CN100577599C - 石粉干粉砂浆 - Google Patents
石粉干粉砂浆 Download PDFInfo
- Publication number
- CN100577599C CN100577599C CN200810156406A CN200810156406A CN100577599C CN 100577599 C CN100577599 C CN 100577599C CN 200810156406 A CN200810156406 A CN 200810156406A CN 200810156406 A CN200810156406 A CN 200810156406A CN 100577599 C CN100577599 C CN 100577599C
- Authority
- CN
- China
- Prior art keywords
- mortar
- stone flour
- yellow ground
- flyash
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种石粉干粉砂浆，其特征在于该石粉干粉砂浆主要由水泥、粉煤灰、黄砂、石粉或砂浆稠化粉制成。本发明首创将石粉作为干粉砂浆的原料，并且砂浆中石粉的力学性能较黄砂优越，我们变废为宝，既经济又环保。
Description
技术领域
本发明属于建筑材料领域，具体涉及一种石粉干粉砂浆。
背景技术
石粉是采石场生产石子过程中产生的废弃物，堆积如山的石粉对环境造成严重污染，并且石粉的粉状物含量较多，所以人们不用石粉作为干粉砂浆的原料，认为会对强度和其他性能产生不利影响。
以前主要采用黄砂及一些添加剂生产干粉砂浆，就黄砂而言，需要中砂(细度模数2.3～3.0)，因湿拌混凝土等建筑施工对黄砂需求量很大，这就使得中砂供应不足。
我们经过对相同强度等级不同掺量以及对不同强度等级砂、石粉对掺进行试配、研究、调整，经过长期的努力，试配出强度合格的干粉砂浆，首创将石粉作为干粉砂浆的原料。
发明内容
本发明的目的是针对上述不足之处提供一种石粉干粉砂浆。
本发明的目的是通过以下方式实施的：
一种石粉干粉砂浆，其特征是该石粉干粉砂浆主要由如下质量百分比的干燥状态的原料制成：
水泥 10～35％
粉煤灰 3～12％
黄砂 25～55％
石粉 25～55％
砂浆稠化粉 1.3～5.2％。
上述石粉干粉砂浆，其特征是该干粉砂浆还可加入如下添加剂：
占上述石粉干粉砂浆重量0.01～3.0％可再分散乳胶粉，
占上述石粉干粉砂浆重量0.01～1.0％纤维素醚，
占上述石粉干粉砂浆重量0.01～1.0％纤维，
占上述石粉干粉砂浆重量0.01～0.2％缓凝剂，
占上述石粉干粉砂浆重量0.01～1.0％减水剂，
和占上述石粉干粉砂浆重量0.01～4.0％早强剂。
本发明所述百分含量均为质量百分含量。
上述纤维素醚为甲基羟乙基纤维素醚或甲基羟丙基纤维素醚；上述纤维为合成纤维或木质纤维。
上述缓凝剂可为木质磺酸钙或磷酸钠等；所述的减水剂可为木质素磺酸钙或三聚氰胺等；所述的早强剂可为甲酸钙或硫酸钠等。
石粉是石灰石破碎所得，质地坚硬，有尖锐棱角，表面粗糙，和水泥粘结性好。石粉的质量取决于级配，级配好的石粉空隙率小，容量大，密实性好，本发明使用石粉细度模数2.7～3.0，优选2.9，级配二区。黄砂的细度模数2.7～3.0，优选2.8，级配二区。拌合物稠度相近，用于包裹细骨料的净浆适中，刚能填充细骨料间间隙。黄砂与石粉细度模数相近。二者无论按什么比例混合，得到的复合级配与原级配相当。
石粉中“粉”含量较大，过0.080mm筛的粉算作“泥”，但石粉中的“泥”和砂中的“泥”不同，前者和水泥浆粘结性较好。
我们经过长期的、大量的试配工作，在干粉砂浆中掺石粉，研究石粉对砂浆强度的影响，试配结果表明，干粉砂浆中掺石粉并没有对强度产生负面影响。本配比适用普通砂浆，也适用于特种砂浆。将按比例称取各种原料混合均匀，加入总料重量五分之一左右的水搅拌均匀即可使用。
本发明的有益效果：
在工作性相同的条件下，砂浆中石粉的力学性能较黄砂优越。市场上石粉的价格是黄砂的一半，使用石粉，我们变废为宝，既经济又环保，能显著提高经济效益。
具体实施方式
实施例1～12将按比例称取的各种原料混合均匀，加入总料重量五分之一左右的水搅拌均匀。
黄砂细度模数在2.7～3.0，二区中砂。石粉细度模数在2.7～3.0，级配二区。
结果：通过表1、表2中12个配比的试配的结果可以看出，石粉用量递增，强度影响不大。
实施例13～18将按比例称取的各种原料混合均匀，加入总料重量五分之一左右的水搅拌均匀。所用黄砂细度模数2.8，二区中砂。石粉细度模数2.9，级配二区。
结果：通过表3、表4对比，是一组6个不同强度等级的普通砂浆试配，砂、石粉对半掺与基准砂浆比较。(同时也做了这6个强度等级基准试配，即用水泥、粉煤灰、黄砂、稠化粉，强度合格)。
Claims (1)
1、一种石粉干粉砂浆，其特征是由如下质量百分比的原料制成：
水泥 10～35％
粉煤灰 3～12％
黄砂 25～55％
石粉 25～55％
砂浆稠化粉 1.3～5.2％，
占上述水泥、粉煤灰、黄砂、石粉和砂浆稠化粉总重量0.01～3.0％的可再分散乳胶粉，
占上述水泥、粉煤灰、黄砂、石粉和砂浆稠化粉总重量0.01～1.0％的纤维素醚，
占上述水泥、粉煤灰、黄砂、石粉和砂浆稠化粉总重量0.01～1.0％的纤维，
占上述水泥、粉煤灰、黄砂、石粉和砂浆稠化粉总重量0.01～0.2％的缓凝剂，
占上述水泥、粉煤灰、黄砂、石粉和砂浆稠化粉总重量0.01～1.0％的减水剂，
和上述水泥、粉煤灰、黄砂、石粉和砂浆稠化粉总重量0.01～4.0％的早强剂；
其中，所述的石粉细度模数2.7-3.0，级配二区；黄砂细度模数2.7-3.0，级配二区；所述的纤维素醚为甲基羟乙基纤维素醚或甲基羟丙基纤维素醚；所述的纤维为合成纤维或木质纤维；所述的缓凝剂为木质磺酸钙或磷酸钠；所述的减水剂为木质素磺酸钙或三聚氰胺；所述的早强剂为甲酸钙或硫酸钠。