CN102898062A - 一种卵石型透水混凝土专用的复合型添加剂 - Google Patents

一种卵石型透水混凝土专用的复合型添加剂 Download PDF

Info

Publication number
CN102898062A
CN102898062A CN201210410096XA CN201210410096A CN102898062A CN 102898062 A CN102898062 A CN 102898062A CN 201210410096X A CN201210410096X A CN 201210410096XA CN 201210410096 A CN201210410096 A CN 201210410096A CN 102898062 A CN102898062 A CN 102898062A
Authority
CN
China
Prior art keywords
pebble
pervious concrete
concrete
parts
type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201210410096XA
Other languages
English (en)
Other versions
CN102898062B (zh
Inventor
高育欣
徐芬莲
赵晚群
李预奇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China West Construction Guangxi Co Ltd
Original Assignee
China Construction Ready Mixed Concrete Chengdu Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Construction Ready Mixed Concrete Chengdu Co Ltd filed Critical China Construction Ready Mixed Concrete Chengdu Co Ltd
Priority to CN201210410096.XA priority Critical patent/CN102898062B/zh
Publication of CN102898062A publication Critical patent/CN102898062A/zh
Application granted granted Critical
Publication of CN102898062B publication Critical patent/CN102898062B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各材料的质量份数为：超细微珠80-90份，硅灰10-15份，锂渣粉20-30份，聚氧化乙烯0.0005-0.001份。将以上各原材料按配方计量之后，加入到混料机中混合均匀，即可得到本发明产品。使用本发明后，可明显地提高水泥浆体的粘性与保水性，增加水泥浆体对卵石表面的包裹性以及与卵石表面粘结性能，使卵石型透水混凝土拌合物具有良好的粘聚性、保水性与匀质性，解决了卵石型透水混凝土粗骨料表面裹浆差的问题，保证该混凝土的透水性与力学性能，确保工程施工质量，具有良好的综合效益。

