CN103102602A - 一种耐用型合成橡胶材料 - Google Patents
一种耐用型合成橡胶材料 Download PDFInfo
- Publication number
- CN103102602A CN103102602A CN 201210459392 CN201210459392A CN103102602A CN 103102602 A CN103102602 A CN 103102602A CN 201210459392 CN201210459392 CN 201210459392 CN 201210459392 A CN201210459392 A CN 201210459392A CN 103102602 A CN103102602 A CN 103102602A
- Authority
- CN
- China
- Prior art keywords
- parts
- synthetic rubber
- rubber material
- durable synthetic
- aging agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐用型合成橡胶材料，其由以下重量份数的原料制成：丁基胶5.3-8.6份，氧化锌1.5-3.6份，铂化合物0.82-1.13份，乙烯醋酸乙烯共聚物4.6-7.8份，羟基硅油0.5-1.5份，过氧化二异丙苯0.8-1.3份，硅烷偶联剂0.8-1.5份，防老剂2.6-4.3份。本发明具有好的耐高温性能及优良的导热性能，不仅能进一步提高材料本身的导热性能，也提高了材料在高温环境下的稳定性；配方合理，能耐老化、耐腐蚀，从而能提高使用寿命；易存储，固化后也不容易变黄，还可以显著提高材料的力学性能，从而提高产品的机械强度和密封性能。
Description
技术领域
本发明涉及一种橡胶材料，尤其是涉及一种耐用型合成橡胶材料，属于橡胶生产领域。
背景技术
橡胶护舷是码头或船舶上使用的一种充气或充水用的橡胶缓冲制品。主要用以减缓船舶与码头或船舶之间在靠岸或系泊时的冲击，保护船舶、码头免受损坏。一般由纯橡胶或者橡胶与金属骨架、帘布层组成。用贴合成型法经模压硫化而成，或先模压成型后用硫化罐硫化。橡胶护舷广泛用于港口、码头和船舶上。目前所使用的护舷主要是用废弃的轮胎安装在船体、码头上，虽然能起到隔离的作用，但是由于废弃轮胎的弹性不足，在出现碰撞时还是会损伤船体和码头。针对废弃轮胎，人们也在致力研究其他结构的护舷，但是它们的结构不合理，在碰撞时弹性差，回弹力不足，因此防撞能力差、缓冲性能差；而且在使用过程中，常常还会造成护舷撕裂，从而导致使用寿命短。
发明内容
针对现有技术存在的不足，本发明所要解决的技术问题是，提供一种耐用型合成橡胶材料，耐腐蚀、不易老化、使用寿命长。
为解决上述技术问题，本发明采取的技术方案是，一种耐用型合成橡胶材料，其由以下重量份数的原料制成：
丁基胶5.3-8.6 份，氧化锌1.5-3.6份，铂化合物0.82-1.13份，乙烯醋酸乙烯共聚物4.6-7.8份，羟基硅油0.5-1.5份，过氧化二异丙苯0.8-1.3份，硅烷偶联剂0.8-1.5 份，防老剂2.6-4.3份。
优化的，上述耐用型合成橡胶材料，其由以下重量份数的原料制成：
丁基胶5.3份，氧化锌1.5份，铂化合物0.82份，乙烯醋酸乙烯共聚物4.6份，羟基硅油0.5份，过氧化二异丙苯0.8份，硅烷偶联剂0.8份，防老剂2.6份。
优化的，上述耐用型合成橡胶材料，其由以下重量份数的原料制成：
丁基胶6.6 份，氧化锌2.6份，铂化合物1.03份，乙烯醋酸乙烯共聚物5.8份，羟基硅油0.9份，过氧化二异丙苯1.1份，硅烷偶联剂1.2 份，防老剂3.3份。
优化的，上述耐用型合成橡胶材料，其防老剂为NBC防老剂。
优化的，上述耐用型合成橡胶材料，其羟基硅油的粘度为15-25Pc。
本发明具有好的耐高温性能及优良的导热性能，不仅能进一步提高材料本身的导热性能，也提高了材料在高温环境下的稳定性；配方合理，能耐老化、耐腐蚀，从而能提高使用寿命；易存储，固化后也不容易变黄，还可以显著提高材料的力学性能，从而提高产品的机械强度和密封性能。
具体实施方式
实施例1
本发明为一种耐用型合成橡胶材料，其由以下重量份数的原料制成：
丁基胶5.3份，氧化锌1.5份，铂化合物0.82份，乙烯醋酸乙烯共聚物4.6份，羟基硅油0.5份，过氧化二异丙苯0.8份，硅烷偶联剂0.8份，防老剂2.6份。
防老剂为NBC防老剂。羟基硅油的粘度为15-25Pc。
实施例2
本发明为一种耐用型合成橡胶材料，其由以下重量份数的原料制成：
丁基胶6.6 份，氧化锌2.6份，铂化合物1.03份，乙烯醋酸乙烯共聚物5.8份，羟基硅油0.9份，过氧化二异丙苯1.1份，硅烷偶联剂1.2 份，防老剂3.3份。
防老剂为NBC防老剂。羟基硅油的粘度为15-25Pc。
实施例3
本发明为一种耐用型合成橡胶材料，其由以下重量份数的原料制成：
丁基胶8.6 份，氧化锌3.6份，铂化合物1.13份，乙烯醋酸乙烯共聚物7.8份，羟基硅油1.5份，过氧化二异丙苯1.3份，硅烷偶联剂1.5 份，防老剂4.3份。
防老剂为NBC防老剂。羟基硅油的粘度为15-25Pc。本发明具有好的耐高温性能及优良的导热性能，不仅能进一步提高材料本身的导热性能，也提高了材料在高温环境下的稳定性；配方合理，能耐老化、耐腐蚀，从而能提高使用寿命；易存储，固化后也不容易变黄，还可以显著提高材料的力学性能，从而提高产品的机械强度和密封性能。
当然，上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改型、添加或替换，都应属于本发明的保护范围。
Claims (5)
1.一种耐用型合成橡胶材料，其特征在于：由以下重量份数的原料制成：丁基胶5.3-8.6 份，氧化锌1.5-3.6份，铂化合物0.82-1.13份，乙烯醋酸乙烯共聚物4.6-7.8份，羟基硅油0.5-1.5份，过氧化二异丙苯0.8-1.3份，硅烷偶联剂0.8-1.5 份，防老剂2.6-4.3份。
2.根据权利要求1所述的耐用型合成橡胶材料，其特征在于：由以下重量份数的原料制成：丁基胶5.3份，氧化锌1.5份，铂化合物0.82份，乙烯醋酸乙烯共聚物4.6份，羟基硅油0.5份，过氧化二异丙苯0.8份，硅烷偶联剂0.8份，防老剂2.6份。
3.根据权利要求2所述的耐用型合成橡胶材料，其特征在于：由以下重量份数的原料制成：丁基胶6.6 份，氧化锌2.6份，铂化合物1.03份，乙烯醋酸乙烯共聚物5.8份，羟基硅油0.9份，过氧化二异丙苯1.1份，硅烷偶联剂1.2 份，防老剂3.3份。
4.根据权利要求1所述的耐用型合成橡胶材料，其特征在于：所述防老剂为NBC防老剂。
5.根据权利要求1所述的耐用型合成橡胶材料，其特征在于：所述羟基硅油的粘度为15-25Pc。