CN103013296A - 一种含有改性凹凸棒土的粉末涂料及其制备方法 - Google Patents

一种含有改性凹凸棒土的粉末涂料及其制备方法 Download PDF

Info

Publication number
CN103013296A
CN103013296A CN2012105342453A CN201210534245A CN103013296A CN 103013296 A CN103013296 A CN 103013296A CN 2012105342453 A CN2012105342453 A CN 2012105342453A CN 201210534245 A CN201210534245 A CN 201210534245A CN 103013296 A CN103013296 A CN 103013296A
Authority
CN
China
Prior art keywords
powder coating
resin
powder
epoxy
modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105342453A
Other languages
English (en)
Other versions
CN103013296B (zh
Inventor
王新志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHUZHOU HONGYUAN SPRAYING Co Ltd
Original Assignee
CHUZHOU HONGYUAN SPRAYING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHUZHOU HONGYUAN SPRAYING Co Ltd filed Critical CHUZHOU HONGYUAN SPRAYING Co Ltd
Priority to CN201210534245.3A priority Critical patent/CN103013296B/zh
Publication of CN103013296A publication Critical patent/CN103013296A/zh
Application granted granted Critical
Publication of CN103013296B publication Critical patent/CN103013296B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有改性凹凸棒土的粉末涂料及其制备方法，其组成原料为：改性环氧树脂、环氧化聚丁二烯树脂、线型低密度聚乙烯树脂、改性凹凸棒土、聚乙烯蜡粉、成膜树脂、聚二甲基硅氧烷、高色素炭黑、甲基丙烯酸树脂、纳米二氧化硅、三乙烯四胺、抗氧剂DLTP、二苯胺和偏苯三酸三辛酯；本发明粉末涂料为绿色环保型涂料，无毒，耐高温，不含溶剂，无VOC排放，而且本发明中添加了改性凹凸棒土，增强了改性环氧树脂、环氧化聚丁二烯树脂和线型低密度聚乙烯树脂的混溶性，改进了粉末涂料的表面流平，具有高保光性，提高了粉末涂料的装饰性；制备得到的成品合格率高，可实现工业化大生产。

