CN103045063A - 一种适合层压的耐温型证件转移涂料 - Google Patents
一种适合层压的耐温型证件转移涂料 Download PDFInfo
- Publication number
- CN103045063A CN103045063A CN2012105638344A CN201210563834A CN103045063A CN 103045063 A CN103045063 A CN 103045063A CN 2012105638344 A CN2012105638344 A CN 2012105638344A CN 201210563834 A CN201210563834 A CN 201210563834A CN 103045063 A CN103045063 A CN 103045063A
- Authority
- CN
- China
- Prior art keywords
- lamination
- temperature
- heat
- solvent
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种适合层压的耐温型证件转移涂料。目前的证件转移涂料大多耐温性差，且耐溶剂性也较差，不适合层压，无法在图层表面直接印刷。本发明适合层压的耐温型证件转移涂料包括下述以重量份计的各组分：树脂10-30；助剂1-10；流变控制剂0-15；助溶剂0-20；乙酸乙酯15-80；所述的树脂为丙烯酸改性树脂、耐高温环氧树脂、缩水甘油型多官能团环氧树脂、脂环族环氧树脂的一种或几种；所述的助剂为消泡剂、成膜助剂或交联剂中的一种或几种；所述的助溶剂为酯类溶剂或醇醚类溶剂。本发明的涂料与同类涂料相比耐温性高，最高层压温度可达到150℃、层压30S，可直接印刷，耐溶剂性好。
Description
技术领域
本发明涉及耐温转移涂料，尤其是一种适合层压的耐温型证件转移涂料。
背景技术
转移镀硫化锌涂料近年来在包装行业得到了广泛应用。大部分使用转移涂料与胶水、纸张等经过涂布、镀硫化锌、复合、印刷等工艺制成包装纸。由于这种包装纸的防伪性好，其应用逐渐向证件领域渗透。其一般是使用转移涂料与胶水、纸张经过涂布、镀硫化锌、上胶、层压工艺印制的。
转移涂料，它不仅要有良好地剥离性以实现基膜与纸张的顺利分离、良好的与铝附着力以确保镀铝效果的完整，而且要有较高的耐温性，即在135℃甚至更高温度的热烫压条件下30S不发生可见的变形。
目前的证件转移涂料大多耐温性差，且耐溶剂性也较差，不适合层压，无法在图层表面直接印刷。
发明内容
本发明所要解决的技术问题是克服上述现有转移涂料耐温性差，提供一种适合层压的耐温型证件转移涂料，其兼具耐溶剂性强、可直接印刷的特点。
为此，本发明采用如下的技术方案：一种适合层压的耐温型证件转移涂料，其包括下述以重量份计的各组分：树脂10-30；助剂1-10；流变控制剂0-15；助溶剂0-20；乙酸乙酯15-80；所述的树脂为丙烯酸改性树脂、耐高温环氧树脂、缩水甘油型多官能团环氧树脂、脂环族环氧树脂的一种或几种；所述的助剂为消泡剂、成膜助剂或交联剂中的一种或几种；所述的助溶剂为酯类溶剂或醇醚类溶剂。
本发明的涂料具有适合层压的特点，层压转移时无毛边、破裂，层压转移成膜性好。层压在图像层上层叠，对图像具有粘着性，形成平滑的表面，而且具有可以对抗密封层变形的刚性。
本发明形成的层压耐高温图层，能够不受墨水的微滴描绘的图层的凹凸的影响，维持表面的平滑状态，印刷后能够赋予图象层光泽，从而可在图层表面直接印刷。
根据中华人民共和国国家标准铝塑复合板G13／T17748-1999国标中对该耐温型证件转移涂料的耐溶剂性的测试，测试次数为50次。比一般的耐高温转移涂料有了很大的提高。
作为优选，所述的丙烯酸改性树脂和耐高温环氧树脂的层压温度Tg≥150℃，形成图层最高层压温度达到150℃、层压30S,形成图层耐溶剂性丁酮擦拭≥50次。
作为优选，所述的消泡剂为有机硅氧烷或聚醚。
作为优选，所述的成膜助剂为丙二醇丁醚或一缩丙二醇甲醚醋酸酯。
作为优选，所述的交联剂为二乙烯基苯或二异氰酸酯。
作为优选，所述的酯类溶剂为乙酸正丙酯或乙酸正丁酯。
作为优选，所述的醇醚类溶剂为丙二醇甲醚。
作为优选，所述的流变控制剂为二氧化硅。
与现有技术相比，本发明具有以下优点：
1）本发明层压转移涂料的耐温性为在150℃甚至更高温度的热烫压条件下30S不发生可见的变形，其耐温性有明显的优势。
2）对本发明耐温型证件转移涂料的耐溶剂性的测试，测试次数为50次。比一般的耐高温转移涂料有了很大的提高。
