CN102992727A - Reflection reinforced adiabatic inorganic coating - Google Patents
Reflection reinforced adiabatic inorganic coating Download PDFInfo
- Publication number
- CN102992727A CN102992727A CN 201110270936 CN201110270936A CN102992727A CN 102992727 A CN102992727 A CN 102992727A CN 201110270936 CN201110270936 CN 201110270936 CN 201110270936 A CN201110270936 A CN 201110270936A CN 102992727 A CN102992727 A CN 102992727A
- Authority
- CN
- China
- Prior art keywords
- adiabatic
- reflection
- inorganic
- reinforced
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a constructional reflection reinforced adiabatic inorganic coating. Ultrafine calcium silicate having an excellent adiabatic effect is adopted as an inorganic filler to reinforce the adiabatic effect, an inorganic coating has an inherent adiabatic effect, and a ceramic bead also has a certain adiabatic effect, so the adiabatic effect of a coat is substantially improved, and the good adiabatic effect is maintained when the coating having a deep color loses a reflection function in order to reach an effective energy saving purpose. An inorganic fireproof coat having the advantages of strong ultraviolet resistance, strong weather tolerance, no hollowing, no cracking, no condensation and respiratory function is formed through the effective combination of a coat formed by the reflection reinforced adiabatic inorganic coating with a wall base. The reflection reinforced adiabatic inorganic coating is characterized in that the reflection reinforced adiabatic inorganic coating comprises 5-15wt% of fine calcium silicate powder, 7-20wt% of the ceramic bead, 88-65wt% of other ultrafine inorganic filler blends, and water and a solvent, where in the total amount of the water and the solvent accounts for 35-45wt% of the above dry powders.
Description
Technical field
The present invention relates to a kind of not only can sunlight reflection and heat and the reinforced heat insulation inorganic paint of reflection for building that can be heat insulation.The reinforced heat insulation inorganic paint of this reflection for building uses as reflection and the thermal insulating coating of the outside surface of the surface of the exterior wall of industry or civil building, interior wall, mechanical means, container, pipeline.
Background technology
Current, its solvent of reflective heat-insulation paint for building that adopts both at home and abroad is take water-based or organism solvent as main for example emulsion paint, becomes belong to organic coating as reflection with heat insulation with ceramic fine bead etc. with space.The coating anti-ultraviolet property that reflective insulation organic coating for building forms is weak, not fire-retardant, work-ing life is relatively short, when also only being used in white or light color solar ray and heat is brought into play good reflection function.When dark colour loses reflecting effect, utilize air in the inorganic hollow microballon to postpone the absorbing heats such as heat conduction such as ceramic fine bead and reach heat and also can lose effect of heat insulation when saturated.Therefore the reflection inorganic paint for building that overcomes above-mentioned reflective insulation organic coating shortcoming for building will be development trend.
Summary of the invention
The reinforced heat insulation inorganic paint of reflection for building among the present invention, being not only the reflection inorganic paint for building that overcomes above-mentioned reflective insulation organic coating shortcoming for building also is to have adopted the good Calucium Silicate powder of ultra-fine disconnected thermal effect as mineral filler for strengthening effect of heat insulation, add the effect of heat insulation that inorganic paint itself is intrinsic, in addition the effect of heat insulation of ceramic fine bead this just greatly improved the effect of heat insulation of coating, when dark colour loses reflection function, also keep good disconnected hot effect of heat insulation to reach more effective energy-conservation purpose even deserve coating of the present invention.The coating that coating of the present invention forms, fine and smooth straight and even its reflection and heat-proof quality satisfy the requirement of the G B/T 25261-2010 that carried out on August 1st, 2011.Its added ingredients of the reinforced thermal insulating coating of reflection for building of the present invention all is inorganics, it is can be more effective strong and weathering resistance is strong in conjunction with forming uvioresistant to be applied to various bodies of wall and basic material, not hollowing, do not ftracture, not dewfall, the inorganic coating of respiratory Function is arranged.
The reinforced heat insulation inorganic paint of reflection provided by the invention is characterized in that, comprises the composition of following weight percent:
In product source mill, above-mentioned materials adds water and evenly mixes in stirrer, prefabricated product of the present invention.The key technical indexes sees table:
Embodiment
The constructional method of the reinforced heat insulation inorganic paint of reflection of the present invention, it is characterized in that, the prefabricated paste barreled product i.e. usefulness of uncapping at the construction field (site) in the construction process, for example can directly be applied to cleaning, without the newly-built body of wall of greasy dirt or the existing surface of wall of old wall renovation.
Surface treatment:
Remove surperficial dirt or grease;
Facing is processed:
Do not need putty layer can directly be applied to the surface, as far as possible the concavo-convex place of levelling.
The present invention compared with prior art, with ultra-fine inorganic cenosphere such as ceramic fine bead as the reflective insulation filler, other filler has also all adopted inorganic ultrafine particulate, be mixed with the reflective insulation inorganic paint, and the Calucium Silicate powder ultrafine powder of hot fire-proof function excellence is resolved in one of them employing of filler, so formulated coating is the reinforced heat insulation inorganic paint of reflection.Its characteristics: just formed in hydration reaction or moisture evaporative drying process when inorganic paint of the present invention is applied to matrix surface that bonding force is strong, the uvioresistant weathering resistance is strong, alkali-resistivity by force, not the hollowing cracking, not dewfall mouldy, with the coating of breathing performance and inorganic fire long service life.Coating is the trinity on heat-proof quality: the intrinsic effect of heat insulation to a certain degree of coating itself that inorganic paint forms; The inorganic hollow microballon such as the ceramic fine bead that add have good heat insulating function; Adopt simultaneously the Calucium Silicate powder of resolving the thermal effect excellence as filler, this has just improved the effect of heat insulation of coating greatly.Coating is the inorganic fire trinity on fire resistance: the inorganic fire of inorganic paint own, ceramic fine bead inorganic fire, Calucium Silicate powder also are inorganic fires.That effect of heat insulation or flameproof effect also all have the incomparable performance of existing reflective insulation organic coating.Product of the present invention not only possesses reflection function and more has both good heat insulation inorganic fire effect, and its refractory temperature is more than 1000 degree.
Claims (5)
1. reinforced heat insulation inorganic paint of reflection by the modulation of inorganic paint and hollow beads.It is characterized in that:
In another container, evenly mix with hollow beads after above-mentioned Calucium Silicate powder ultrafine powder, ultra-fine inorganic dry powder filler batch mixing and water evenly mix and be made into the paste product.
2. hollow (being also referred to as: hollow) microballon can be wherein a kind of or several compound of ceramic fine bead, fly ash micro-sphere, glass bead.
3. hollow beads can be with wherein a kind of or several compound of look or painted ceramic fine bead, fly ash micro-sphere, glass bead.
4. for strengthening the heat-proof quality to the reflective insulation of solar ray and heat, in reflective insulation inorganic paint of the present invention, add and resolve the good Calucium Silicate powder powder of thermal characteristics.What replace the Calucium Silicate powder powder can be the ultra-fine dry powder of the good light material of other disconnected thermal characteristicss such as vermiculite power, diatomite, utilizes a kind of or several combination wherein wherein.
5. reflect reinforced heat insulation inorganic paint, directly handle
Direct Uniform mixes together.For obtaining the reinforced heat insulation inorganic paint of reflection of the present invention, be not limited to making processes or the construction technology of above-mentioned demonstration.