Description

一种含有改性凹凸棒土的粉末涂料及其制备方法
技术领域
本发明涉及粉末涂料领域，尤其涉及一种含有改性凹凸棒土的粉末涂料及其制备方法。
背景技术
随着我国经济的持续稳定增长以及人民生活水平的不断提高，金属构件的粉末涂装业务也不断增加，尤其是家用电器、仪器仪表、交通设施、铝型材、各种车辆以及日用五金等行业，粉末涂层能给金属提供优良的防腐保护及装饰性能，但由于用于上述领域的现有涂料的抗污染性能不理想，涂层上经常附着各类灰尘、污垢甚至是油污；抗粘贴能力也不理想，且现有粉末涂料形成的涂层在户外长期暴晒、雨淋等自然条件影响下易出现起泡、开裂、剥离等现象，因此，涂层的机械性能也不理想。
发明内容
本发明所要解决的技术问题是克服现有技术的不足，提供一种含有改性凹凸棒土的粉末涂料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
含有改性凹凸棒土的粉末涂料，其组成原料的重量份为：改性环氧树脂33-38、环氧化聚丁二烯树脂  13-15、线型低密度聚乙烯树脂4-6、改性凹凸棒土2-4、聚乙烯蜡粉0.7-1.0、成膜树脂1.5-2.5、聚二甲基硅氧烷0.8-1.5、高色素炭黑0.9-1.1、甲基丙烯酸树脂0.6-0.8、纳米二氧化硅37-39、三乙烯四胺3-5、抗氧剂DLTP 0.5-0.7、二苯胺0.2-0.4和偏苯三酸三辛酯0.6-0.8。
含有改性凹凸棒土的粉末涂料，其组成原料的重量份为：改性环氧树脂35、环氧化聚丁二烯树脂  14、线型低密度聚乙烯树脂5、改性凹凸棒土3、聚乙烯蜡粉0.8、成膜树脂2、聚二甲基硅氧烷1.2、高色素炭黑1、甲基丙烯酸树脂0.7、纳米二氧化硅8、三乙烯四胺4、抗氧剂DLTP 0.6、二苯胺0.3和偏苯三酸三辛酯0.7。
含有改性凹凸棒土的粉末涂料的制备方法，包括以下步骤：
（1）成膜树脂的制备：按组成配方尿素3-5、聚乙烯蜡5-7、聚对苯二甲酸二乙酯3-5、聚乙二醇4-6、锌粉0.2-0.3、甘油0.3-0.5、环氧硬脂酸辛酯3-5、苯乙烯2-3、过氧化苯甲酸叔丁酯0.2-0.3和氧化锌0.3-0.5；制成方法如下：
a：将聚乙烯蜡、聚对苯二甲酸二乙酯、聚乙二醇、甘油、环氧硬脂酸辛酯、苯乙烯加入不锈钢反应釜，升温至110±5℃，开动搅拌加入尿素、过氧化苯甲酸叔丁酯、氧化锌、锌粉；
b：然后以50-60℃/小时速率升温到180-195℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：85±5℃；二区温度控制在：95±5℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成180-220目的粉末，包装入库，粉末固化条件为：固化温度180-190℃，烘烤15-20分钟。
所述的改性环氧树脂的制备方法如下：
配方：E-12环氧树脂60-70、SG-2型聚氯乙烯10-12、二甲苯20-25、二茂铁1-2、聚异丁烯6-8、桐油酸酐5-8、苄基三乙基溴化铵2-3、氢氧化铝3-5、松香10-12、尿素8-10、氧化锌5-8、2.4.6-三（二甲胺基甲基）苯酚10-12、二氯过氧化苯甲酰0.2-0.4、过氧化苯甲酸叔丁酯0.2-0.4、甲基三乙氧基硅烷1-2、抗氧剂1010 1-2；
制备方法如下：
（1）、将E-12环氧树脂、SG-2型聚氯乙烯加热至110-120℃熔化；600-800转/分搅拌；
（2）、加入二茂铁、氢氧化铝、桐油酸酐，升温至150-160℃，400-600转/分高速搅拌搅拌，反应1-2小时，
（3）、加入其它物料，升温至180-200℃，800-1000转/分高速搅拌，保温反应1-2小时，冷却；干燥、脱去有机溶剂二甲苯，得到改性环氧树脂。
所述的改性凹凸棒土的制备方法为：将凹凸棒土用10-15%的氢氧化钠溶液浸泡2-3小时后；再用10-15%盐酸溶液浸泡2-3小时；然后去离子水洗涤多次，至凹凸棒土为中性，烘干；最后研磨为0.8-1.2μm粉末，得到改性凹凸棒土。
本发明的优点：
本发明粉末涂料为绿色环保型涂料，无毒，耐高温，不含溶剂，无VOC 排放，而且本发明中添加了改性凹凸棒土，增强了改性环氧树脂、环氧化聚丁二烯树脂和线型低密度聚乙烯树脂的混溶性，改进了粉末涂料的表面流平，具有高保光性，提高了粉末涂料的装饰性；制备得到的成品合格率高，可实现工业化大生产。
具体实施方式
实施例1：含有改性凹凸棒土的粉末涂料，其组成原料的重量份（kg）为：改性环氧树脂35、环氧化聚丁二烯树脂  14、线型低密度聚乙烯树脂5、改性凹凸棒土3、聚乙烯蜡粉0.8、成膜树脂2、聚二甲基硅氧烷1.2、高色素炭黑1、甲基丙烯酸树脂0.7、纳米二氧化硅38、三乙烯四胺4、抗氧剂DLTP 0.6、二苯胺0.3和偏苯三酸三辛酯0.7。
含有改性凹凸棒土的粉末涂料的制备方法，包括以下步骤：
（1）成膜树脂的制备：按组成配方（kg）尿素4、聚乙烯蜡6、聚对苯二甲酸二乙酯4、聚乙二醇5、锌粉0.25、甘油0.4、环氧硬脂酸辛酯4、苯乙烯2.5、过氧化苯甲酸叔丁酯0.25和氧化锌0.4；制成方法如下：
a：将聚乙烯蜡、聚对苯二甲酸二乙酯、聚乙二醇、甘油、环氧硬脂酸辛酯、苯乙烯加入不锈钢反应釜，升温至110±5℃，开动搅拌加入尿素、过氧化苯甲酸叔丁酯、氧化锌、锌粉；
b：然后以50-60℃/小时速率升温到180-195℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：85±5℃；二区温度控制在：95±5℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成200目的粉末，包装入库，粉末固化条件为：固化温度180-190℃，烘烤15-20分钟。
所述的改性环氧树脂的制备方法如下：
配方（kg）：E-12环氧树脂65、SG-2型聚氯乙烯11、二甲苯22、二茂铁1.5、聚异丁烯7、桐油酸酐6.5、苄基三乙基溴化铵2.5、氢氧化铝4、松香11、尿素9、氧化锌7、2.4.6-三（二甲胺基甲基）苯酚11、二氯过氧化苯甲酰0.3、过氧化苯甲酸叔丁酯0.3、甲基三乙氧基硅烷1.5、抗氧剂1010 1.5；
制备方法如下：
（1）、将E-12环氧树脂、SG-2型聚氯乙烯加热至110-120℃熔化；600-800转/分搅拌；
（2）、加入二茂铁、氢氧化铝、桐油酸酐，升温至150-160℃，400-600转/分高速搅拌搅拌，反应1-2小时，
（3）、加入其它物料，升温至180-200℃，800-1000转/分高速搅拌，保温反应1-2小时，冷却；干燥、脱去有机溶剂二甲苯，得到改性环氧树脂。
所述的改性凹凸棒土的制备方法为：将凹凸棒土用10%的氢氧化钠溶液浸泡2-3小时后；再用10%盐酸溶液浸泡2-3小时；然后去离子水洗涤多次，至凹凸棒土为中性，烘干；最后研磨为0.8-1.2μm粉末，得到改性凹凸棒土。
    将该粉末涂料采用静电喷涂施工方法作用于经喷涂处理的冰箱外壳表面上，经180℃的充分固化，自然冷却至室温，放置24h 后，测定涂层性能，其涂层冲击强度≥ 88cm，耐盐雾时间≥ 2900h，人工加速老化时间≥ 3100h，耐热性能≥585，天然曝晒13个月不起泡、不生锈、不开裂、不剥离，对油污的分解率≥98.5%。

