CN102851764A - 防火防霉织物的织造方法 - Google Patents

防火防霉织物的织造方法 Download PDF

Info

Publication number
CN102851764A
CN102851764A CN2012103500912A CN201210350091A CN102851764A CN 102851764 A CN102851764 A CN 102851764A CN 2012103500912 A CN2012103500912 A CN 2012103500912A CN 201210350091 A CN201210350091 A CN 201210350091A CN 102851764 A CN102851764 A CN 102851764A
Authority
CN
China
Prior art keywords
mildew
fire prevention
resistant
weaving method
fireproof
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103500912A
Other languages
English (en)
Inventor
严为忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN CITY ZHOUSHI FEIHUANG GARMENT FACTORY
Original Assignee
KUNSHAN CITY ZHOUSHI FEIHUANG GARMENT FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by KUNSHAN CITY ZHOUSHI FEIHUANG GARMENT FACTORY filed Critical KUNSHAN CITY ZHOUSHI FEIHUANG GARMENT FACTORY
Priority to CN2012103500912A priority Critical patent/CN102851764A/zh
Publication of CN102851764A publication Critical patent/CN102851764A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防火防霉织物的织造方法，包括如下步骤：将面料在含有防火防霉剂的浸渍液中经过浸轧工序后在65-80℃下烘干，然后在175-190℃之间恒温0.5-2小时；所述防火防霉剂由如下重量份的组分组成：有机磷化合物50-65份、六羟甲基三聚氰胺20-30份、渗透剂2-8份、硅烷偶联剂2-5份。本发明采用复配的防火防霉剂，可和纺织材料牢固结合，对纤维或纺织品有显著的阻燃、防霉作用；具有良好的耐久性，包括耐水洗、耐干洗、耐气候性等；不影响或较少影响纤维和织物的色泽、外观、手感和其他物理机械性能。