Description

一种卵石型透水混凝土专用的复合型添加剂
技术领域
本发明涉及建筑材料领域，确切地说是指一种卵石型透水混凝土专用的复合型添加剂。
背景技术
混凝土是由胶凝材料（包括水泥、矿物掺合料等），粗细骨料（如砂、石），水，以及必要时加入的外加剂按一定比例配制而得到的一种建筑材料；透水混凝土不含细骨料，是由粗骨料表面包覆一薄层胶凝材料浆体相互粘结而形成孔穴均匀分布的蜂窝状结构的多孔混凝土，故具有透气、透水的特点。
混凝土中的粗骨料是指粒径＞4.75mm的岩石颗粒，分为碎石与卵石两大类。卵石型透水混凝土是指用卵石作为粗骨料的透水混凝土，由于卵石表面光滑，拌制的透水混凝土往往包裹性较差，经振动后，浆体极易下沉，导致堵塞下部孔隙，影响透水性，而上部的浆体较少，也影响粗骨料之间的粘结性，导致透水混凝土的强度不合格。
为增加卵石型透水混凝土拌合物的粘聚性，目前常用的方法是掺入硅灰（用量为胶凝材料总量的3-5%，约为9-25kg/m3）、乳胶粉（用量为胶凝材料总量的3-4%，约为9-20kg/m3）、纤维素醚（用量为胶凝材料总量的0.8-1‰，约为0.3-1kg/m3，取决于纤维素醚的粘度以及各种原材料的性能）等增稠材料，但是此类材料造价都较高，在透水混凝土中的用量也较少，计量精度要求较高，0.1-5kg的误差就会对混凝土的性能会产生极大的不利影响，不便于现场搅拌施工的混凝土质量控制。同时，此类材料虽然能够增加水泥浆体的粘度，却不能很好地增加水泥浆体与卵石表面的粘结性，卵石表面裹浆仍不均匀，透水混凝土的匀质性不好，仍然影响其透水性。
因此，为了解决卵石型透水混凝土粗骨料表面光滑不易裹浆的问题，提高其综合性能，保证工程质量，需要研制出一种便于使用、性能良好的卵石型透水混凝土专用的添加剂。
发明内容
有鉴于此，本发明解决的技术问题在于提供一种卵石型透水混凝土专用的复合型添加剂，不仅可以增加水泥浆体的粘性与保水性，也可以增加水泥浆体对卵石表面的包裹性及与卵石表面的粘结性能，从而使卵石型透水混凝土拌合物具有良好的粘聚性、保水性与匀质性，保证该混凝土的综合性能，确保工程施工质量，具有良好的技术效益与社会效益。
为了解决以上的技术问题，本发明提供的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：
超细微珠         80-90份，
硅灰             10-15份，
锂渣粉           20-30份，
聚氧化乙烯       0.0005-0.001份。
优选的，所述的超细微珠为粉煤灰超细微珠，是从粉煤灰中分选出来的空心玻璃微珠，呈浅灰色粉末状，密度约为2.49g/cm3，比表面积1200m2/kg。
优选的，所述的硅灰为灰色粉末状，加密型，SiO2含量≥90％，比表面积≥15000m2/kg。
优选的，所述的锂渣粉为浅黄色粉末状，密度约为2.36g/cm3，比表面积≥400m2/kg。
优选的，所述的聚氧化乙烯呈白色粉末状，溶于水，分子量在400-600万之间。
进一步的，所述的超细微珠既是载体，也可以起到保水、增稠、增强的作用。
进一步的，所述的锂渣粉、硅灰和聚氧化乙烯起保水增稠作用，其中硅灰还可以起到提高卵石型透水混凝土早期强度的作用。
本发明提供的一种卵石型透水混凝土专用的复合型添加剂，其制备方法如下：按上述的质量配比称取各原材料，加入混料机中，充分混合均匀，即可得到本发明产品。
本发明在卵石型透水混凝土中的适宜用量为50-100kg/m3，根据使用的各种原材料性能，通过试验对比确定本发明合适的用量，±5kg的误差对于混凝土性能无明显的影响。
与现有技术相比，本发明取得的有益效果为：
（1）使用本发明后，可明显地提高水泥浆体的粘性与保水性，增加水泥浆体对卵石表面的包裹性与粘结性，使卵石型透水混凝土拌合物具有良好的粘聚性、保水性与匀质性，解决了卵石型透水混凝土粗骨料表面裹浆差的问题，保证该混凝土的透水性与力学性能，确保工程施工质量，具有良好的技术效益与社会效益；
（2）本发明在卵石型透水混凝土中的适宜用量达到50-100kg/m3，允许误差为±5kg，根据实际需求，直接加入混凝土混合料中即可使用，操作方便，适用于现场施工操作，也便于混凝土质量控制；
（3）利用了工业废渣——锂渣粉，将锂渣粉变废为宝，符合国家废弃资源综合利用与可持续发展的政策。
附图说明
图1为仅添加纤维素醚的卵石型透水混凝土拌合物示意图；
图2为添加本发明产品的卵石型透水混凝土拌合物示意图。
具体实施方式
本发明提供的一种卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，将以上各原材料按配方计量之后，加入到混料机中混合均匀，即可得到本发明产品。
表1为本发明配方；表2为本发明具体实施配方；表3为本发明实施例应用到C20卵石型透水混凝土中的配合比；表4为基准混凝土性能及使用本发明1-4实施例配方的C20卵石型透水混凝土各项性能；表5为行业标准CJJ/T 135-2009《透水水泥混凝土路面技术规程》对C20透水混凝土的技术要求。
为了更好地理解本发明，下面结合实施例进一步阐明本发明的内容，但本发明的内容不仅仅局限于以下的实施例。
表1卵石型透水混凝土专用复合型添加剂配方
Figure BDA00002300965100041
表2卵石型透水混凝土专用复合型添加剂具体实施例配方
Figure BDA00002300965100042
所述的超细微珠为粉煤灰超细微珠，是从粉煤灰中分选出来的空心玻璃微珠，呈浅灰色粉末状，密度2.50g/cm3，比表面积1250m2/kg。
所述的硅灰为灰色粉末状，加密型，SiO2含量93%，比表面积20000m2/kg。
所述的锂渣粉为浅黄色粉末状，密度2.37g/cm3，比表面积410m2/kg。
