CN102786774A - 一种烘烤涂料用水分散环氧树脂及其制备方法 - Google Patents
一种烘烤涂料用水分散环氧树脂及其制备方法 Download PDFInfo
- Publication number
- CN102786774A CN102786774A CN2012102575470A CN201210257547A CN102786774A CN 102786774 A CN102786774 A CN 102786774A CN 2012102575470 A CN2012102575470 A CN 2012102575470A CN 201210257547 A CN201210257547 A CN 201210257547A CN 102786774 A CN102786774 A CN 102786774A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- water
- diethylolamine
- dispersed
- toluene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及了一种烘烤涂料用水分散环氧树脂及其制备方法。其特征在于该烘烤涂料用水分散环氧树脂主要由：环氧树脂、甲苯、正丁醇、二乙醇胺、葡萄糖酸、蒸馏水等组成。该烘烤涂料用水分散环氧树脂具有涂层透明光亮，漆膜弹性好，耐有机酸、耐化学性和耐气候性等特点。
Description
技术领域
本发明涉及一种烘烤涂料用水分散环氧树脂及其制备方法，属化工涂料防护领域。
背景技术
环氧树脂涂料它具有优良的工艺性能、机械性能和物理性能，应用十分广泛。目前，常用的环氧树脂涂料大多数为粘稠的液体或固体的，不溶于水，而溶于芳烃类、酮类等有机溶剂，而有机溶剂易挥发、且易燃易爆，有毒，对环境和人体造成很大的危害，随着人们对环境保护的要求日益迫切和严格，使用水性涂料的要求日益高涨，环氧树脂水性化便应用而生。
所谓水性环氧树脂是通过物理或化学的方法，使环氧树脂以微粒或液滴的形式分散在以水为连续相的分散介质中而配制的稳定分散体系。按物理特性可分为水乳型体系和水溶型体系。其中，以环氧树脂为母体，自由基引发甲基丙烯酸，丙烯酸乙脂，丙烯酸丁脂及苯乙烯，接枝共聚反应。然后加氨水成盐，制得水性环氧涂料。该涂料不能室温固化；水乳型体系典型方法是以聚乙二醇-邻苯二甲酸酐-环氧树脂多元嵌段其聚体为乳化剂，环氧树脂以液滴的方式分散于水而形成半透明至乳白色的乳液体系，液滴表面为具有亲水性基因的乳化剂分子液滴，内部为疏水性的环氧树脂分子，该体系虽然工艺简单，但乳液稳定性差；还有把环氧树脂溶解在乙二醇丁醚和乙醇混合溶剂中，与氨基苯甲酸进行反应，产物用乙醇胺中和，加水制成乳液，而该涂膜不能在室温固化，应用受到限制。
发明内容
为了解决上述存在的技术问题，本发明的目的是要提供一种用于烘烤涂料用的水分散环氧树脂，其特征在于该烘烤涂料用水分散环氧树脂主要由：环氧树脂、甲苯、正丁醇、二乙醇胺、葡萄糖酸、蒸馏水等组成。
按以重量比为：环氧树脂350～400；甲苯40～50；正丁醇130～140；二乙醇胺60～90；葡萄糖酸8.0～12；蒸馏水350～500等组成。
其二乙醇胺的质量为0.01mol/100g的环氧树脂。
其制备方法为：先将环氧树脂进行熔融，加入甲苯和正丁醇，在125℃中熔化1h，将温度逐渐降到80℃，然后在15min中内滴加二乙醇胺，使该混合物在80℃中进一步反应1h，然后加入5％浓度的葡萄糖酸，在70℃保持1h，所得混合物冷却到40℃，在1h内边搅拌边加入蒸馏水，保持在40℃的温度下，以真空除去水和溶剂混合物，测得其固体含量63～64，PH值3.7，然后用50～60μm的纱布过滤，得到水分散环氧树脂。
具体实施方法
1、分别按重量比称取环氧树脂365；甲苯43；正丁醇135；二乙醇胺65；葡萄糖酸11；蒸馏水450，备用。
2、制备方法
先将环氧树脂进行熔融，加入甲苯和正丁醇，在125℃中熔化1h，将温度逐渐降到80℃，然后在15min中内滴加二乙醇胺，使该混合物在80℃中进一步反应1h，然后加入5％浓度的葡萄糖酸，在70℃保持1h，所得混合物冷却到40℃，在1h内边搅拌边加入蒸馏水，保持在40℃的温度下，以真空除去水和溶剂混合物，测得其固体含量63～64，PH值3.7，然后用50～60μm的纱布过滤，得到水分散环氧树脂。
Claims (4)
1.一种烘烤涂料用水分散环氧树脂及其制备方法。其特征在于该烘烤涂料用水分散环氧树脂主要由：环氧树脂、甲苯、正丁醇、二乙醇胺、葡萄糖酸、蒸馏水等组成。
2.根据权利1所述的一种烘烤涂料用水分散环氧树脂。按以重量比为：环氧树脂350～400；甲苯40～50；正丁醇130～140；二乙醇胺60～90；葡萄糖酸8.0～12；蒸馏水350～500等组成。
3.根据权利1、2所述的一种烘烤涂料用水分散环氧树脂，其二乙醇胺的质量为0.01mol/100g的环氧树脂。
4.根据权利1和2所述的一种烘烤涂料用水分散环氧树脂，其制备方法为：先将环氧树脂进行熔融，加入甲苯和正丁醇，在125℃中熔化1h，将温度逐渐降到80℃，然后在15min中内滴加二乙醇胺，使该混合物在80℃中进一步反应1h，然后加入5％浓度的葡萄糖酸，在70℃保持1h，所得混合物冷却到40℃，在1h内边搅拌边加入蒸馏水，保持在40℃的温度下，以真空除去水和溶剂混合物，测得其固体含量63～64，PH值3.7，然后用50～60μm的纱布过滤，得到水分散环氧树脂。