CN102746592B - 一种耐火耐高温型防腐控制电缆料及其制备方法 - Google Patents

一种耐火耐高温型防腐控制电缆料及其制备方法 Download PDF

Info

Publication number
CN102746592B
CN102746592B CN201210185783.6A CN201210185783A CN102746592B CN 102746592 B CN102746592 B CN 102746592B CN 201210185783 A CN201210185783 A CN 201210185783A CN 102746592 B CN102746592 B CN 102746592B
Authority
CN
China
Prior art keywords
temperature resistant
control cable
paracril
pvc
resins
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210185783.6A
Other languages
English (en)
Other versions
CN102746592A (zh
Inventor
何忠胜
高世宏
闻广圈
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SHENGHUA CABLE GROUP Co Ltd
Original Assignee
ANHUI SHENGHUA CABLE GROUP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SHENGHUA CABLE GROUP Co Ltd filed Critical ANHUI SHENGHUA CABLE GROUP Co Ltd
Priority to CN201210185783.6A priority Critical patent/CN102746592B/zh
Publication of CN102746592A publication Critical patent/CN102746592A/zh
Application granted granted Critical
Publication of CN102746592B publication Critical patent/CN102746592B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种耐火耐高温型防腐控制电缆料及其制备方法，该电缆料包括以下组分及含量：丁腈橡胶30-40份、聚氯乙烯树脂90-100份、增塑剂3-8份、半补强炭黑5-10份、硬脂酸锌3-5份、三氧化锑5-10份、改性石蜡10-15份、氢氧化铝1.5-3份、三烯丙基异三聚氰酸酯1-3份和ECHO.A噻二唑衍生物1-4份。本发明由于采用丁腈橡胶和聚氯乙烯树脂高分子材料并用作为本发明的基础材料，解决了目前市场该类材料不能满足在高温强腐蚀的环境下工作使用现状，具有耐火耐高温抗腐蚀的特性，以及具有良好的耐磨、耐油、绝缘电气、物理机械以及柔软的特性。

Description

一种耐火耐高温型防腐控制电缆料及其制备方法
技术领域
本发明涉及一种耐火耐高温型防腐控制电缆料及其制备方法，属于电缆制造领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，随着电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视；电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，特别是航空导线、汽车用线、高温仪表电缆、石油钻井平台电缆等许多场合，越来越需要使用耐高温、耐气候的耐火耐高温型防腐控制电缆料。
发明内容
本发明的目的是在于克服上述已有技术的不足，提供一种耐火耐高温型防腐控制电缆料及其制备方法。
为了实现上述目的本发明采用如下技术方案：
耐火耐高温型防腐控制电缆料，各原料组分的重量份为：
丁腈橡胶30-40份
聚氯乙烯树脂90-100份
增塑剂3-8份
半补强炭黑5-10份
硬脂酸锌3-5份
三氧化锑140-150份
改性石蜡10-15份
氢氧化铝1.5-3份
三烯丙基异三聚氰酸酯1-3份
ECHO.A噻二唑衍生物1-4份。
耐火耐高温型防腐控制电缆料，所述的增塑剂由柠檬酸三丁酯10-15、正丁醇3-5、聚乙二醇5-10、氯化石蜡20-25、纳米TiO20.2-0.5、纳米氧化钡0.2-0.5、甘油三醋酸酯10-15、甲基丙烯酸正丁酯20-25、偏苯三酸三辛酯10-15和丙三醇三甘油酸酯20-25混合制备而成。
耐火耐高温型防腐控制电缆料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，将丁腈橡胶和聚氯乙烯树脂混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入增塑剂、半补强炭黑、硬脂酸锌、三氧化锑、改性石蜡、氢氧化铝、三烯丙基异三聚氰酸酯、ECHO.A噻二唑衍生物，常温下低速搅拌1-2分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度140-180℃，得到成品。
本发明的优点：
本发明由于采用丁腈橡胶和聚氯乙烯树脂高分子材料并用作为本发明的基础材料，解决了目前市场该类材料不能满足在高温强腐蚀的环境下工作使用现状，具有耐火耐高温抗腐蚀的特性，以及具有良好的耐磨、耐油、绝缘电气、物理机械以及柔软的特性。
具体实施方式
实施例1：
耐火耐高温型防腐控制电缆料，各原料组分的重量份为：
丁腈橡胶35份
聚氯乙烯树脂90份
增塑剂8份
半补强炭黑5份
硬脂酸锌3份
三氧化锑140份
改性石蜡12份
氢氧化铝1.9份
三烯丙基异三聚氰酸酯1.5份
ECHO.A噻二唑衍生物1.5份。
耐火耐高温型防腐控制电缆料，所述的增塑剂由柠檬酸三丁酯10-15、正丁醇3-5、聚乙二醇5-10、氯化石蜡20-25、纳米TiO20.2-0.5、纳米氧化钡0.2-0.5、甘油三醋酸酯10-15、甲基丙烯酸正丁酯20-25、偏苯三酸三辛酯10-15和丙三醇三甘油酸酯20-25混合制备而成。
耐火耐高温型防腐控制电缆料的制备方法，包括以下步骤：
（1）按组成原料的重量份称取各原料，将丁腈橡胶和聚氯乙烯树脂混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入增塑剂、半补强炭黑、硬脂酸锌、三氧化锑、改性石蜡、氢氧化铝、三烯丙基异三聚氰酸酯、ECHO.A噻二唑衍生物，常温下低速搅拌1-2分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度140-180℃，得到成品。
本发明的电缆料性能数据：绝缘0.35-0.55mm，火花实验通过，耐火实验3.5/5min通过，电缆弯曲半径：15倍电缆直径，低温-40℃下不开裂，-40℃温度下拉伸实验：250%，热延伸实验：载荷下伸张率≤175，冷却后永久伸张率≤15。

Claims (2)

1.一种耐火耐高温型防腐控制电缆料，其特征在于各原料组分的重量份为：
丁腈橡胶30-40份
聚氯乙烯树脂90-100份
增塑剂3-8份
半补强炭黑5-10份
硬脂酸锌3-5份
三氧化锑140-150份
改性石蜡10-15份
氢氧化铝1.5-3份
三烯丙基异三聚氰酸酯1-3份
ECHO.A噻二唑衍生物1-4份；
所述的增塑剂由柠檬酸三丁酯10-15、正丁醇3-5、聚乙二醇5-10、氯化石蜡20-25、纳米TiO20.2-0.5、纳米氧化钡0.2-0.5、甘油三醋酸酯10-15、甲基丙烯酸正丁酯20-25、偏苯三酸三辛酯10-15和丙三醇三甘油酸酯20-25混合制备而成。
2.一种如权利要求1所述的耐火耐高温型防腐控制电缆料的制备方法，其特征在于包括以下步骤：
（1）按组成原料的重量份称取各原料，将丁腈橡胶和聚氯乙烯树脂混合均匀，得到混合料A；
（2）在上述步骤（1）中的混合料A中按重量份加入增塑剂、半补强炭黑、硬脂酸锌、三氧化锑、改性石蜡、氢氧化铝、三烯丙基异三聚氰酸酯、ECHO.A噻二唑衍生物，常温下低速搅拌1-2分钟，使得混合均匀，得到混合料B；
（3）将上述步骤（2）得到的混合料B加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度140-180℃，得到成品。
CN201210185783.6A 2012-06-07 2012-06-07 一种耐火耐高温型防腐控制电缆料及其制备方法 Expired - Fee Related CN102746592B (zh)