Claims (5)

1.一种含有改性凹凸棒土的粉末涂料，其特征在于其组成原料的重量份为：改性环氧树脂33-38、环氧化聚丁二烯树脂  13-15、线型低密度聚乙烯树脂4-6、改性凹凸棒土2-4、聚乙烯蜡粉0.7-1.0、成膜树脂1.5-2.5、聚二甲基硅氧烷0.8-1.5、高色素炭黑0.9-1.1、甲基丙烯酸树脂0.6-0.8、纳米二氧化硅37-39、三乙烯四胺3-5、抗氧剂DLTP 0.5-0.7、二苯胺0.2-0.4和偏苯三酸三辛酯0.6-0.8。
2.根据权利要求1所述的含有改性凹凸棒土的粉末涂料，其特征在于其组成原料的重量份为：改性环氧树脂35、环氧化聚丁二烯树脂  14、线型低密度聚乙烯树脂5、改性凹凸棒土3、聚乙烯蜡粉0.8、成膜树脂2、聚二甲基硅氧烷1.2、高色素炭黑1、甲基丙烯酸树脂0.7、纳米二氧化硅38、三乙烯四胺4、抗氧剂DLTP 0.6、二苯胺0.3和偏苯三酸三辛酯0.7。
3.一种如权利要求1所述的含有改性凹凸棒土的粉末涂料的制备方法，其特征在于包括以下步骤：
（1）成膜树脂的制备：按组成配方尿素3-5、聚乙烯蜡5-7、聚对苯二甲酸二乙酯3-5、聚乙二醇4-6、锌粉0.2-0.3、甘油0.3-0.5、环氧硬脂酸辛酯3-5、苯乙烯2-3、过氧化苯甲酸叔丁酯0.2-0.3和氧化锌0.3-0.5；制成方法如下：
a：将聚乙烯蜡、聚对苯二甲酸二乙酯、聚乙二醇、甘油、环氧硬脂酸辛酯、苯乙烯加入不锈钢反应釜，升温至110±5℃，开动搅拌加入尿素、过氧化苯甲酸叔丁酯、氧化锌、锌粉；
b：然后以50-60℃/小时速率升温到180-195℃；反应1-2小时停止加热得到；
（2）按组成原料的重量份称取各原料，然后配料并放入混合机内混合，将混合好的混合料放入双螺杆挤出机挤出，挤出机的一区温度控制在：85±5℃；二区温度控制在：95±5℃；挤出后的片状料冷却后，投入到粉碎机内粉碎、研磨成180-220目的粉末，包装入库，粉末固化条件为：固化温度180-190℃，烘烤15-20分钟。
4.根据权利要求1所述的含有改性凹凸棒土的粉末涂料，其特征在于：所述的改性环氧树脂的制备方法如下：
配方：E-12环氧树脂60-70、SG-2型聚氯乙烯10-12、二甲苯20-25、二茂铁1-2、聚异丁烯6-8、桐油酸酐5-8、苄基三乙基溴化铵2-3、氢氧化铝3-5、松香10-12、尿素8-10、氧化锌5-8、2.4.6-三（二甲胺基甲基）苯酚10-12、二氯过氧化苯甲酰0.2-0.4、过氧化苯甲酸叔丁酯0.2-0.4、甲基三乙氧基硅烷1-2、抗氧剂1010 1-2；
制备方法如下：
（1）、将E-12环氧树脂、SG-2型聚氯乙烯加热至110-120℃熔化；600-800转/分搅拌；
（2）、加入二茂铁、氢氧化铝、桐油酸酐，升温至150-160℃，400-600转/分高速搅拌搅拌，反应1-2小时，
（3）、加入其它物料，升温至180-200℃，800-1000转/分高速搅拌，保温反应1-2小时，冷却；干燥、脱去有机溶剂二甲苯，得到改性环氧树脂。
5.根据权利要求1所述的含有改性凹凸棒土的粉末涂料，其特征在于：所述的改性凹凸棒土的制备方法为：将凹凸棒土用10-15%的氢氧化钠溶液浸泡2-3小时后；再用10-15%盐酸溶液浸泡2-3小时；然后去离子水洗涤多次，至凹凸棒土为中性，烘干；最后研磨为0.8-1.2μm粉末，得到改性凹凸棒土。
CN201210534245.3A 2012-12-12 2012-12-12 一种含有改性凹凸棒土的粉末涂料及其制备方法 Active CN103013296B (zh)