CN102827412A - 一种天然杜仲橡胶增韧热塑性树脂的制备方法 - Google Patents

一种天然杜仲橡胶增韧热塑性树脂的制备方法 Download PDF

Info

Publication number
CN102827412A
CN102827412A CN2012103338383A CN201210333838A CN102827412A CN 102827412 A CN102827412 A CN 102827412A CN 2012103338383 A CN2012103338383 A CN 2012103338383A CN 201210333838 A CN201210333838 A CN 201210333838A CN 102827412 A CN102827412 A CN 102827412A
Authority
CN
China
Prior art keywords
preparation
thermoplastic resin
parts
rubber
gutta percha
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103338383A
Other languages
English (en)
Other versions
CN102827412B (zh
Inventor
方庆红
金鑫
胡之朗
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHILANG BIOLOGICAL RESOURCES APPLICATION INST ANKANG CITY
Shenyang University of Chemical Technology
Original Assignee
ZHILANG BIOLOGICAL RESOURCES APPLICATION INST ANKANG CITY
Shenyang University of Chemical Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHILANG BIOLOGICAL RESOURCES APPLICATION INST ANKANG CITY, Shenyang University of Chemical Technology filed Critical ZHILANG BIOLOGICAL RESOURCES APPLICATION INST ANKANG CITY
Priority to CN201210333838.3A priority Critical patent/CN102827412B/zh
Publication of CN102827412A publication Critical patent/CN102827412A/zh
Application granted granted Critical
Publication of CN102827412B publication Critical patent/CN102827412B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种天然杜仲橡胶增韧热塑性树脂的制备方法，涉及一种热塑性树脂的制备方法，（1）以天然杜仲橡胶为原料，增韧热塑性树脂制备复合材料，按以下配比进行混料：天然杜仲橡胶0-50份，热塑性树脂100份，其他塑料常用填加助剂10份；（2）将共混物按常规工艺挤出，造粒50℃烘干4小时；（3）将造粒共混物进行注射成型；（4）将造粒共混物进行模压成型即可。该增韧热塑性树脂具有优异抗冲击性能、较高的熔点和维卡软化温度。其制备方法工艺简单、易于操作，适用于各种热塑性树脂的增韧，广泛适用于工程与制品领域。因此，具有较强的推广和应用价值。