所述的聚氧化乙烯为白色粉末状，溶于水，分子量500万。
为更好地说明本发明的实施效果，将添加纤维素醚(粘度75000mpa·s)X0C20卵石型透水混凝土作为对比的基准混凝土，如表3。
表3基准混凝土及使用本发明的C20卵石型透水混凝土配合比/(kg/m3)
Figure BDA00002300965100051
基准混凝土性能及使用本发明1-4实施例配方的C20卵石型透水混凝土各项性能如表4。
表4基准混凝土性能及使用本发明1-4实施例配方的C20卵石型透水混凝土各项性能
Figure BDA00002300965100052
表5行业标准CJJ/T 135-2009对C20透水混凝土的技术要求
Figure BDA00002300965100053
Figure BDA00002300965100061
由表4可知，X0混凝土拌合物包裹性较差，粗骨料（卵石）裸露较为严重，混凝土匀质性较差，添加本发明产品的X1-X4混凝土拌合物包裹性好，粗骨料（卵石）完全不裸露，混凝土匀质性好。
由表4可见，基准卵石型透水混凝土的孔隙率为9％，透水系数为1.2mm/s，28d抗折强度为2.6MPa，28d抗压强度为20.7MPa，使用本发明1-4实施例配方的C20卵石型透水混凝土X1-X4的孔隙率为14-16％，透水系数为2.1-2.3mm/s，28d抗折强度为3.8-4.3MPa，28d抗压强度为28.4-31.2MPa，表明本发明提供的卵石型透水混凝土专用复合型添加剂，可以显著地改善卵石型透水混凝土拌合物的粘聚性、保水性、匀质性，振动成型后浆体不下沉，保证了卵石型透水混凝土内部结构裹浆的均匀性，解决了其拌合物表面裹浆差的问题，保证了该类型混凝土的孔隙率、透水性及力学性能。
对比表5可知，该混凝土的各项技术性能指标完全满足并且优于行业标准CJJ/T135-2009《透水水泥混凝土路面技术规程》对C20透水混凝土的技术要求。
实施例5：
所述的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠80份，硅灰11份，锂渣粉20份，聚氧化乙烯0.001份。
实施例6：
所述的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠85份，硅灰13份，锂渣粉18份，聚氧化乙烯0.001份。
实施例7：
所述的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠86份，硅灰15份，锂渣粉25份，聚氧化乙烯0.0009份。
实施例8：
所述的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠88份，硅灰13份，锂渣粉24份，聚氧化乙烯0.0005份。
实施例9：
所述的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠90份，硅灰15份，锂渣粉20份，聚氧化乙烯0.0006份。
实施例10：
所述的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠89份，硅灰14份，锂渣粉28份，聚氧化乙烯0.0008份。
实施例11：
所述的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠90份，硅灰10份，锂渣粉27份，聚氧化乙烯0.0007份。
实施例12：
所述的卵石型透水混凝土专用的复合型添加剂，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠90份，硅灰15份，锂渣粉30份，聚氧化乙烯0.001份。
实施例5-12的应用效果，不再一一列举。
与现有技术相比，本发明取得的有益效果为：
（1）使用本发明后，可明显地提高水泥浆体的粘性与保水性，增加水泥浆体对卵石表面的包裹性与粘结性，使卵石型透水混凝土拌合物具有良好的粘聚性、保水性与匀质性，解决了卵石型透水混凝土粗骨料表面裹浆差的问题，保证该混凝土的透水性与力学性能，确保工程施工质量，具有良好的技术效益与社会效益；
（2）本发明在卵石型透水混凝土中的适宜用量达到50-100kg/m3，允许误差为±5kg，根据实际需求，直接加入混凝土混合料中即可使用，操作方便，适用于现场施工操作，也便于混凝土质量控制；
（3）利用了工业废渣——锂渣，将锂渣变废为宝，符合国家废弃资源综合利用与可持续发展的政策。
对所公开的实施例的上述说明，使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。

Claims (5)

1.一种卵石型透水混凝土专用的复合型添加剂，其特征在于，包括超细微珠、硅灰、锂渣粉、聚氧化乙烯，各原料的质量份数为：超细微珠80-90份，硅灰10-15份，锂渣粉20-30份，聚氧化乙烯0.0005-0.001份。
2.根据权利要求1所述的一种卵石型透水混凝土专用的复合型添加剂，其特征在于，所述的超细微珠为粉煤灰超细微珠，比表面积≥1200m2/kg。
3.根据权利要求1所述的一种卵石型透水混凝土专用的复合型添加剂，其特征在于，所述的硅灰中SiO2含量≥90%，比表面积≥15000m2/kg。
4.根据权利要求1所述的一种卵石型透水混凝土专用的复合型添加剂，其特征在于，所述的锂渣粉比表面积≥400m2/kg。
5.根据权利要求1所述的一种卵石型透水混凝土专用的复合型添加剂，其特征在于，所述聚氧化乙烯的分子量在400-600万之间。
CN201210410096.XA 2012-10-24 2012-10-24 一种卵石型透水混凝土专用的复合型添加剂 Active CN102898062B (zh)