CN103056280A - 铸钢件铸造用砂 - Google Patents
铸钢件铸造用砂 Download PDFInfo
- Publication number
- CN103056280A CN103056280A CN 201210517930 CN201210517930A CN103056280A CN 103056280 A CN103056280 A CN 103056280A CN 201210517930 CN201210517930 CN 201210517930 CN 201210517930 A CN201210517930 A CN 201210517930A CN 103056280 A CN103056280 A CN 103056280A
- Authority
- CN
- China
- Prior art keywords
- casting sand
- casting
- weight
- sand
- sodium silicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铸钢件铸造用砂，以水玻璃或改性水玻璃作为粘结剂，所述铸造用砂的主要成分是冶钛废渣60%-70%，占冶钛废渣重量1%-80%的镁砂、1%-15%的氧化钙、1%-65%的三氧化二铝，上述四种成分均匀混合，所述作为粘结剂加入的水玻璃或改性水玻璃加入量为总重量的4%-10%。该铸造用砂成本低，在制芯方面开屏了新的领域，使用该铸造砂生产的铸件尺寸精度高。
Description
技术领域
本发明属于铸造用材料，具体涉及一种铸钢件铸造用砂。
背景技术
铸钢件生产中，特别是大型铸钢件的生产中，铬铁矿砂是防止金属渗透及粘砂的优良面砂，但是我国铬铁矿石资源缺乏，长期依靠进口，不仅价格高而且由于供货得不到保证，严重地影响了铸钢件生产的稳定性，影响了产品的质量。
发明内容
为了克服现有技术领域存在的上述问题，本发明的目的在于，提供一种铸钢件铸造用砂，解决目前的铸造用砂价格高且货源短缺的问题。
本发明提供的铸钢件铸造用砂，以水玻璃或改性水玻璃作为粘结剂，所述铸造用砂的主要成分是冶钛废渣60%-70%，占冶钛废渣重量1%-80%的镁砂、1%-15%的氧化钙、1%-65%的三氧化二铝，上述四种成分均匀混合。所述作为粘结剂加入的水玻璃或改性水玻璃加入量为总重量的4%-10%。
本发明提供的铸钢件铸造用砂，其有益效果在于，该铸造用砂成本低，在制芯方面开屏了新的领域，使用该铸造砂生产的铸件尺寸精度高。
具体实施方式
下面结合实施例，对本发明提供的铸钢件铸造用砂，进行详细的说明。
实施例
本实施例的铸钢件铸造用砂，以水玻璃或改性水玻璃作为粘结剂，所述铸造用砂的主要成分是冶钛废渣60%-70%，占冶钛废渣重量1%-80%的镁砂、1%-15%的氧化钙、1%-65%的三氧化二铝，上述四种成分均匀混合。所述作为粘结剂加入的水玻璃或改性水玻璃加入量为总重量的4%-10%。
将按比例配置的镁砂、氧化钙、三氧化二铝在混砂机中干混2分钟后，再加入水玻璃或改性水玻璃，混半个小时后即可出砂。
Claims (2)
1.一种铸钢件铸造用砂，其特征在于：以水玻璃或改性水玻璃作为粘结剂，所述铸造用砂的主要成分是冶钛废渣60%-70%，占冶钛废渣重量1%-80%的镁砂、1%-15%的氧化钙、1%-65%的三氧化二铝，上述四种成分均匀混合。
2.根据权利要求1所述的铸钢件铸造用砂，其特征在于：所述作为粘结剂加入的水玻璃或改性水玻璃加入量为总重量的4%-10%。