Description

一种天然杜仲橡胶增韧热塑性树脂的制备方法
技术领域
本发明涉及一种热塑性树脂的制备方法，特别是涉及一种天然杜仲橡胶增韧热塑性树脂的制备方法。
背景技术
我国天然杜仲资源丰富,自然分布在湘、黔、川、陕、鄂、豫等地山区,近20年来,国家大力推广人工种植,种植范围扩大到南起两广,北至吉林,西达新疆,可种植范围远远超过了天然橡胶树,目前种植面积已逾300万亩。
天然杜仲橡胶的化学成分是反-1，4-聚异戊二烯，是巴西橡胶的成分顺-1，4-聚异戊二烯的同分异构体, 它们的物理性质大不相同。杜仲胶在室温时是皮革状的坚韧物质，纯杜仲橡胶为无色，商品胶则带有各种颜色。纯杜仲橡胶在10℃时结晶，40～50℃开始表现有弹性，易伸长，100℃软化，具有可塑性,冷却后可恢复原来的性质。其软化点与可塑性随树脂含量而异。
热塑性树脂加热时变软以至流动，冷却变硬，这种过程是可逆的，可以反复进行。聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、聚甲醛，聚碳酸酯，聚酰胺、丙烯酸类塑料、其它聚烯烃及其共聚物、聚讽、聚苯醚，氯化聚醚等热塑性塑料。热塑性塑料中树脂分子链都是线型或带支链的结构，分子链之间无化学键产生，加热时软化流动．冷却变硬的过程是物理变化。
近年来的研究发现，天然杜仲橡胶可以用于热塑性树脂的增韧，开发热塑性功能材料，顺应了国际上发展反式橡胶的趋势。
发明内容
本发明的目的在于提供一种天然杜仲橡胶增韧热塑性树脂的制备方法，将天然杜仲橡胶与热塑性树脂或热塑性树脂复合材料共混，制得的材料具有较好的加工性和韧性，特别是银纹剪切带的快速增长时的增韧效果非常明显。
本发明的目的是通过以下技术方案实现的：
一种天然杜仲橡胶增韧热塑性树脂的制备方法，所述方法包括以下过程：
（1）以天然杜仲橡胶为原料，增韧热塑性树脂制备复合材料，按以下配比进行混料：天然杜仲橡胶0-50份，热塑性树脂100份，其他塑料常用填加助剂10份；
（2）将共混物按常规工艺挤出，造粒50℃烘干4小时；
（3）将造粒共混物进行注射成型；
（4）将造粒共混物进行模压成型即可。
所述的一种天然杜仲橡胶增韧热塑性树脂的制备方法，所述热塑性树脂包含聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、聚甲醛，聚碳酸酯，聚酰胺、丙烯酸类塑料、其它聚烯烃及其共聚物、聚讽、聚苯醚，氯化聚醚。
本发明的优点与效果是：
本发明增韧热塑性树脂效果明显，特别是银纹剪切带的快速增长（如进行标准的悬臂梁冲击实验）时的增韧效果非常明显。在增韧条件下，该增韧热塑性树脂具有优异抗冲击性能、较高的熔点和维卡软化温度，适用于非常广泛的领域，其制备方法工艺简单、易于操作，适用于各种热塑性树脂的增韧，因此，具有较强的推广和应用价值。
附图说明
图1为银纹剪切带的快速增长纯聚丙烯照片示意图；
图2为银纹剪切带的快速增长含5份天然杜仲橡胶照片示意图；
图3为银纹剪切带的快速增长含10份天然杜仲橡胶照片示意图；
图4为银纹剪切带的快速增长含15粉天然杜仲橡胶照片示意图；
图5为银纹剪切带的快速增长含20份天然杜仲橡胶照片示意图；
图6为银纹剪切带的快速增长含25份杜仲天然橡胶照片示意图；
图7为银纹剪切带的快速增长含30份天然杜仲橡胶照片示意图。
注：本发明的图1—图7为产物状态的分析示意图照片，图中文字或影像不清晰并不影响对本发明技术方案的理解。
具体实施方式
下面结合实施例对本发明进行详细说明。
实施例：
（1）将天然杜仲粗胶低温烘干（50℃干燥24小时）。
（2）按以下配比进行混料：杜仲胶0-30份，以5份为变量，聚丙烯100份。其他为抗氧剂5份。
（3）将杜仲胶与聚丙烯的共混物挤出（工艺条件依照表1），造粒。
（4）将杜仲胶与聚丙烯的共混颗粒用注塑机注塑（工艺条件依照表2）出被测试样。
表1：挤出条件
控区 一区 二区 三区 四区 五区 机头
温度/℃ 180 190 200 200 190 180
表2：注塑条件
控 区 一 区/℃ 二区/℃ 三区/℃ 四区/℃ 五区/℃ 机头/℃ 开模压力/Mpa 锁模压力/Mpa
  180 190 200 200 190 180 90 128
利用所申请方法，依照如下配方方案进行试验。
表3：配方
杜仲胶/份数 0 5 10 15 20 25 30
聚丙烯/份数 100 95 90 85 80 75 70
表4：试样的性能
Figure 2012103338383100002DEST_PATH_IMAGE001
。
本发明以天然杜仲橡胶为增韧原料，增韧热塑性树脂，制备复合材料。热塑性树脂包含聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、聚甲醛，聚碳酸酯，聚酰胺、丙烯酸类塑料、其它聚烯烃及其共聚物、聚讽、聚苯醚，氯化聚醚等。增韧材料为天然杜仲橡胶。其他添加剂为常规加工助剂。
将共混物挤出，造粒。将所造出的共混物颗粒在50℃的烘箱内烘4小时。将造粒共混物进行常规工艺注射成型。将造粒共混物进行常规工艺模压成型。

Claims (2)

1.一种天然杜仲橡胶增韧热塑性树脂的制备方法，其特征在于，所述方法包括以下过程：
（1）以天然杜仲橡胶为原料，增韧热塑性树脂制备复合材料，按以下配比进行混料：天然杜仲橡胶0-50份，热塑性树脂100份，其他塑料常用填加助剂10份；
（2）将共混物按常规工艺挤出，造粒50℃烘干4小时；
（3）将造粒共混物进行注射成型；
（4）将造粒共混物进行模压成型即可。
2.根据权利要求1所述的一种天然杜仲橡胶增韧热塑性树脂的制备方法，其特征在于，所述热塑性树脂包含聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、聚甲醛，聚碳酸酯，聚酰胺、丙烯酸类塑料、其它聚烯烃及其共聚物、聚讽、聚苯醚，氯化聚醚。
CN201210333838.3A 2012-09-11 2012-09-11 一种天然杜仲橡胶增韧热塑性树脂的制备方法 Active CN102827412B (zh)