CN103087670A - 一种紫外及底涂双重固化触摸屏粘胶剂 - Google Patents

一种紫外及底涂双重固化触摸屏粘胶剂 Download PDF

Info

Publication number
CN103087670A
CN103087670A CN2013100074617A CN201310007461A CN103087670A CN 103087670 A CN103087670 A CN 103087670A CN 2013100074617 A CN2013100074617 A CN 2013100074617A CN 201310007461 A CN201310007461 A CN 201310007461A CN 103087670 A CN103087670 A CN 103087670A
Authority
CN
China
Prior art keywords
primary coat
glue paste
ultraviolet
organic solvent
dual cure
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100074617A
Other languages
English (en)
Other versions
CN103087670B (zh
Inventor
颜明发
夏忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN YOUBANG MATERIAL TECHNOLOGY CO., LTD.
Original Assignee
DONGGUAN U-BOND MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN U-BOND MATERIAL TECHNOLOGY Co Ltd filed Critical DONGGUAN U-BOND MATERIAL TECHNOLOGY Co Ltd
Priority to CN201310007461.7A priority Critical patent/CN103087670B/zh
Publication of CN103087670A publication Critical patent/CN103087670A/zh
Application granted granted Critical
Publication of CN103087670B publication Critical patent/CN103087670B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种紫外及底涂双重固化触摸屏粘胶剂，该粘胶剂是由以下质量份的原料组成：30-60份的丙烯酸酯改性橡胶、10-30份的聚氨酯丙烯酸酯、10-40份的活性稀释剂、1-3份的光引发剂、0.5-2份的过氧化物、0.5-2份的抗氧剂。本发明的粘胶剂既可以进行紫外光固化，也可以在底涂的作用下进行还原固化，避免了因为紫外照射不到的地方的固化问题，提高了产品的质量。

Description

一种紫外及底涂双重固化触摸屏粘胶剂
技术领域
本发明涉及一种紫外及底涂双重固化触摸屏粘胶剂。
背景技术
触摸屏早期在组装过程中一般所采用的粘接材料为双面胶带，利用模具将胶带裁剪成适合的形状，进行粘接。由于其使用简便，无需后端的固化流程，在很长的一段时间内受到触摸屏生产厂家的欢迎。
但是随着触摸屏产业化的扩大及品质的提升，双面胶带的缺陷逐渐显现。首先是透光率的问题，从微观的角度来看双面胶带有三个界面，众所周知光在遇到界面时会发生折射，故而大大影响了触摸屏的透光率从而影响终端电子产品的清晰度。其次是返修困难，成品率不高。第三是无法实现高效率的机械操作。
触摸屏粘接胶水的出现有效的解决了这些问题，首先胶水层在固化后只有一个界面，可以大大提升产品的透光率。其次触摸屏粘接胶在生产过程中可以采用先点固化初步固定，检测性能后再完全固化，提升了成品率。第三胶水可以采用专门的机械配合，可以提高生产效率。越来越多的厂家开始认识到触摸屏粘接胶水的优势所在，因此国内外对触摸屏粘接胶的需求也在日益增加。
目前市场上成熟的触摸屏粘接胶水多为单UV固化体系，这存在了一个问题： UV光照射不到的阴影部分的固化。UV固化是指胶水要经过UV光的照射(即紫外线的照射)才能够发生固化反应，但是在实际操作过程中，总会有一些区域无法照射到紫外线即所谓的阴影部分,这些无法照射到UV光的区域胶水会出现了固化不良，甚至于不固化的状况,这对于触摸屏的长期使用埋下了隐患。为解决此问题国外有一些专业的生产粘胶剂生产厂家一直再做研究，但仍未有较为成熟的产品。因此,解决阴影部分固化问题,成为触摸屏胶水行业的急需攻克的技术难点。
发明内容
本发明的目的是提供一种紫外及底涂双重固化触摸屏粘胶剂。
本发明所采取的技术方案是：
一种紫外及底涂双重固化触摸屏粘胶剂，该粘胶剂是由以下质量份的原料组成：30-60份的丙烯酸酯改性橡胶、15-30份的聚氨酯丙烯酸酯、10-40份的活性稀释剂、1-3份的光引发剂、0.5-2份的过氧化物、0.5-2份的抗氧剂。 
所述的活性稀释剂为丙烯酸酯类活性稀释剂、乙烯基类活性稀释剂、乙烯基醚类活性稀释剂、环氧类活性稀释剂。
所述的活性稀释剂包括丙烯酸正丁酯、丙烯酸异辛酯、丙烯酸异癸酯、丙烯酸月桂酯、丙烯酸羟乙酯、甲基丙烯酸羟乙酯、丙烯酸羟丙酯、甲基丙烯酸羟丙酯、聚乙二醇二丙烯酸酯、1，6-己二醇双甲基丙烯酸酯、二缩丙二醇双丙烯酸酯、三缩丙二醇双丙烯酸酯、羟丁基乙烯基醚。
所述的光引发剂包括二苯甲酮、4-甲基二苯甲酮、2,4,6-三甲基二苯甲酮、2-氯硫杂蒽酮、二烷基苯乙酮、1-羟基环己基苯基甲酮、酰基膦氧化物。
所述的过氧化物包括酰类过氧化物、氢过氧化物、二烷基过氧化物、酯类过氧化物、酮类过氧化物、二碳酸酯过氧化物。
所述的抗氧剂为受阻酚类抗氧剂或者亚磷酸酯类抗氧剂。
所述的粘胶剂可被底涂还原固化，所述的底涂是由以下质量份的原料组成：5-50份的还原性有机物质、95-50份的有机溶剂。
所述的还原性有机物质包括有机取代肼、叔胺。
所述的有机溶剂包括脂肪烃类有机溶剂、脂环烃类有机溶剂、醇类有机溶剂、醚类有机溶剂、酯类有机溶剂、酮类有机溶剂、二醇衍生物。
本发明的有益效果是：本发明的粘胶剂既可以进行紫外光固化，也可以在底涂的作用下进行还原固化，避免了因为紫外照射不到的地方的固化问题，提高了产品的质量。
具体实施方式
下面结合具体实施例对本发明做进一步的说明：
实施例1：
一种紫外及底涂双重固化触摸屏粘胶剂，其原料的配方组成如下表1：
Figure 2013100074617100002DEST_PATH_IMAGE002
与此粘胶剂配套使用的底涂的配方组成为：
实施例2：
一种紫外及底涂双重固化触摸屏粘胶剂，其原料的配方组成如下表3：
与此粘胶剂配套使用的底涂的配方组成为：
Figure 2013100074617100002DEST_PATH_IMAGE008
实施例3：
一种紫外及底涂双重固化触摸屏粘胶剂，其原料的配方组成如下表5：
Figure DEST_PATH_IMAGE010
与此粘胶剂配套使用的底涂的配方组成为：
Figure DEST_PATH_IMAGE012
本发明中，所述的粘胶剂及与粘胶剂配套使用的底涂的制备方法为：将各原料混合分散均匀即可。
使用本发明的触摸屏粘胶剂与底涂的方法为：先喷涂底涂，再于底涂上施加粘胶剂从而实现界面粘结。该使用方法和一般的触摸屏UV胶水使用的唯一不同在于：因为本产品可底涂固化，所以先需要施加底涂。
实施例1-3中所用的三元乙丙橡胶—丙烯酸正丁酯接枝物可按照“三元乙丙橡胶—丙烯酸正丁酯接枝物的表征和正交设计在共聚反应中的应用，李凤奎，齐兰英，程蕾，盛京，精细石油化工，1997年1月，No.1，p38-40”中的方法合成。
而实施例1-3中聚氨酯丙烯酸酯的型号为： W2527B。
本发明实施例1的产品性能如下表，
Figure DEST_PATH_IMAGE014

