CN103100639A - 一种高透气性铸造型砂的制备方法 - Google Patents
一种高透气性铸造型砂的制备方法 Download PDFInfo
- Publication number
- CN103100639A CN103100639A CN2012105268402A CN201210526840A CN103100639A CN 103100639 A CN103100639 A CN 103100639A CN 2012105268402 A CN2012105268402 A CN 2012105268402A CN 201210526840 A CN201210526840 A CN 201210526840A CN 103100639 A CN103100639 A CN 103100639A
- Authority
- CN
- China
- Prior art keywords
- parts
- sand
- plant ash
- gas
- molding sand
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高透气性铸造型砂的制备方法,由以下重量份计的下述组分组成:草木灰颗粒15-20份,矿渣14-21份,玉米面粉10-15份,铸造用原砂20-25份,膨润土6-8份,石灰粉2-5份,羧甲基纤维素3-4份,碳酸氢钠1-3份,稻糠粉0.5-1份,水85-110份,将上述称量好的原料除草木灰颗粒外,加入反应釜内搅拌混合,并加热至120-145℃,持续时间为2-3小时,然后将反应釜内的混合材料倒出,晾干或烘干并加工成粉剂,再与草木灰颗粒混合,即制得。本发明型砂生产的铸件发气量小、烘干时间短、透气性好、干拉强度高,并可改善砂型的脱模性,降低浇注时对水分的敏感性,同时对铸件的粘砂、夹砂、冲砂、气孔等缺陷有显著地改善,能使铸件进一步提高光洁度。
Description
技术领域
本发明涉及铸造型砂制备方法,具体属于一种高透气性铸造型砂的制备方法。
背景技术
在铸造中用来造型的材料。型砂一般由铸造用原砂、型砂粘结剂和辅加物等造型材料按一定的比例混合而成。型砂在铸造生产中的作用极为重要,因型砂的质量不好而造成的铸件废品约占铸件总废品的30~50%。通常对型砂的要求是:1、具有较高的强度和热稳定性,以承受各种外力和高温的作用。2、良好的流动性,即型砂在外力或本身重力作用下砂粒间相互移动的能力。3、一定的可塑性,即型砂在外力作用下变形,当外力去除后能保持所给予的形状的能力。4、较好的透气性,即型砂孔隙透过气体的能力。5、高的溃散性,又称出砂性,即在铸件凝固后型砂是否容易破坏,是否容易从铸件上清除的性能。
发明内容
本发明的目的是提供一种高透气性铸造型砂的制备方法,该型砂生产的铸件发气量小、烘干时间短、透气性好、干拉强度高,并可改善砂型的脱模性,降低浇注时对水分的敏感性,同时对铸件的粘砂、夹砂、冲砂、气孔等缺陷有显著地改善,能使铸件进一步提高光洁度。
本发明的技术方案如下:
一种高透气性铸造型砂的制备方法,由以下重量份计的下述组分组成:草木灰颗粒15-20份,矿渣14-21份,玉米面粉10-15份,铸造用原砂20-25份,膨润土6-8 份,石灰粉2-5 份,羧甲基纤维素3-4份,碳酸氢钠1-3 份,黄壤土5-8,,铅锌矿渣粉1-2,稻糠粉0.5-1 份,水85-110 份,将上述称量好的原料除草木灰颗粒外,加入反应釜内搅拌混合,并加热至120-145℃,持续时间为2-3小时,然后将反应釜内的混合材料倒出,晾干或烘干并加工成粉剂,再与草木灰颗粒混合,即制得;所述的草木灰颗粒采用草木灰加入相当于其重量5-8%的淀粉浆糊、5-9%的三聚磷酸钠粉、适量水混合后造粒即得。
所述草木灰颗粒的粒度为2-5mm。
本发明的制备方法具有如下有益效果:
1、本发明的型砂性能好,具体来说,在铸造过程中,采用该型砂生产的铸件发气量小、烘干时间短、透气性好、干拉强度高,并可改善砂型的脱模性,降低浇注时对水分的敏感性,同时对铸件的粘砂、夹砂、冲砂、气孔等缺陷有显著地改善,能使铸件进一步提高光洁度。
2、所使用原料和配料无毒、无害、无污染,不采用煤粉,车间干净、污染少;采用秸秆粉料、改性淀粉等可再生原料,成本低,浇注时无刺鼻的气味,无粉状吸入物,属于新型环保铸造材料。
具体实施方式
一种高透气性铸造型砂的制备方法,由以下重量份(公斤)计的下述组分组成:草木灰颗粒15,矿渣14,玉米面粉10,铸造用原砂20,膨润土6,石灰粉2,羧甲基纤维素3,碳酸氢钠1,黄壤土5,,铅锌矿渣粉1,稻糠粉0.5,水110 ,将上述称量好的原料除草木灰颗粒外,加入反应釜内搅拌混合,并加热至120-145℃,持续时间为2-3小时,然后将反应釜内的混合材料倒出,晾干或烘干并加工成粉剂,再与草木灰颗粒混合,即制得;所述的草木灰颗粒采用草木灰加入相当于其重量8%的淀粉浆糊、9%的三聚磷酸钠粉、适量水混合后造粒即得,草木灰颗粒的粒度为2-5mm。
利用本发明方法生产的铸造型砂的工艺检测性能为:
湿压强度(MPa):0.092-0.095
透气性100
热湿拉强度(KPa):320-330
破碎指数(j) :80-83%。
Claims (2)
1.一种高透气性铸造型砂的制备方法,其特征在于,由以下重量份计的下述组分组成:草木灰颗粒15-20份,矿渣14-21份,玉米面粉10-15份,铸造用原砂20-25份,膨润土6-8 份,石灰粉2-5 份,羧甲基纤维素3-4份,碳酸氢钠1-3 份,黄壤土5-8,铅锌矿渣粉1-2,稻糠粉0.5-1 份,水85-110 份,将上述称量好的原料除草木灰颗粒外,加入反应釜内搅拌混合,并加热至120-145℃,持续时间为2-3小时,然后将反应釜内的混合材料倒出,晾干或烘干并加工成粉剂,再与草木灰颗粒混合,即制得;所述的草木灰颗粒采用草木灰加入相当于其重量5-8%的淀粉浆糊、5-9%的三聚磷酸钠粉、适量水混合后造粒即得。
2.根据权利要求1所述的高透气性铸造型砂的制备方法,其特征在于,所述草木灰颗粒的粒度为2-5mm。