CN103012647B - 一种铅离子吸附树脂的制备方法 - Google Patents
一种铅离子吸附树脂的制备方法 Download PDFInfo
- Publication number
- CN103012647B CN103012647B CN201210489541.6A CN201210489541A CN103012647B CN 103012647 B CN103012647 B CN 103012647B CN 201210489541 A CN201210489541 A CN 201210489541A CN 103012647 B CN103012647 B CN 103012647B
- Authority
- CN
- China
- Prior art keywords
- warming
- preparation
- ion
- polymeric adsorbent
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种铅离子吸附树脂的制备方法,在传统生产工艺基础上,采用苯乙烯系合成树脂为骨架,进行络合吸附物,本发明处理Pb2+初始浓度为0.80mmol/L、pH=4.5的模拟污水,树脂用量为0.25g/L时,30℃静态吸附8h,树脂对Pb2+离子的吸附量达2.70-2.83mmol/g,残余液中Pb2+离子浓度为0.0015-0.0020mol/L,去除率达98以上%,效果较好。用0.15mol/L稀盐酸洗脱再生3次后,该颗粒树脂对Pb2+离子的吸附量下降较小,具备较好的反复使用性能。
Description
技术领域
本发明属于一种树脂的制备方法,具体是一种铅离子吸附树脂的制备方法。
背景技术
近年来,随着我国经济的快速发展,冶金、电池、颜料、橡胶等工厂废水大量排放,土壤和水源中Pb2+积累日益加剧,带来了严重的污染。目前,对溶液中金属离子铅等铅离子的吸附,大多数吸附树脂或多或少存在一些缺点:吸附容量小,或反复使用次数少,或选择性较差,或成本高。
发明内容
本发明的目的是提供一种铅离子吸附树脂的制备方法,本发明通过水相的改进,使得分散性、悬浮性提高,进而达到增加对铅离子的吸附容量的效果。
本发明的技术方案如下:
一种铅离子吸附树脂的制备方法,其特征在于包括以下步骤:
按下列重量份比例配好水相,升温至45℃;
去离子水350-380
聚乙烯醇15-20
羟乙基纤维素20-25
树木灰烬8-12
纳米凹凸棒土7-10
氯化钠60-65
过硫酸铵1-2
用硫酸调水相PH为中性
称取下列重量份的原料,混合后加入水相中,开机搅拌,视粒度情况调整转速;
苯乙烯65-70
二乙烯苯330-335
甲苯235-245
200#溶剂油30-35
TAIC30-40
二茂铁10-12
偶氮二异丁腈1-2
以5-6℃/10分钟的速度升温至79±1℃保温定型4-5h;
用20-40分钟升温至92-95℃保温5-6h;
用热水洗球数遍至水清澈为止;
烘干后用丙酮浸泡;
水洗至无丙酮味为止,抽干水包装。
本发明处理Pb2+初始浓度为0.80mmol/L、pH=4.5的模拟污水,树脂用量为0.25g/L时,30℃静态吸附8h,树脂对Pb2+离子的吸附量达2.70-2.83mmol/g,残余液中Pb2+离子浓度为0.0015-0.0020mol/L,去除率达98以上%,效果较好。用0.15mol/L稀盐酸洗脱再生3次后,该颗粒树脂对Pb2+离子的吸附量下降较小,具备较好的反复使用性能。
具体实施方式
一种铅离子吸附树脂的制备方法,其特征在于包括以下步骤:
按下列重量(公斤)比例配好水相,升温至45℃;
去离子水350
聚乙烯醇15
羟乙基纤维素20
树木灰烬8
纳米凹凸棒土7
氯化钠60
过硫酸铵1
用硫酸调水相PH为中性
称取下列重量(公斤)的原料,混合后加入水相中,开机搅拌,视粒度情况调整转速;
苯乙烯65
二乙烯苯330
甲苯235
200#溶剂油30
TAIC30
二茂铁10
偶氮二异丁腈1
以5-6℃/10分钟的速度升温至79±1℃保温定型4-5h;
用20-40分钟升温至92-95℃保温5-6h;
用热水洗球数遍至水清澈为止;
烘干后用丙酮浸泡;
水洗至无丙酮味为止,抽干水包装。
本发明处理Pb2+初始浓度为0.80mmol/L、pH=4.5的模拟污水,树脂用量为0.25g/L时,30℃静态吸附8h,树脂对Pb2+离子的吸附量达2.70-2.83mmol/g,残余液中Pb2+离子浓度为0.0015-0.0020mol/L,去除率达98以上%,效果较好。用0.15mol/L稀盐酸洗脱再生3次后,该颗粒树脂对Pb2+离子的吸附量下降较小,具备较好的反复使用性能。
Claims (1)
1.一种铅离子吸附树脂的制备方法,其特征在于包括以下步骤:按下列重量份比例配好水相,升温至45℃;去离子水350-380聚乙烯醇15-20羟乙基纤维素20-25树木灰烬8-12纳米凹凸棒土7-10氯化钠60-65过硫酸铵1-2用硫酸调水相pH为中性称取下列重量份的原料,混合后加入水相中,开机搅拌,视粒度情况调整转速;苯乙烯65-70二乙烯苯330-335甲苯235-245200#溶剂油30-35TAIC30-40二茂铁10-12偶氮二异丁腈1-2以5-6℃/10分钟的速度升温至79±1℃保温定型4-5h;用20-40分钟升温至92-95℃保温5-6h;用热水洗球数遍至水清澈为止;烘干后用丙酮浸泡;水洗至无丙酮味为止,抽干水包装。