CN102863885A - 一种具有变色效应的合成革用聚氨酯树脂组合物及其制备方法 - Google Patents

一种具有变色效应的合成革用聚氨酯树脂组合物及其制备方法 Download PDF

Info

Publication number
CN102863885A
CN102863885A CN2012103453254A CN201210345325A CN102863885A CN 102863885 A CN102863885 A CN 102863885A CN 2012103453254 A CN2012103453254 A CN 2012103453254A CN 201210345325 A CN201210345325 A CN 201210345325A CN 102863885 A CN102863885 A CN 102863885A
Authority
CN
China
Prior art keywords
polyurethane resin
synthetic leather
resin composition
parts
wax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103453254A
Other languages
English (en)
Other versions
CN102863885B (zh
Inventor
朱春凤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Lover Health Science and Technology Development Co Ltd
Original Assignee
Zhejiang Lover Health Science and Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Lover Health Science and Technology Development Co Ltd filed Critical Zhejiang Lover Health Science and Technology Development Co Ltd
Priority to CN201210345325.4A priority Critical patent/CN102863885B/zh
Publication of CN102863885A publication Critical patent/CN102863885A/zh
Application granted granted Critical
Publication of CN102863885B publication Critical patent/CN102863885B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种具有变色效应的合成革用聚氨酯树脂组合物及其制备方法，所述聚氨酯树脂组合物由如下质量份的组份制备得到：有机硅改性脂肪族聚氨酯树脂30-40份；N-二甲基甲酰胺40-70份；石油醚20-30份；变色蜡2-5份；疏水二氧化硅0.5-2份；端羟基烷烃聚硅氧烷1-3份。本发明选用耐黄变有机硅改性脂肪族聚氨酯树脂、变色蜡，尤其采用C15-C20的高级脂肪酸酯，并配合其他原料，用于合成革效应层，具有耐高温、耐黄变、稳定、蜡不析出、变色效果好等特点的聚氨酯树脂、蜡组合物。