3）本发明形成的层压耐高温图层，能够不受墨水的微滴描绘的图层的凹凸的影响，维持表面的平滑状态，印刷后能够赋予图象层光泽，从而可在图层表面直接印刷。
具体的实施方式
下面结合具体实施方式对本发明进行详细说明。
实施例1
按照以下组分及含量准备原料：10Kg丙烯酸改性聚氨酯树脂、2Kg耐高温环氧树脂，树脂的软化点≥150℃；0.2Kg消泡剂有机硅氧烷、0.3Kg成膜剂一缩丙二醇甲醚醋酸酯、0.1Kg交联剂二乙烯基苯作为助剂；乙酸乙酯47.4Kg。将上述组分置于反应釜中，加热、搅拌混合反应90min，即得到耐温层压转移涂料。制得的层压耐温转移涂料层压转移性好，形成图层最高模压温度可达到200℃，耐温可到150℃。
将制成的水性转移涂料直接涂布于聚酯(PET)薄膜表面，经适宜温度(90℃～140℃)与时间(5s～15s)的连续烘干固化成膜后，进入真空镀铝机镀硫化锌，然后上C胶 ，与白卡纸通过常用胶水复合并在一定条件下烘干，待复合体冷却至室温后层压转移，剥去最外层的PET薄膜(可多次重复应用于此工艺)，即得具有表面金属光泽鲜艳、可耐150℃以上高温的转移镀硫化锌证卡纸。
实施例2
按照以下组分及含量准备原料：20Kg丙烯酸改性聚氨酯树脂，3Kg缩水甘油型多官能团环氧树脂，树脂的软化点≥150℃；0.3Kg消泡剂有机硅氧烷、0.5Kg成膜剂一缩丙二醇甲醚醋酸酯、0.2Kg交联剂二乙烯基苯作为助剂；乙酸乙酯96Kg。将上述组分置于反应釜中，加热、搅拌混合反应90min，即得到耐温层压转移涂料。制得的层压耐温转移涂料层压转移性好，形成图层最高模压温度可达到200℃，耐温可到155℃。
将制成的水性转移涂料直接涂布于聚酯(PET)薄膜表面，经适宜温度(90℃～140℃)与时间(5s～15s)的连续烘干固化成膜后，进入真空镀铝机镀硫化锌，然后上C胶 ，与白卡纸通过常用胶水复合并在一定条件下烘干，待复合体冷却至室温后层压转移，剥去最外层的PET薄膜(可多次重复应用于此工艺)，即得具有表面金属光泽鲜艳、可耐150℃以上高温的转移镀硫化锌证卡纸。
实施例3
按照以下组分及含量准备原料：10Kg丙烯酸改性聚氨酯树脂、2Kg耐高温环氧树脂，树脂的软化点≥150℃；0.2Kg消泡剂有机硅氧烷、0.3Kg成膜剂一缩丙二醇甲醚醋酸酯、0.1Kg交联剂二乙烯基苯作为助剂；二氧化硅3Kg；乙酸正丙酯1Kg；乙酸乙酯47.4Kg。将上述组分置于反应釜中，加热、搅拌混合反应90min，即得到耐温层压转移涂料。制得的层压耐温转移涂料层压转移性好，形成图层最高模压温度可达到200℃，耐温可到155℃。
实施例4
按照以下组分及含量准备原料：20Kg丙烯酸改性聚氨酯树脂，3Kg缩水甘油型多官能团环氧树脂，树脂的软化点≥150℃；0.3Kg消泡剂有机硅氧烷、0.5Kg成膜剂一缩丙二醇甲醚醋酸酯、0.2Kg交联剂二乙烯基苯作为助剂；二氧化硅3Kg；丙二醇甲醚1Kg；乙酸乙酯96Kg。将上述组分置于反应釜中，加热、搅拌混合反应90min，即得到耐温层压转移涂料。制得的层压耐温转移涂料层压转移性好，形成图层最高模压温度可达到200℃，耐温可到158℃。
Claims (8)
1.一种适合层压的耐温型证件转移涂料，其包括下述以重量份计的各组分：树脂10-30；助剂1-10；流变控制剂0-15；助溶剂0-20；乙酸乙酯15-80；所述的树脂为丙烯酸改性树脂、耐高温环氧树脂、缩水甘油型多官能团环氧树脂、脂环族环氧树脂的一种或几种；所述的助剂为消泡剂、成膜助剂或交联剂中的一种或几种；所述的助溶剂为酯类溶剂或醇醚类溶剂。
2.根据权利要求1所述的适合层压的耐温型证件转移涂料，其特征在于，所述的丙烯酸改性树脂和耐高温环氧树脂的层压温度Tg≥150℃，形成图层最高层压温度达到150℃、层压30S,形成图层耐溶剂性丁酮擦拭≥50次。
3.根据权利要求l所述的适合层压的耐温型证件转移涂料，其特征在于，所述的消泡剂为有机硅氧烷或聚醚。
4.根据权利要求l所述的适合层压的耐温型证件转移涂料，其特征在于，所述的成膜助剂为丙二醇丁醚或一缩丙二醇甲醚醋酸酯。
5.根据权利要求l所述的适合层压的耐温型证件转移涂料，其特征在于，所述的交联剂为二乙烯基苯或二异氰酸酯。
6.根据权利要求l所述的适合层压的耐温型证件转移涂料，其特征在于，所述的酯类溶剂为乙酸正丙酯或乙酸正丁酯。
7.根据权利要求l所述的适合层压的耐温型证件转移涂料，其特征在于，所述的醇醚类溶剂为丙二醇甲醚。
8.根据权利要求l所述的适合层压的耐温型证件转移涂料，其特征在于，所述的流变控制剂为二氧化硅。