593 A CN2012104467593 A CN 2012104467593A CN 201210446759 A CN201210446759 A CN 201210446759A CN 103107331 A CN103107331 A CN 103107331A
Authority
CN
China
Prior art keywords
lead
kilogram
kilograms
milliliters
pole plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104467593A
Other languages
English (en)
Inventor
洪银龙
李政东
王先龙
邵浩洲
彭微微
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGXI SWAN STORAGE BATTERY CO Ltd
Original Assignee
GUANGXI SWAN STORAGE BATTERY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGXI SWAN STORAGE BATTERY CO Ltd filed Critical GUANGXI SWAN STORAGE BATTERY CO Ltd
Priority to CN2012104467593A priority Critical patent/CN103107331A/zh
Publication of CN103107331A publication Critical patent/CN103107331A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种铅酸蓄电池负极板铅膏，涉及电化学技术领域，它由下列各组分物质混合而成：铅粉495-505千克，硫酸钡2.49-2.51千克，乙炔炭黑1.04-1.06千克，木素磺酸钠0.3-0.5千克，腐植酸0.99-1.01千克，硫酸29500-30500毫升，纯水58000-62000毫升，短纤维0.34-0.36千克，硬脂酸钡1.05-1.15千克。本发明可以解决蓄电池极板的机械强度低和电性能差的问题。

Description

铅酸蓄电池负极板铅膏
技术领域
本发明涉及电化学技术领域，尤其是一种用于制造铅酸蓄电池负极板的铅膏。
背景技术
混合电动车用电池是电池行业新增的巨大市场。铅酸蓄电池用于混合电动车以及电动车具有极大的优势，其价格低廉、单体电压稳定、安全性能高，且制造基础良好。
蓄电池的核心部件就是极板，极板由板栅和铅膏构成，因而极板的性能好坏直接决定于板栅和铅膏，而铅膏的质量好坏取决于和膏时所用的铅粉和硫酸以及所采用的添加剂。目前的极板还存在着机械强度低和电性能差问题。
发明内容
本发明所要解决的技术问题是提供一种铅酸蓄电池负极板铅膏，它可以解决蓄电池极板的机械强度低和电性能差的问题。
为了解决上述问题，本发明的技术方案是：这种蓄电池负极板铅膏由下列组分的物质混合而成：铅粉495-505千克，硫酸钡2.49-2.51千克，乙炔炭黑1.04-1.06千克，木素磺酸钠0.3-0.5千克，腐植酸0.99-1.01千克，硫酸29500-30500毫升，纯水58000-62000毫升，短纤维0.34-0.36千克，硬脂酸钡1.05-1.15千克。
上述技术方案要中，更为具体的方案还可以是：所述硫酸是密度为1.4±0.005克/毫升的硫酸；所述短纤维是长度为2-4毫米的短纤维。
进一步的：这种铅酸蓄电池负极板铅膏由下列组分的物质混合而成：铅粉495千克，硫酸钡2.51千克，乙炔炭黑1.04千克，木素磺酸钠0.5千克，腐植酸0.99千克，密度为1.4±0.005克/毫升的硫酸30500毫升，纯水58000毫升，短纤维0.36千克，硬脂酸钡1.05千克。
进一步的：这种铅酸蓄电池负极板铅膏由下列组分的物质混合而成：铅粉505千克，硫酸钡2.49千克，乙炔炭黑1.06千克，木素磺酸钠0.3千克，腐植酸1.01千克，密度为1.4±0.005克/毫升的硫酸29500毫升，纯水62000毫升，短纤维0.34千克，硬脂酸钡1.15千克。
由于采用上述技术方案 ，本发明具有如下有益效果：
1、由于在铅膏配方中加入了短纤维，短纤维的加入增强了极板的机械强度。加入短纤维后，在涂板过程中铅膏容易成型，同时也防止了固化干燥过程中极板的开裂和减少了装配过程中极板的脱粉。
2、由于在铅膏配方中加入了硫酸钡，增加了蓄电池放电时硫酸铅的晶核，使得硫酸铅能够快速均匀的凝结在极板的表面，提高了电池的大电流放电能力，尤其是在电池的低温启动性能方面。在加入硫酸钡后，电池的低温启动性能得到了极大地提高。
具体实施方式
下面用实施例对本发明进一步详述：
实施例1：
这种铅酸蓄电池负极板铅膏由下列组分的物质混合而成：铅粉495千克，硫酸钡2.51千克，乙炔炭黑1.04千克，木素磺酸钠0.5千克，腐植酸0.99千克，密度为1.4±0.005克/毫升的硫酸30500毫升，纯水58000毫升，长度为2-4毫米的短纤维0.36千克，硬脂酸钡1.05千克。
实施例2：
这种铅酸蓄电池负极板铅膏由下列组分的物质混合而成：铅粉505千克，硫酸钡2.49千克，乙炔炭黑1.06千克，木素磺酸钠0.3千克，腐植酸1.01千克，密度为1.4±0.005克/毫升的硫酸29500毫升，纯水62000毫升，长度为2-4毫米的短纤维0.34千克，硬脂酸钡1.15千克。
实施例3：
这种铅酸蓄电池负极板铅膏由下列组分的物质混合而成：铅粉500千克，硫酸钡2.5千克，乙炔炭黑1.05千克，木素磺酸钠0.4千克，腐植酸1千克，密度为1.4±0.005克/毫升的硫酸30000毫升，纯水60000毫升，长度为2-4毫米的短纤维0.35千克，硬脂酸钡1.1千克。
实施例4：
这种铅酸蓄电池负极板铅膏由下列各组分物质混合而成：铅粉495千克，硫酸钡2.49千克，乙炔炭黑1.04千克，木素磺酸钠0.3千克，腐植酸0.99千克，密度为1.4±0.005克/毫升的硫酸29500毫升，纯水58000毫升，长度为2-4毫米的短纤维0.34千克，硬脂酸钡1.05千克。
实施例5：
这种铅酸蓄电池的负极板铅膏由下列各组分物质混合而成：铅粉505千克，硫酸钡2.51千克，乙炔炭黑1.06千克，木素磺酸钠0.5千克，腐植酸1.01千克，密度为1.4±0.005克/毫升的硫酸30500毫升，纯水62000毫升，长度为2-4毫米的短纤维0.36千克，硬脂酸钡1.15千克。

