CN102965504A - 一种除去硫酸锌溶液中有害氯离子的方法 - Google Patents
一种除去硫酸锌溶液中有害氯离子的方法 Download PDFInfo
- Publication number
- CN102965504A CN102965504A CN2012104265657A CN201210426565A CN102965504A CN 102965504 A CN102965504 A CN 102965504A CN 2012104265657 A CN2012104265657 A CN 2012104265657A CN 201210426565 A CN201210426565 A CN 201210426565A CN 102965504 A CN102965504 A CN 102965504A
- Authority
- CN
- China
- Prior art keywords
- solution
- zinc sulfate
- copper
- chlorion
- sulfate solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种除去硫酸锌溶液中有害氯离子的方法,包括以下步骤:(1)先向硫酸锌溶液中加硫酸10-15%调至溶液酸度在5-10g/L;(2)再加入适量铜粉与硫酸铜的混合物,搅拌5-6h,铜及铜离子与溶液中的氯离子相互作用,形成难溶的氯化亚铜沉淀得以分离,过程温度控制在45-60℃。本发明除氯效果好,处理后的硫酸锌液体中氯离子浓度在20mmg/L左右,完全符合工艺要求,操作简单,成本低,不会引入其它的有害杂质,综合实现了经济效益和环境效益。
Description
技术领域
本发明涉及一种除去硫酸锌溶液中有害氯离子的方法,属于化工技术领域。
背景技术
一般情况下,氯的主要来源是锌烟尘中的氯化物及自来水中的氯离子。在利用硫酸锌溶液制得特级透明氧化锌时,由于氯离子的存在会严重影响产品质量,所以在硫酸锌净化过程中必须将氯离子除去。常用的除氯方法不适用于本工艺,为此我公司开发出一种硫酸锌净化过程中氯离子的净化方法。
发明内容
本发明的目的是为了解决现有的问题,提供一种除去硫酸锌溶液中有害氯离子的方法。
本发明采用的技术方案如下:
一种除去硫酸锌溶液中有害氯离子的方法,其特征在于包括以下步骤:
(1)先向硫酸锌溶液中加10-15%硫酸调至溶液酸度在5-10g/L;
(2)再加入适合于氯离子反应当量的铜粉与硫酸铜的混合物及相当于硫酸锌溶液重量2-3%的硅藻土、1-2%的活性炭,搅拌5-6h,铜及铜离子与溶液中的氯离子相互作用,形成难溶的氯化亚铜沉淀得以分离,过程温度控制在45-60℃。
所述的铜粉与硫酸铜的混合物中铜粉与硫酸铜的摩尔比为1:1.5-2。
上述方法反应方程式如下:
Cu + Cu2+ + Cl------→CuCl↓
本发明的有益效果:
本发明除氯效果好,处理后的硫酸锌液体中氯离子浓度在20mmg/L左右,完全符合工艺要求,操作简单,成本低,不会引入其它的有害杂质,综合实现了经济效益和环境效益。
具体实施方式实施例
一种除去硫酸锌溶液中有害氯离子的方法,包括以下步骤:
(1)先向硫酸锌溶液中加10%硫酸调至溶液酸度在8g/L;
(2)再加入适合于氯离子反应当量的铜粉与硫酸铜的混合物及相当于硫酸锌溶液重量2%的硅藻土、1%的活性炭,搅拌5-6h,铜及铜离子与溶液中的氯离子相互作用,形成难溶的氯化亚铜沉淀得以分离,过程温度控制在45-60℃。
其中,所述的铜粉与硫酸铜的混合物中铜粉与硫酸铜的摩尔比为1:2。
经过本发明方法处理后的硫酸锌液体中氯离子浓度在20mmg/L左右,完全符合工艺要求。
Claims (2)
1.一种除去硫酸锌溶液中有害氯离子的方法,其特征在于包括以下步骤:
(1)先向硫酸锌溶液中加10-15%硫酸调至溶液酸度在5-10g/L;
(2)再加入适合于氯离子反应当量的铜粉与硫酸铜的混合物及相当于硫酸锌溶液重量2-3%的硅藻土、1-2%的活性炭,搅拌5-6h,铜及铜离子与溶液中的氯离子相互作用,形成难溶的氯化亚铜沉淀得以分离,过程温度控制在45-60℃。
2.根据权利要求1所述的除去硫酸锌溶液中有害氯离子的方法,其特征在于,所述的铜粉与硫酸铜的混合物中铜粉与硫酸铜的摩尔比为1:1.5-2。