Claims (9)

1.一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：该粘胶剂是由以下质量份的原料组成：30-60份的丙烯酸酯改性橡胶、10-30份的聚氨酯丙烯酸酯、15-40份的活性稀释剂、1-3份的光引发剂、0.5-2份的过氧化物、0.5-2份的抗氧剂。
2.根据权利要求1所述的一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：所述的活性稀释剂为丙烯酸酯类活性稀释剂、乙烯基类活性稀释剂、乙烯基醚类活性稀释剂、环氧类活性稀释剂。
3.根据权利要求1所述的一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：所述的活性稀释剂包括丙烯酸正丁酯、丙烯酸异辛酯、丙烯酸异癸酯、丙烯酸月桂酯、丙烯酸羟乙酯、甲基丙烯酸羟乙酯、丙烯酸羟丙酯、甲基丙烯酸羟丙酯、聚乙二醇二丙烯酸酯、1，6-己二醇双甲基丙烯酸酯、二缩丙二醇双丙烯酸酯、三缩丙二醇双丙烯酸酯、羟丁基乙烯基醚。
4.根据权利要求1所述的一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：所述的光引发剂包括二苯甲酮、4-甲基二苯甲酮、2,4,6-三甲基二苯甲酮、2-氯硫杂蒽酮、二烷基苯乙酮、1-羟基环己基苯基甲酮、酰基膦氧化物。
5.根据权利要求1所述的一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：所述的过氧化物包括酰类过氧化物、氢过氧化物、二烷基过氧化物、酯类过氧化物、酮类过氧化物、二碳酸酯过氧化物。
6.根据权利要求1所述的一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：所述的抗氧剂为受阻酚类抗氧剂或者亚磷酸酯类抗氧剂。
7.根据权利要求1所述的一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：所述的粘胶剂可被底涂还原固化，所述的底涂是由以下质量份的原料组成：5-50份的还原性有机物质、95-50份的有机溶剂。
8.根据权利要求7所述的一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：所述的还原性有机物质包括有机取代肼、叔胺。
9.根据权利要求8所述的一种紫外及底涂双重固化触摸屏粘胶剂，其特征在于：所述的有机溶剂包括脂肪烃类有机溶剂、脂环烃类有机溶剂、醇类有机溶剂、醚类有机溶剂、酯类有机溶剂、酮类有机溶剂、二醇衍生物。
CN201310007461.7A 2013-01-09 2013-01-09 一种紫外及底涂双重固化触摸屏粘胶剂 Active CN103087670B (zh)