Description

一种具有变色效应的合成革用聚氨酯树脂组合物及其制备方法
 
技术领域
本发明涉及一种聚氨酯树脂组合物，具体涉及一种具有变色效应的合成革用聚氨酯树脂组合物以及该组合物的制备方法。
背景技术
聚氨酯合成革是由无纺布、纺织布或可编织布等基布与聚氨酯树脂层及表面处理层组成。聚氨酯合成革按照聚氨酯成膜工艺的不同，可分为干法聚氨酯人造革和湿法聚氨酯人造革。所谓干法聚氨酯人造革，是指将溶剂型聚氨酯树脂中的溶剂挥发掉后，得到的多层薄膜加上底布而构成的多层结构体的半成品，再进行表面处理，制成各种风格和表面性能的合成革。通常干法合成革要求表面处理层光滑耐磨，耐弯曲性好，耐溶剂性好，有良好的重复涂敷性，颜料分散均匀、展色性佳等特点。 
湿法聚氨酯合成革是新—代天然皮革的最佳替代产品，它的生产方法是将聚氨酯树脂用溶剂DMF（N-二甲基甲酰胺）溶解，再添加各种助剂，制成浆料，浸渍或徐覆于基布上，然后放入与DMF（N-二甲基甲酰胺）溶剂具有较好的相溶性、而与聚氨酯树脂不亲相、不相溶的液体(如水)中，溶剂DMF(N-二甲基甲酰胺)被水置换，聚氨酯树脂逐渐凝固，从而形成多孔性的皮膜，即微孔聚氨酯粒面层。制得湿法聚氨酯半成品革，经表面整饰后．才能成为聚氨酯合成革成品。
具有变色效应的合成革（俗称疯马革）是市场上很流行的一种合成革，价格高，其表面具有真皮的外观，在拉伸、顶起、弯曲、折叠等外部应力作用下产生形变的部位会出现颜色由深到浅的变化，当外部应力消除，颜色恢复。但只有在效应层中加入一种特定碳原子数的蜡，才能出现这种变色效应。目前市场上用于合成革效应层的蜡粉变色效果较差，且在合成革的二次加工及在使用过程中，因所用的蜡粉是二氧化硅类，与聚氨酯类树脂相溶性较差，易迁移至革表面析出（行业俗称“吐蜡”），白白的呈现在革面上，尤其是在冬季，这种现象就更为突出。且涂层易发生黄变现象，导致合成革产品报废。 
发明内容
本发明所要解决的技术问题是，提供一种具有变色效应的合成革用聚氨酯树脂组合物，该组合物用于聚氨酯合成革表面处理后，合成革具有真皮一样的感观，在拉伸、顶起、弯曲、折叠等外部应力作用下产生形变的部位会出现颜色由深到浅的变化，当外部应力消除，颜色恢复。并且使用和加工过程不会有蜡析出。
本发明的技术方案：本发明所述的具有变色效应的合成革用聚氨酯树脂组合物，由如下质量份的组份制备得到：
有机硅改性脂肪族聚氨酯树脂     30-40份
N-二甲基甲酰胺           40-70份
石油醚                   20-30份
变色蜡                   2-5份
疏水二氧化硅             0.5-2份
端羟基烷烃聚硅氧烷       1-3份。
优选地，所述变色蜡是C15-C20的高级脂肪酸酯。
本发明所述的具有变色效应的合成革用聚氨酯树脂组合物的制备方法包括如下步骤：
（1）、按量取变色蜡、疏水二氧化硅、端羟基烷烃聚硅氧烷和石油醚，混合，搅拌均匀，得混合物A；
（2）、在所述混合物A中按量加入N-二甲基甲酰胺，搅拌均匀，得混合物B；
（3）、对混合物B继续搅拌，边搅拌边按量加入有机硅改性聚氨酯树脂，搅拌均匀，过滤，弃去滤渣，即得具有变色效应的聚氨酯树脂组合物。
本发明选用耐黄变有机硅改性脂肪族聚氨酯树脂、变色蜡，尤其采用C15-C20的高级脂肪酸酯，并配合其他原料，用于合成革效应层，具有耐高温、耐黄变、稳定、蜡不析出、变色效果好等特点的聚氨酯树脂、蜡组合物。具有耐黄变、自动梯度分层、表面滑爽、耐磨等特点。N-二甲基甲酰胺用作溶剂，石油醚是助溶剂，体系稳定，二者搭配，干燥速度合适，成膜效果好，涂层不会出现泛白现象。综上所述，采用本发明的聚氨酯树脂组合物进行合成革表面处理后，合成革具有真皮一样的感观，在拉伸、顶起、弯曲、折叠等外部应力作用下产生形变的部位会出现颜色由深到浅的变化，当外部应力消除，颜色恢复。并且使用和加工过程不会有蜡析出。 
具体实施方式
下面通过具体实施例进一步详细阐述本发明。
实施例1
取变色蜡2.5份，疏水二氧化硅1.5份，端羟基烷烃聚硅氧烷1.5份，石油醚20份，搅拌均匀，再加入N-二甲基甲酰胺61.5份，搅拌均匀，再边搅拌边加入30份的有机硅改性脂肪族聚氨酯树脂，搅拌均匀，过滤，弃去滤渣，即得上述所述的具有变色效应的合成革用聚氨酯树脂组合物。
实施例2
变色蜡3.5份，疏水二氧化硅1.0份，端羟基烷烃聚硅氧烷2.0份，石油醚25份，搅拌均匀，再加入60份的N-二甲基甲酰胺，搅拌均匀，再边搅拌边加入30份的有机硅改性脂肪族聚氨酯树脂，搅拌均匀，过滤，弃去滤渣，即得上述所述的具有变色效应的合成革用聚氨酯树脂组合物。
实施例3
变色蜡4.0份，疏水二氧化硅0.5份，端羟基烷烃聚硅氧烷2.5份，石油醚30份，搅拌均匀，再加入56.5份的N-二甲基甲酰胺，搅拌均匀，再边搅拌边加入30份的有机硅改性脂肪族聚氨酯树脂，搅拌均匀，过滤，弃去滤渣，即得上述所述的具有变色效应的合成革用聚氨酯树脂组合物。
以上有机硅改性脂肪族聚氨酯树脂采用市售产品以及现有文献所公开技术制备得到产品即可。
N-二甲基甲酰胺与石油醚的比例，春夏秋冬四季会有所不同，夏天石油醚的比例适当增加，冬季石油醚的比例适当减少，主要根据溶剂在不同温度环境中有不同的挥发速度的因素来确定的。
 
Figure 2012103453254100002DEST_PATH_IMAGE002

Claims (3)

1.一种具有变色效应的合成革用聚氨酯树脂组合物，其特征在于所述聚氨酯树脂组合物由如下质量份的组份制备得到：
有机硅改性脂肪族聚氨酯树脂     30-40份
N-二甲基甲酰胺           40-70份
石油醚                   20-30份
变色蜡                   2-5份
疏水二氧化硅             0.5-2份
端羟基烷烃聚硅氧烷       1-3份。
2.根据权利要求1所述的具有变色效应的合成革用聚氨酯树脂组合物，其特征在于所述变色蜡是C15-C20的高级脂肪酸酯。
3.一种如权利要求1或2任意一项权利要求所述的具有变色效应的合成革用聚氨酯树脂组合物的制备方法,其特征在于所述制备方法包括如下步骤：
（1）、按量取变色蜡、疏水二氧化硅、端羟基烷烃聚硅氧烷和石油醚，混合，搅拌均匀，得混合物A；
（2）、在所述混合物A中按量加入N-二甲基甲酰胺，搅拌均匀，得混合物B；
（3）、对混合物B继续搅拌，边搅拌边按量加入有机硅改性脂肪族聚氨酯树脂，搅拌均匀，过滤，弃去滤渣，即得具有变色效应的合成革用聚氨酯树脂组合物。
CN201210345325.4A 2012-09-18 2012-09-18 一种具有变色效应的合成革用聚氨酯树脂组合物及其制备方法 Expired - Fee Related CN102863885B (zh)