CN102807713A - 三元乙丙橡胶组合物及应用 - Google Patents

三元乙丙橡胶组合物及应用 Download PDF

Info

Publication number
CN102807713A
CN102807713A CN2012102711403A CN201210271140A CN102807713A CN 102807713 A CN102807713 A CN 102807713A CN 2012102711403 A CN2012102711403 A CN 2012102711403A CN 201210271140 A CN201210271140 A CN 201210271140A CN 102807713 A CN102807713 A CN 102807713A
Authority
CN
China
Prior art keywords
ethylene propylene
diene monomer
propylene diene
accelerant
monomer composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102711403A
Other languages
English (en)
Inventor
张洪起
张桂林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Pengling Rubber Hose Co Ltd
Original Assignee
Tianjin Pengling Rubber Hose Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Pengling Rubber Hose Co Ltd filed Critical Tianjin Pengling Rubber Hose Co Ltd
Priority to CN2012102711403A priority Critical patent/CN102807713A/zh
Publication of CN102807713A publication Critical patent/CN102807713A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种三元乙丙橡胶组合物及应用,三元乙丙生胶、氧化锌、聚乙二醇、硬脂酸、防老剂RD、古马隆、快压出炭黑、功能性填料Create-E2、石蜡油、促进剂BZ、促进剂TMTD、促进剂DPTT和硫化剂硫磺组成;使用本发明的三元乙丙橡胶应用于汽车软管;具有工艺性能稳定,使用寿命长等特点,完全可以满足当前的使用要求。

Description

三元乙丙橡胶组合物及应用
技术领域
本发明涉及橡胶技术领域,具体地涉及一种用于耐热老化性和耐电化学腐蚀的三元乙丙橡胶组合物及应用。
背景技术
随着汽车工业的飞速发展,汽车正朝着轻型、高效、经济的方向发展这就导致汽车车身和发动机结构变得越来越紧凑,整车的性能也不断提高,因此使汽车冷却系统的工作温度在升高,同时由于汽车在运行过程中,发动机与周边部件之间形成电位差,在长期的电化学腐蚀作用下使胶管内壁产生裂纹,严重影响胶管的使用寿命。用于耐热老化性和耐电化学腐蚀的三元乙丙橡胶组合物比硫磺硫化的三元乙丙橡胶电阻率高得多,不易产生电化学腐蚀,而且耐热老化性也更好,是今后应用的趋势。
发明内容
本发明的目的在于提供一种用于耐热老化性和耐电化学腐蚀的三元乙丙橡胶组合物,以更好的满足当前的使用要求。
所述用于耐热老化性和耐电化学腐蚀的三元乙丙橡胶组合物的组份与质量份数比为:
  组分   质量份数
  三元乙丙生胶   100
  氧化锌   3~10
  聚乙二醇   2~6
  硬脂酸   1~4
  防老剂RD   0.5~2
  古马隆   2~7
  快压出炭黑   70~100
  功能性填料Create-E2   65~95
  石蜡油   35~65
  促进剂BZ   0.8~2.2
  促进剂TMTD   0.4~0.8
  促进剂DPTT   0.7~1.5
  促进剂DTDM   0.8~2.0
  硫磺   0~0.8
在本发明中优选用ML(1+4)125℃门尼粘度为70~90的三元乙丙生胶,使胶料具有较高的门尼粘度,从而赋予了胶料在挤出过程中具有良好的耐塌瘪性。
本发明中选用快压出炭黑,既赋予了产品良好的挤出特性,又提供了产品较好的补强性能。
本发明中选用功能性填料Create-E2,其成份为水合二氧化硅及其盐类衍生物,部分代替原有配方中的炭黑,又提供了产品优异的耐热老化性和耐电化学腐蚀性。
本发明选用闪点大于260℃的石蜡油,赋予了产品良好的耐热老化性和耐冷却液性。
在本发明中选用低硫(或无硫)高促进剂的硫化体系,赋予了胶料良好的耐热和压变性能。
在本发明中加入的防老剂为RD为2,2,4-三甲基-1,2-二氢化喹啉、促进剂BZ为二丁基二硫代氨基甲酸锌、促进剂TMTD为二硫化四甲基秋兰姆、促进剂DPTT为六硫化双(1,5-亚戊基)秋兰姆、促进剂DTDM为二硫化二吗啡啉。
使用本发明的三元乙丙橡胶生产的散热器胶管具有工艺性能稳定,使用寿命长等特点,完全可以满足当前的使用要求。
具体实施方式
用于耐热老化性和耐电化学腐蚀的三元乙丙橡胶组合物实施方式:以质量份数计
Figure BDA00001964324900021
按实施例配方中原材料做成胶片进行试验检测,用于耐冷却液和耐电化学腐蚀的三元乙丙橡胶组合物性能如下:
Figure BDA00001964324900032
由上表的数据可以得出,与现有配方相比,耐冷却液和耐电化学腐蚀的三元乙丙橡胶组合物制造的汽车软管,具有更好的耐热老化性、耐冷却液和耐电化学腐蚀性,能够满足当前的使用要求。

Claims (2)

1.一种三元乙丙橡胶组合物,其特征是组份与质量份数为:
Figure 6
2.如权利要求1所述的三元乙丙橡胶组合物应用于汽车软管。 
CN2012102711403A 2012-07-31 2012-07-31 三元乙丙橡胶组合物及应用 Pending CN102807713A (zh)