CN103007900A - 一种硅藻土改性的吸附树脂的制备方法 - Google Patents

一种硅藻土改性的吸附树脂的制备方法 Download PDF

Info

Publication number
CN103007900A
CN103007900A CN2012104896673A CN201210489667A CN103007900A CN 103007900 A CN103007900 A CN 103007900A CN 2012104896673 A CN2012104896673 A CN 2012104896673A CN 201210489667 A CN201210489667 A CN 201210489667A CN 103007900 A CN103007900 A CN 103007900A
Authority
CN
China
Prior art keywords
water
resin
warming
preparation
ion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104896673A
Other languages
English (en)
Other versions
CN103007900B (zh
Inventor
姚能平
梅德华
陈建国
林伟
王海宽
王玉兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Wandong Chemical Co Ltd
Original Assignee
Anhui Wandong Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Wandong Chemical Co Ltd filed Critical Anhui Wandong Chemical Co Ltd
Priority to CN201210489667.3A priority Critical patent/CN103007900B/zh
Publication of CN103007900A publication Critical patent/CN103007900A/zh
Application granted granted Critical
Publication of CN103007900B publication Critical patent/CN103007900B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种硅藻土改性的吸附树脂的制备方法，在传统生产工艺基础上，采用苯乙烯系合成树脂为骨架，进行络合吸附物，本发明处理Pb2+初始浓度为0.750mmol/L、pH=4.8的模拟污水，树脂用量为0.20g/L时，26℃静态吸附10h，树脂对Pb2+离子的吸附量达2.60-2.8mmol/g，残余液中Pb2+离子浓度为0.0018-0.0025mol/L，去除率达98以上％，效果较好。用0.15mol/L稀盐酸洗脱再生3次后，该颗粒树脂对Pb2+离子的吸附量下降较小，具备较好的反复使用性能。

