CN102911428B - 一种煤矿用交联聚乙烯绝缘电力电缆料及其制备方法 - Google Patents
一种煤矿用交联聚乙烯绝缘电力电缆料及其制备方法 Download PDFInfo
- Publication number
- CN102911428B CN102911428B CN201210346142.4A CN201210346142A CN102911428B CN 102911428 B CN102911428 B CN 102911428B CN 201210346142 A CN201210346142 A CN 201210346142A CN 102911428 B CN102911428 B CN 102911428B
- Authority
- CN
- China
- Prior art keywords
- parts
- compound
- ethylene
- power cable
- insulated power
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种煤矿用交联聚乙烯绝缘电力电缆料及其制备方法，其组成原料的重量份为：混合料A：甲基乙烯基硅橡胶30-40、聚乙烯树脂20-30、柠檬酸三丁酯25-35、聚磷酸铵3-8、白炭黑1-3、改性椴木灰40-60、秸秆灰烬10-15、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1.5-2.5、乙撑基双硬酯酰胺0.5-1.0、过硫化钠1-3和聚酰亚胺 3-4；混合料B：乙烯-醋酸乙烯共聚物50-70、三元乙丙橡胶20-30、三聚氰胺2-5、聚-4-甲基-1-戊烯0.3-0.5、焙烧沸石粉3-5、过氧化二烷烃1-3、聚乙烯蜡2-4、二邻甲苯胍1-3、甲基乙烯硅油2-4、六偏磷酸钠1-3、硅烷偶联剂KH550 2-4和硼酸锌10-15。本发明的改性后的三元乙丙橡胶与传统的三元乙丙橡胶相比较，本发明改性的三元乙丙橡胶具有很高的氧指数，同时具有很高的机械强度，优良的断裂伸长率、很好的体积电阻率。
Description
技术领域
本发明涉及橡胶材料加工领域，具体涉及一种煤矿用交联聚乙烯绝缘电力电缆料及其制备方法。
背景技术
三元乙丙橡胶因其优良的电气性能、机械物理性能及优异的加工性能，在电缆行业广泛地应用，由于三元乙丙橡胶自身的氧指数较低，限制了其在矿用电缆领域的推广和应用，因此提高三元乙丙橡胶的阻燃氧指数，对于三元乙丙橡胶在矿用电缆领域的运用有着现实的意义；用改性椴木灰改性，由于其优异的表面亲和力，对三元乙丙橡胶的物理机械性能不会产生破坏。
发明内容
本发明的目的在于解决现有技术中的缺陷，提供一种煤矿用交联聚乙烯绝缘电力电缆料及其制备方法，本发明三元乙丙橡胶具有很高的氧指数，同时具有很高的机械强度，优良的断裂伸长率、很好的体积电阻率。
为实现上述目的本发明的采用如下技术方案：
煤矿用交联聚乙烯绝缘电力电缆料，其组成原料的重量份为：
混合料A：甲基乙烯基硅橡胶 30-40、聚乙烯树脂20-30、柠檬酸三丁酯25-35、聚磷酸铵3-8、白炭黑1-3、改性椴木灰40-60、秸秆灰烬10-15、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯 1.5-2.5、乙撑基双硬酯酰胺0.5-1.0、过硫化钠1-3和聚酰亚胺 3-4；
混合料B：乙烯-醋酸乙烯共聚物50-70、三元乙丙橡胶20-30、三聚氰胺2-5、聚-4-甲基-1-戊烯0.3-0.5、焙烧沸石粉3-5、过氧化二烷烃 1-3、聚乙烯蜡2-4、二邻甲苯胍1-3、甲基乙烯硅油2-4、六偏磷酸钠1-3、硅烷偶联剂KH550 2-4和硼酸锌10-15。
煤矿用交联聚乙烯绝缘电力电缆料，其组成原料的重量份为：
混合料A：甲基乙烯基硅橡胶35、聚乙烯树脂25、柠檬酸三丁酯30、聚磷酸铵5、白炭黑2、改性椴木灰50、秸秆灰烬12、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯2、乙撑基双硬酯酰胺0.8、过硫化钠2和聚酰亚胺3.5；
混合料B：乙烯-醋酸乙烯共聚物60、三元乙丙橡胶25、三聚氰胺4、聚-4-甲基-1-戊烯0.4、焙烧沸石粉4、过氧化二烷烃2、聚乙烯蜡3、二邻甲苯胍2、甲基乙烯硅油3、六偏磷酸钠2、硅烷偶联剂KH550 3和硼酸锌12。