Description

防火防霉织物的织造方法
技术领域
本发明涉及一种防火防霉织物的织造方法。
背景技术
据统计，中国火灾死亡人数每年达上千人，而其中由纺织品引起的火灾约占一半，直接经济损失5亿元。其中床上用品、家具装饰用布和衣着用品是起火的主要原因。特别是建筑住宅火灾，纺织品着火蔓延所占的比例更大。纺织服装与人类直接接触，一旦燃烧，轻则部分皮肤烧伤，遭受痛苦，重则皮肤大面积烧焦烧伤，危及生命。另外，纺织品燃烧产生的有害气体也危害人的生命，如一氧化碳、二氧化碳、氰化氢、氧化氮、氨类和醛类气体等，都会造成人的窒息或毒害而死亡。
现有防霉面料通常采用在面料表面喷涂防霉剂，其短期有一定效果，但耐久性很差，经过水洗后很快失去防霉功效。而且目前很少既防火又防霉的多功能面料面世。
发明内容
本发明的目的在于提供一种防火防霉织物的织造方法，以克服现有技术存在的上述缺陷。
为解决上述技术问题，本发明防火防霉织物的织造方法，包括如下步骤：
1)防火防霉母粒制备：将防火防霉剂与纤维基料掺混、干燥，进入螺旋挤出机熔融共混挤出，造粒，得到防火防霉母粒；
2)防火防霉织物生产：将防火防霉母粒和纤维切片共混后，经纺丝、卷绕、拉伸后形成防火防霉纤维，然后和至少一种天然纤维混纺后得到防火防霉织物。
所述防火防霉剂由如下重量份的组分组成：
有机磷化合物        50-65份、
六羟甲基三聚氰胺    20-30份、
渗透剂              2-8份、
硅烷偶联剂          2-5份。
作为一种优选方案，所述有机磷化合物为含至少一个芳基的磷化合物；优选氧化三苯基膦。
渗透剂为脂肪醇聚氧乙烯醚(JFC)。
所述纤维基料与所述防火防霉剂的重量比为100∶3～100∶15。
防火防霉母粒和纤维切片按质量比1∶10～1∶20混合。
本发明采用复配的防火防霉剂，通过母粒法合成防火防霉纤维织物，可和纺织材料牢固结合，耐久性强，且具有如下有益效果：1、对纤维或纺织品有显著的阻燃、防霉作用；2、具有良好的耐久性，包括耐水洗、耐干洗、耐气候性等；3、不影响或较少影响纤维和织物的色泽、外观、手感和其他物理机械性能。本发明加工路线简单，易操作，成本低，易于工业化生产。且可和纤维组织牢固结合，耐久性强，无毒安全。
具体实施方式
实施例1
防火防霉剂的制备：
原料准备：
氧化三苯基膦      50份、
六羟甲基三聚氰胺  30份、
渗透剂JFC         2份、
硅烷偶联剂        5份。
防火防霉母粒制备：
将防火防霉剂与纤维基料掺混、干燥，进入螺旋挤出机熔融共混挤出，造粒，得到防火防霉母粒，纤维基料与防火防霉剂的重量比为100∶5；
防火防霉织物生产：
将防火防霉母粒和纤维切片按质量比1∶20共混后，经纺丝、卷绕、拉伸后形成防火防霉纤维，然后和羊毛按2∶1混纺后得到防火防霉织物。
实施例2
防火防霉剂的制备：
原料准备：
氧化三苯基膦      65份、
六羟甲基三聚氰胺  20份、
渗透剂JFC         8份、
硅烷偶联剂        2份。
防火防霉母粒制备：
将防火防霉剂与纤维基料掺混、干燥，进入螺旋挤出机熔融共混挤出，造粒，得到防火防霉母粒，纤维基料与防火防霉剂的重量比为100∶10；
防火防霉织物生产：
将防火防霉母粒和纤维切片按质量比1∶10共混后，经纺丝、卷绕、拉伸后形成防火防霉纤维，然后和木棉纤维按1∶1混纺后得到防火防霉织物。
应用实施例
1、耐久性
将防火防霉织物用含1克/升的中性洗涤剂以1∶50的织物与洗涤剂溶液的比例，在60℃左右洗涤30分钟，离心机脱水后60℃左右干燥。按上述方法分别洗涤5次、30次。
2、防火性能
按照国家标准GBT 17591-2006《阻燃织物》的方法测定防火性能(产品类别按照装饰用织物)，结果如下：
表1不同洗涤次数后的阻燃性能
Figure BSA00000779937300041
表甲a表示未经洗涤的防火防霉织物，b表示洗涤5次，c表示洗涤30次。
可见，本发明具有优良的耐水洗性能，经多次洗涤后仍具有良好的防火效果。
3、防霉性能
将本发明防火防霉织物放置在湿度大于90，温度20-30摄氏度的室内3个月后，未发现霉斑。

Claims (6)

1.一种防火防霉织物的织造方法，其特征在于，包括如下步骤：1)防火防霉母粒制备：将防火防霉剂与纤维基料掺混、干燥，进入螺旋挤出机熔融共混挤出，造粒，得到防火防霉母粒；2)防火防霉织物生产：将防火防霉母粒和纤维切片共混后，经纺丝、卷绕、拉伸后形成防火防霉纤维，然后和至少一种天然纤维混纺后得到防火防霉织物。
2.根据权利要求1所述的防火防霉织物的织造方法，其特征在于，所述防火防霉剂由如下重量份的组分组成：
有机磷化合物        50-65份、
六羟甲基三聚氰胺    20-30份、
渗透剂              2-8份、
硅烷偶联剂          2-5份。
3.根据权利要求2所述的防火防霉织物的织造方法，其特征在于，所述有机磷化合物为含有至少一个芳基的磷化合物。
4.根据权利要求3所述的防火防霉织物的织造方法，其特征在于，所述有机磷化合物为氧化三苯基膦。
5.根据权利要求1所述的防火防霉织物的织造方法，其特征在于，所述纤维基料与所述防火防霉剂的重量比为100∶3～100∶15。
6.根据权利要求1所述的防火防霉织物的织造方法，其特征在于，所述防火防霉母粒和纤维切片按质量比1∶10～1∶20混合。
CN2012103500912A 2012-09-20 2012-09-20 防火防霉织物的织造方法 Pending CN102851764A (zh)