CN102952250A - 一种耐低温聚氨酯 - Google Patents

一种耐低温聚氨酯 Download PDF

Info

Publication number
CN102952250A
CN102952250A CN2011102469176A CN201110246917A CN102952250A CN 102952250 A CN102952250 A CN 102952250A CN 2011102469176 A CN2011102469176 A CN 2011102469176A CN 201110246917 A CN201110246917 A CN 201110246917A CN 102952250 A CN102952250 A CN 102952250A
Authority
CN
China
Prior art keywords
low temperature
temperature resistant
urethane
massfraction
resistant polyurethane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102469176A
Other languages
English (en)
Inventor
彭德
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YOUTAIKE (SUZHOU) SEALING TECHNOLOGY Co Ltd
Original Assignee
YOUTAIKE (SUZHOU) SEALING TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YOUTAIKE (SUZHOU) SEALING TECHNOLOGY Co Ltd filed Critical YOUTAIKE (SUZHOU) SEALING TECHNOLOGY Co Ltd
Priority to CN2011102469176A priority Critical patent/CN102952250A/zh
Publication of CN102952250A publication Critical patent/CN102952250A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种耐低温聚氨酯，由二苯基甲烷二异氰酸酯、乙二醇己二酸酯混聚酯二醇、1，4-丁二醇、三乙烯二胺制得，本发明产品可应用于-55℃的低温环境中的密封行业中，可广泛应用于冷冻设备、森林机械、工程机械及自卸式卡车行业中。

Description

一种耐低温聚氨酯
技术领域
本发明涉及聚氨酯领域，特别是涉及一种耐低温聚氨酯。
背景技术
聚氨酯是由多异氰酸酯和聚醚多元醇或聚酯多元醇或/及小分子多元醇、多元胺或水等扩链剂或交联剂等原料制成的聚合物。通过改变原料种类及组成，可以大幅℃地改变产品形态及其性能，得到从柔软到坚硬的最终产品。聚氨酯制品形态有软质、半硬质及硬质泡沫塑料、弹性体、油漆涂料、胶粘剂、密封胶、合成革涂层树脂、弹性纤维等，广泛应用于汽车制造、冰箱制造、交通运输、土木建筑、鞋类、合成革、织物、机电、石油化工、矿山机械、航空、医疗、农业等许多领域。
普通的聚氨酯材料耐低温只能达到-35℃，所以在一些超低温工况环境下的密封造成的困难。
发明内容
本发明的目的是开发一种能够耐-55℃的一种耐低温聚氨酯。
为实现上述目的，本发明采用如下技术方案：
一种耐低温聚氨酯，按质量分数计由以下组分组成，
Figure BSA00000562760300011
所述的一种耐低温聚氨酯内添加有染料。
按质量分数计，所述的乙二醇己二酸酯混聚酯二醇用量优选为20.5。
按质量分数计，所述的1，4-丁二醇用量优选为10.5。
本发明中，采用二苯基甲烷二异氰酸酯作为该耐高温水聚氨酯的基料，其配比可改变聚氨酯材料的硬度，采用乙二醇己二酸酯混聚酯二醇作为耐高温水聚氨酯的辅料，其配比可改变聚氨酯材料的韧性、柔软性，采用1，4-丁二醇作为耐高温水聚氨酯的的辅料，其配比可改变聚氨酯材料的韧性、柔软性。
由于异氰酸酯的种类繁多，依据产品的用途不同选用不同的异氰酸酯，如甲苯二异氰酸酯(TDI)，分为2，4和2，6两种异构体，混合比例为80/20(TDI-80)和65/35(TDI-65)两种，可用于软质到硬质泡沫制品；多亚甲基对苯基多异氰酸酯(PAPI)，它含有三官能℃，可用于热固型的硬质泡沫、混炼及浇铸PU制品。本发明中选用二苯基甲烷二异氰酸酯作为基料，因其自身性质适用于半硬和硬质聚氨酯弹性体制品，除此之外，二苯基甲烷二异氰酸酯也是一种物理性能优越的聚氨酯弹性体材料，因此，本发明产品可应用于-55℃的低温环境中的密封行业中，可广泛应用于冷冻设备、森林机械、工程机械及自卸式卡车行业中。
具体实施内容
下面通过具体实施例，对本发明做详细的描述。
实施例1
一种耐低温聚氨酯，按质量分数计由以下组分组成：
Figure BSA00000562760300021
Figure BSA00000562760300031
实施例2
一种耐低温聚氨酯，按质量分数计由以下组分组成：
Figure BSA00000562760300032
实施例3
一种耐低温聚氨酯，按质量分数计由以下组分组成：
Figure BSA00000562760300033

Claims (4)

1.一种耐低温聚氨酯，其特征在于：按质量分数计由以下组分组成，
Figure FSA00000562760200011
2.根据权利要求书1所述的一种耐低温聚氨酯，其特征在于：所述的一种耐低温聚氨酯内添加有染料。
3.根据权利要求书1所述的一种耐低温聚氨酯，其特征在于：按质量分数计，所述的乙二醇己二酸酯混聚酯二醇用量优选为20.5。
4.根据权利要求书1所述的一种耐低温聚氨酯，其特征在于：按质量分数计，所述的1，4-丁二醇用量优选为10.5。
CN2011102469176A 2011-08-26 2011-08-26 一种耐低温聚氨酯 Pending CN102952250A (zh)