煤矿用交联聚乙烯绝缘电力电缆料的制备方法，包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料分别在温度105-115℃在密炼4-6分钟后，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。
所述的改性椴木灰制备方法为先用15-20%盐酸浸泡椴木灰1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干。
本发明的优点：
本发明的改性后的三元乙丙橡胶与传统的三元乙丙橡胶相比较，本发明改性的三元乙丙橡胶具有很高的氧指数，同时具有很高的机械强度，优良的断裂伸长率、很好的体积电阻率。
具体实施方式
实施例1：煤矿用交联聚乙烯绝缘电力电缆料，其组成原料的重量份为：
混合料A：甲基乙烯基硅橡胶35、聚乙烯树脂25、柠檬酸三丁酯30、聚磷酸铵5、白炭黑2、改性椴木灰50、秸秆灰烬12、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯2、乙撑基双硬酯酰胺0.8、过硫化钠2和聚酰亚胺3.5；
混合料B：乙烯-醋酸乙烯共聚物60、三元乙丙橡胶25、三聚氰胺4、聚-4-甲基-1-戊烯0.4、焙烧沸石粉4、过氧化二烷烃2、聚乙烯蜡3、二邻甲苯胍2、甲基乙烯硅油3、六偏磷酸钠2、硅烷偶联剂KH550 3和硼酸锌12。
煤矿用交联聚乙烯绝缘电力电缆料的制备方法，包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料分别在温度105-115℃在密炼4-6分钟后，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。
所述的改性椴木灰制备方法为先用15-20%盐酸浸泡椴木灰1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干。
下表为本实施例中改性后的三元乙丙橡胶与传统的三元乙丙橡胶机械物理性能的试验对比：
由上表可见，本发明中较传统的三元乙丙橡胶有大幅的提高，同时阻燃氧指数有很大的提高。
Claims (3)
1.一种煤矿用交联聚乙烯绝缘电力电缆料，其特征在于其组成原料的重量份为：
混合料A：甲基乙烯基硅橡胶30-40、聚乙烯树脂20-30、柠檬酸三丁酯25-35、聚磷酸铵3-8、白炭黑1-3、改性椴木灰40-60、秸秆灰烬10-15、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1.5-2.5、乙撑基双硬酯酰胺0.5-1.0、过硫化钠1-3和聚酰亚胺3-4；
混合料B：乙烯-醋酸乙烯共聚物50-70、三元乙丙橡胶20-30、三聚氰胺2-5、聚-4-甲基-1-戊烯0.3-0.5、焙烧沸石粉3-5、过氧化二烷烃 1-3、聚乙烯蜡2-4、二邻甲苯胍1-3、甲基乙烯硅油2-4、六偏磷酸钠1-3、硅烷偶联剂KH550 2-4和硼酸锌10-15；
所述的改性椴木灰制备方法为先用15-20%盐酸浸泡椴木灰1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干。
2.根据权利要求1所述的煤矿用交联聚乙烯绝缘电力电缆料，其特征在于其组成原料的重量份为：
混合料A：甲基乙烯基硅橡胶35、聚乙烯树脂25、柠檬酸三丁酯30、聚磷酸铵5、白炭黑2、改性椴木灰50、秸秆灰烬12、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯2、乙撑基双硬酯酰胺0.8、过硫化钠2和聚酰亚胺3.5；
混合料B：乙烯-醋酸乙烯共聚物60、三元乙丙橡胶25、三聚氰胺4、聚-4-甲基-1-戊烯0.4、焙烧沸石粉4、过氧化二烷烃2、聚乙烯蜡3、二邻甲苯胍2、甲基乙烯硅油3、六偏磷酸钠2、硅烷偶联剂KH550 3和硼酸锌12。
3.一种如权利要求1或2所述的煤矿用交联聚乙烯绝缘电力电缆料的制备方法，其特征在于包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料在温度105-115℃密炼4-6分钟，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。