Claims (4)

1.一种铅酸蓄电池负极板铅膏，其特征在于：
这种铅酸蓄电池负极板铅膏由下列组分的物质混合而成：铅粉495-505千克，硫酸钡2.49-2.51千克，乙炔炭黑1.04-1.06千克，木素磺酸钠0.3-0.5千克，腐植酸0.99-1.01千克，硫酸29500-30500毫升，纯水58000-62000毫升，短纤维0.34-0.36千克，硬脂酸钡1.05-1.15千克。
2.根据权利要求1所述的铅酸蓄电池负极板铅膏，其特征在于：所述硫酸是密度为1.4±0.005克/毫升的硫酸；所述短纤维是长度为2-4毫米的短纤维。
3.根据权利要求1或2所述的铅酸蓄电池负极板铅膏，其特征在于这种铅酸蓄电池负极板铅膏由下列组分的物质混合而成：铅粉495千克，硫酸钡2.51千克，乙炔炭黑1.04千克，木素磺酸钠0.5千克，腐植酸0.99千克，密度为1.4±0.005克/毫升的硫酸30500毫升，纯水58000毫升，短纤维0.36千克，硬脂酸钡1.05千克。
4.根据权利要求1或2所述的铅酸蓄电池负极板铅膏，其特征在于这种铅酸蓄电池负极板铅膏由下列组分的物质混合而成：铅粉505千克，硫酸钡2.49千克，乙炔炭黑1.06千克，木素磺酸钠0.3千克，腐植酸1.01千克，密度为1.4±0.005克/毫升的硫酸29500毫升，纯水62000毫升，短纤维0.34千克，硬脂酸钡1.15千克。
CN2012104467593A 2012-11-11 2012-11-11 铅酸蓄电池负极板铅膏 Pending CN103107331A (zh)