CN103030774A - 一种有机硅改性阳离子水性聚氨酯的制备方法 - Google Patents

一种有机硅改性阳离子水性聚氨酯的制备方法 Download PDF

Info

Publication number
CN103030774A
CN103030774A CN2012105219745A CN201210521974A CN103030774A CN 103030774 A CN103030774 A CN 103030774A CN 2012105219745 A CN2012105219745 A CN 2012105219745A CN 201210521974 A CN201210521974 A CN 201210521974A CN 103030774 A CN103030774 A CN 103030774A
Authority
CN
China
Prior art keywords
preparation
aqueous polyurethane
silicon
organic
performed polymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012105219745A
Other languages
English (en)
Inventor
苏建丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Wenchuang Technology Co Ltd
Original Assignee
Qingdao Wenchuang Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Wenchuang Technology Co Ltd filed Critical Qingdao Wenchuang Technology Co Ltd
Priority to CN2012105219745A priority Critical patent/CN103030774A/zh
Publication of CN103030774A publication Critical patent/CN103030774A/zh
Pending legal-status Critical Current

Abstract

一种有机硅改性阳离子水性聚氨酯的制备方法，是以TDI、N220、羟基改性硅油为原料制备预聚体，加入封闭剂甲乙酮肟，加入冰醋酸搅拌，加入适量的去离子水制得有机硅改性的阳离子水性聚氨酯乳液。本发明得到的水性聚氨酯成膜后具有较好的手感、耐水性及粘结性。

Description

一种有机硅改性阳离子水性聚氨酯的制备方法
技术领域
本发明涉及一种有机硅改性阳离子水性聚氨酯的制备方法，属化工领域。
技术背景        
随着人们环保意识的增强和各国政府的环保立法。水性聚氨酯正逐步取代溶剂型聚氨酯成为聚氨酯工业发胀的重要方向。目前，水性聚氨酯已经成功的应用于纺织印染行业。封闭型水性聚氨酯作为一类特殊的内交联型水性聚氨酯，具有特殊的性能能和广阔的应用前景，已经受到国内外科研人员的广泛关注。但是作为反应性树脂，其缺点是整理后织物手感会变差、发僵、发硬。
由于有机硅的的主链十分柔软，因此被广泛的应用于水性聚氨酯的改性。若将有机硅引入水性聚氨酯分子中，可使二者性能互补，既无损聚氨酯的固有特性，又具有低的玻璃化转变温度和低表面能。
发明内容
本发明的目的是提供一种有机硅改性阳离子水性聚氨酯的制备方法，得到的水性聚氨酯具有很好的耐寒性、耐水性及粘结性。
为实现以上目的，本发明的一种有机硅改性阳离子水性聚氨酯的制备方法，其步骤具体为：
(1) 以甲苯二异氰酸酯(TDI)、聚醚二醇(N220)、羟基改性硅油为原料制备预聚体，反应2h。
(2) 加入封闭剂甲乙酮肟对预聚体封端，反应50min。
(3) 降温至40℃，加入冰醋酸搅拌，反应3-4min。
(4) 加入水进行乳化60min，得到有机硅改性的阳离子水性聚氨酯乳液。
步骤(1)中预聚体原料的配比为：TDI与N220的摩尔比为1.3:1-1.4:1，羟基改性硅油占预聚体质量的20%-25%。
步骤(2)中甲乙酮肟的物质的量与过量-NCO的物质的量的比值为0.35。
步骤(3)中冰醋酸的物质的量与甲乙酮肟的物质的量相同。
步骤(4)中水的用量为预聚体总质量的2倍。
本发明产生的有益效果为，本专利采用有机硅改性水性聚氨酯，有机硅中含有高键能的硅氧键，并且有机硅氧烷的单分子体积大、内聚能密度低，故将有机硅引入聚氨酯分子的主链或侧链中，有利于提高胶黏剂的耐热性、耐寒性和耐候性等性能；与此同时，有机硅的主链十分柔软，引入有机硅后，制得的聚氨酯涂膜具有较好的手感。
实施例
实施例1：
以甲苯二异氰酸酯(TDI)、聚醚二醇(N220)、羟基改性硅油为原料制备预聚体，反应2h。TDI与N220的摩尔比为1.3:1，羟基改性硅油占预聚体质量的20%。加入封闭剂甲乙酮肟对预聚体封端，反应50min。甲乙酮肟的物质的量与过量-NCO的物质的量的比值为0.35。降温至40℃，加入冰醋酸搅拌，反应3min。冰醋酸的物质的量与甲乙酮肟的物质的量相同。加入水进行乳化60min，水的用量为预聚体总质量的2倍。得到有机硅改性的阳离子水性聚氨酯乳液。
实施例2：
以甲苯二异氰酸酯(TDI)、聚醚二醇(N220)、羟基改性硅油为原料制备预聚体，反应2h。TDI与N220的摩尔比为1.35:1，羟基改性硅油占预聚体质量的22%。加入封闭剂甲乙酮肟对预聚体封端，反应50min。甲乙酮肟的物质的量与过量-NCO的物质的量的比值为0.35。降温至40℃，加入冰醋酸搅拌，反应3min。冰醋酸的物质的量与甲乙酮肟的物质的量相同。加入水进行乳化60min，水的用量为预聚体总质量的2倍。得到有机硅改性的阳离子水性聚氨酯乳液。
实施例3：
以甲苯二异氰酸酯(TDI)、聚醚二醇(N220)、羟基改性硅油为原料制备预聚体，反应2h。TDI与N220的摩尔比为1.4:1，羟基改性硅油占预聚体质量的25%。加入封闭剂甲乙酮肟对预聚体封端，反应50min。甲乙酮肟的物质的量与过量-NCO的物质的量的比值为0.35。降温至40℃，加入冰醋酸搅拌，反应3min。冰醋酸的物质的量与甲乙酮肟的物质的量相同。加入水进行乳化60min，水的用量为预聚体总质量的2倍。得到有机硅改性的阳离子水性聚氨酯乳液。

Claims (5)

1.一种有机硅改性阳离子水性聚氨酯的制备方法，其特征在于：步骤如下：
(1) 以甲苯二异氰酸酯(TDI)、聚醚二醇(N220)、羟基改性硅油为原料制备预聚体，反应2h；
(2) 加入封闭剂甲乙酮肟对预聚体封端，反应50min；
(3) 降温至40℃，加入冰醋酸搅拌，反应3-4min；
(4) 加入水进行乳化60min，得到有机硅改性的阳离子水性聚氨酯乳液。
2.如权利要求1所述的一种有机硅改性阳离子水性聚氨酯的制备方法，其特征在于：所述的步骤(1)中预聚体原料的配比为：TDI与N220的摩尔比为1.3:1-1.4:1，羟基改性硅油占预聚体质量的20%-25%。
3.如权利要求1所述的一种有机硅改性阳离子水性聚氨酯的制备方法，其特征在于：所述的步骤(2)中甲乙酮肟的物质的量与过量-NCO的物质的量的比值为0.35。
4.如权利要求1所述的一种有机硅改性阳离子水性聚氨酯的制备方法，其特征在于：所述的步骤(3)中冰醋酸的物质的量与甲乙酮肟的物质的量相同。
5.如权利要求1所述的一种有机硅改性阳离子水性聚氨酯的制备方法，其特征在于：所述的步骤(4)中水的用量为预聚体总质量的2倍。
CN2012105219745A 2012-12-07 2012-12-07 一种有机硅改性阳离子水性聚氨酯的制备方法 Pending CN103030774A (zh)