Description

一种硅藻土改性的吸附树脂的制备方法
技术领域
本发明属于一种树脂的制备方法，具体是一种硅藻土改性的吸附树脂的制备方法。
背景技术
近年来，随着我国经济的快速发展，冶金、电池、颜料、橡胶等工厂废水大量排放，土壤和水源中Pb2+积累日益加剧，带来了严重的污染。目前，对溶液中金属离子铅等铅离子的吸附，大多数吸附树脂或多或少存在一些缺点：吸附容量小，或反复使用次数少，或选择性较差，或成本高。
发明内容
本发明的目的是提供一种硅藻土改性的吸附树脂的制备方法，本发明通过水相的改进，使得分散性、悬浮性提高，进而达到增加对铅离子的吸附容量的效果。
本发明的技术方案如下：
一种硅藻土改性的吸附树脂的制备方法，其特征在于包括以下步骤：
一种硅藻土改性的吸附树脂的制备方法，其特征在于包括以下步骤：
Figure 607220DEST_PATH_IMAGE002
按下列重量份比例配好水相，升温至45℃；
去离子水   350-380
羟乙基纤维素  20-25
甘油         15-20
改性硅藻土       8-12
纳米凹凸棒土    7-10
氯化钠       60-65
过硫酸铵    1-2
三聚磷酸钠  3-5
用硫酸调水相PH为中性；
所述的改性硅藻土通过以下方法制得：
将硅藻土在450-480℃焙烧4-5小时，再用10-12%盐酸浸泡2-3小时，取出后用水洗至中性，烘干，加入相当于其重量3-5%的纳米碳、1-2%的丙烯腈、2-3%的氢氧化铝，混合均匀即可。
Figure 423866DEST_PATH_IMAGE004
称取下列重量份的原料，混合后加入水相中，开机搅拌，视粒度情况调整转速；
苯乙烯         65-70
二乙烯苯       330-335
丙烯腈          125-145
200# 溶剂油     50-55
二甲苯          10-15
二茂铁         10-12
偶氮二异丁腈    1-2
Figure 466603DEST_PATH_IMAGE006
以5-6℃/10分钟的速度升温至79±1℃保温定型4-5h；
Figure 52305DEST_PATH_IMAGE008
用20-40分钟升温至92-95℃保温5-6h；
Figure 295199DEST_PATH_IMAGE010
用热水洗球数遍至水清澈为止；
Figure 333562DEST_PATH_IMAGE012
烘干后用丙酮浸泡；
Figure 185849DEST_PATH_IMAGE014
水洗至无丙酮味为止，抽干水包装。
本发明处理Pb2+ 初始浓度为0.750mmol/L、pH=4.8 的模拟污水，树脂用量为0.20g/L 时，26℃静态吸附10h，树脂对Pb2+ 离子的吸附量达2.60-2.8mmol/g，残余液中Pb2+ 离子浓度为0.0018-0.0025mol/L，去除率达98以上％，效果较好。用0.15mol/L 稀盐酸洗脱再生3 次后，该颗粒树脂对Pb2+ 离子的吸附量下降较小，具备较好的反复使用性能。
具体实施方式
一种硅藻土改性的吸附树脂的制备方法，包括以下步骤：
Figure 891637DEST_PATH_IMAGE002
按下列重量（公斤）比例配好水相，升温至45℃；
去离子水   350
羟乙基纤维素  20
甘油         15
改性硅藻土      12
纳米凹凸棒土    7
氯化钠       60
过硫酸铵    1
三聚磷酸钠  3
用硫酸调水相PH为中性；
所述的改性硅藻土通过以下方法制得：
将硅藻土在450-480℃焙烧5小时，再用10-12%盐酸浸泡3小时，取出后用水洗至中性，烘干，加入相当于其重量5%的纳米碳、2%的丙烯腈、3%的氢氧化铝，混合均匀即可。
称取下列重量（公斤）的原料，混合后加入水相中，开机搅拌，视粒度情况调整转速；
苯乙烯         65
二乙烯苯       330
丙烯腈          125
200# 溶剂油     50
二甲苯          10
二茂铁         10
偶氮二异丁腈    2
Figure 831091DEST_PATH_IMAGE006
以5-6℃/10分钟的速度升温至79±1℃保温定型4-5h；
Figure 221490DEST_PATH_IMAGE008
用30-40分钟升温至92-95℃保温5-6h；
Figure 781784DEST_PATH_IMAGE010
用热水洗球数遍至水清澈为止；
Figure 100901DEST_PATH_IMAGE012
烘干后用丙酮浸泡；
水洗至无丙酮味为止，抽干水包装。
本发明吸附树脂处理Pb2+ 初始浓度为0.750mmol/L、pH=4.8 的模拟污水，树脂用量为0.20g/L 时，26℃静态吸附10h，树脂对Pb2+ 离子的吸附量达2.60-2.8mmol/g，残余液中Pb2+ 离子浓度为0.0018-0.0025mol/L，去除率达98以上％，效果较好。用0.15mol/L 稀盐酸洗脱再生3 次后，该颗粒树脂对Pb2+ 离子的吸附量下降较小，具备较好的反复使用性能。

Claims (1)

1.一种硅藻土改性的吸附树脂的制备方法，其特征在于包括以下步骤：
按下列重量份比例配好水相，升温至45℃；
去离子水   350-380
羟乙基纤维素  20-25
甘油         15-20
改性硅藻土       8-12
纳米凹凸棒土    7-10
氯化钠       60-65
过硫酸铵    1-2
三聚磷酸钠  3-5
用硫酸调水相PH为中性；
所述的改性硅藻土通过以下方法制得：
将硅藻土在450-480℃焙烧4-5小时，再用10-12%盐酸浸泡2-3小时，取出后用水洗至中性，烘干，加入相当于其重量3-5%的纳米碳、1-2%的丙烯腈、2-3%的氢氧化铝，混合均匀即可；
Figure 781412DEST_PATH_IMAGE002
称取下列重量份的原料，混合后加入水相中，开机搅拌，视粒度情况调整转速；
苯乙烯         65-70
二乙烯苯       330-335
丙烯腈          125-145
200# 溶剂油     50-55
二甲苯          10-15
二茂铁         10-12
偶氮二异丁腈    1-2
Figure 2012104896673100001DEST_PATH_IMAGE003
以5-6℃/10分钟的速度升温至79±1℃保温定型4-5h；
用20-40分钟升温至92-95℃保温5-6h；
Figure 2012104896673100001DEST_PATH_IMAGE005
用热水洗球数遍至水清澈为止；
Figure 699613DEST_PATH_IMAGE006
烘干后用丙酮浸泡；
Figure 2012104896673100001DEST_PATH_IMAGE007
水洗至无丙酮味为止，抽干水包装。
CN201210489667.3A 2012-11-27 2012-11-27 一种硅藻土改性的吸附树脂的制备方法 Active CN103007900B (zh)