CN102922650A - 一种硅胶和塑胶贴合生产工艺 - Google Patents

一种硅胶和塑胶贴合生产工艺 Download PDF

Info

Publication number
CN102922650A
CN102922650A CN2012103979734A CN201210397973A CN102922650A CN 102922650 A CN102922650 A CN 102922650A CN 2012103979734 A CN2012103979734 A CN 2012103979734A CN 201210397973 A CN201210397973 A CN 201210397973A CN 102922650 A CN102922650 A CN 102922650A
Authority
CN
China
Prior art keywords
silica gel
production process
platinum catalyst
pet
production technology
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103979734A
Other languages
English (en)
Inventor
周建峯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DONGGUAN RISHENG RUBBER AND PLASTIC FACTORY Co Ltd
Original Assignee
DONGGUAN RISHENG RUBBER AND PLASTIC FACTORY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DONGGUAN RISHENG RUBBER AND PLASTIC FACTORY Co Ltd filed Critical DONGGUAN RISHENG RUBBER AND PLASTIC FACTORY Co Ltd
Priority to CN2012103979734A priority Critical patent/CN102922650A/zh
Publication of CN102922650A publication Critical patent/CN102922650A/zh
Pending legal-status Critical Current

Abstract

本发明涉及印刷工艺技术领域，特指一种硅胶和塑胶贴合生产工艺，生产方法如下：（1）、选择好厚度在0.05mm至0.3mm的胶片，在胶片上实施热转工艺；（2）、将板材上色、定位好后，根据需要尺寸规则，进行裁切；（3）、进行热压成型；（4）、将硅胶放入铂金催化剂再硅胶成型模具中成型，硅胶成型时加热，温度在50－180℃之间，其贴合生产工艺先进，色彩多样，同时颜色不会脱落。

Description

一种硅胶和塑胶贴合生产工艺
技术领域：
本发明涉及压贴合工艺技术领域，特指一种硅胶和塑胶贴合生产工艺。
背景技术：
硅胶是一种高活性吸附材料，属非晶态物质，不溶于水和任何溶剂，无毒无味，化学性质稳定，除强碱、氢氟酸外不与任何物质发生反应。各种型号的硅胶因其制造方法不同而形成不同的微孔结构。硅胶的化学组份和物理结构，决定了它具有许多其他同类材料难以取代得特点:吸附性能高、热稳定性好、化学性质稳定、有较高的机械强度等。
利用硅胶具有强力吸附能迅速有效地吸附密封包装内的水分、化学性质稳定、无毒无害的特点，在我们日常生活和生产经营活动中，硅胶被经常用于以下几方面:精密光学仪器、电子电器的干燥防霉包装；皮具干燥方面，如放置于皮衣、皮袋、皮鞋内起到干燥保质的作用；食品干燥方面，多见于放在饼干及油炸类食品中，以保证食品松脆；药品干燥方面，放于药瓶内，确保药品延长保存期；宾馆用物品类，如放置在衣柜中，鞋中和床下，吸附各种异味，保持空气干爽清新。
目前，在硅胶生产中，无法在硅胶上实现硅胶色彩多样化，硅胶产品色彩单一，没有鲜艳的色彩效果，同时，颜色会脱落。
发明内容：
本发明的目的是针对现有技术的不足，而提供一种硅胶和塑胶贴合生产工艺，其贴合生产工艺先进，色彩多样，同时颜色不会脱落。
为实现上述目的，本发明采用如下技术方案，生产方法如下：
（1）、选择好厚度在0.05mm至0.3mm的胶片，在胶片上实施热转工艺；
（2）、将板材上色、定位好后，根据需要尺寸规则，进行裁切。
（3）、进行热压成型；
（4）、将硅胶放入铂金催化剂再硅胶成型模具中成型，硅胶成型时加热，温度在50－180℃之间。
所述的胶片为pet、pc、pvc材料中的任意一种。
所述的pet、pc、pvc材料分别为聚对苯二甲酸乙二酯、聚碳酸酯、聚氯乙烯。
所述的铂金催化剂加入硅胶后，铂金催化剂的百分比例为：3-20%。
本发明有益效果为：
（1）、选择好厚度在0.05mm至0.3mm的胶片，在胶片上实施热转工艺；
（2）、将板材上色、定位好后，根据需要尺寸规则，进行裁切。
（3）、进行热压成型；
（4）、将硅胶放入铂金催化剂再硅胶成型模具中成型，硅胶成型时加热，温度在50－180℃之间，其贴合生产工艺先进，色彩多样，同时颜色不会脱落。
具体实施方式：
本发明生产方法如下：生产方法如下：（1）、选择好厚度在0.05mm至0.3mm的胶片，在胶片上实施热转工艺；
（2）、将板材上色、定位好后，根据需要尺寸规则，进行裁切。
（3）、进行热压成型；
（4）、将硅胶放入铂金催化剂再硅胶成型模具中成型，硅胶成型时加热，温度在50－180℃之间，温度在此步骤中克为重要，湿度不可过高或过低。
所述的胶片为pet、pc、pvc材料中的任意一种。
所述的pet、pc、pvc材料分别为聚对苯二甲酸乙二酯、聚碳酸酯、聚氯乙烯，主要取材为上述材料，因为上述三种材料本发明实验得出，其与硅胶粘合效果最佳。
所述的铂金催化剂加入硅胶后，铂金催化剂的百分比例为：3-20%。
为了更好地说明本发明的技术方案，特将本发明工艺说明如下：铂金催化剂又名铂金架桥剂(络合物)可以作为液体硅橡胶、高温硅橡胶、硅胶油墨、丝印等反应的催化剂，具有稳定，反应活性高的优点，无色透明液体。
高性能铂金催化剂催化效率高，可以抑制Si-Vi和Si-H反应过程中伴随发生的副反应，避免了黑色物质的生成，克服了其它催化剂使用中产品出现发黄或变黑现象。因此可以制备高透明制品，本发明中主要挂起到板材上色与硅胶完美的结合（胶粘催化），高透明、无杂质产生。
以上所述仅是本发明的较佳实施例，故凡依本发明专利申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。

Claims (4)

1.一种硅胶和塑胶贴合生产工艺，其特征在于：生产方法如下：（1）、选择好厚度在0.05mm至0.3mm的胶片，在胶片上实施热转工艺；
（2）、将板材上色、定位好后，根据需要尺寸规则，进行裁切。
（3）、进行热压成型；
（4）、将硅胶放入铂金催化剂再硅胶成型模具中成型，硅胶成型时加热，温度在50－180℃之间。
2.根据权利要求1所述的一种硅胶和塑胶贴合生产工艺，其特征在于：所述的胶片为pet、pc、pvc材料中的任意一种。
3.根据权利要求2所述的一种硅胶和塑胶贴合生产工艺，其特征在于：所述的pet、pc、pvc材料分别为聚对苯二甲酸乙二酯、聚碳酸酯、聚氯乙烯。
4.根据权利要求1所述的一种硅胶和塑胶pet[pc或pvc]贴合生产工艺，其特征在于：所述的铂金催化剂加入硅胶后，铂金催化剂的百分比例为：3-20%。
CN2012103979734A 2012-10-18 2012-10-18 一种硅胶和塑胶贴合生产工艺 Pending CN102922650A (zh)