CN102732102A - Environment-friendly emulsion paint formula and manufacturing method thereof - Google Patents
Environment-friendly emulsion paint formula and manufacturing method thereof Download PDFInfo
- Publication number
- CN102732102A CN102732102A CN2011100878135A CN201110087813A CN102732102A CN 102732102 A CN102732102 A CN 102732102A CN 2011100878135 A CN2011100878135 A CN 2011100878135A CN 201110087813 A CN201110087813 A CN 201110087813A CN 102732102 A CN102732102 A CN 102732102A
- Authority
- CN
- China
- Prior art keywords
- emulsion paint
- water
- negative ion
- emulsion
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of chemical engineering and in particular refers to an environment-friendly emulsion paint formula and a manufacturing method thereof, wherein the environment-friendly emulsion paint comprises water, titanium dioxide, heavy calcium carbonate, a styrene acrylic emulsion, glycol and germanium mineral powders. The total formula materials of the emulsion paint comprises, by weight, 10%-30% of water, 10%-30% of titanium dioxide, 1%-10% of heavy calcium carbonate, 20%-38% of styrene acrylic emulsion, 0.1%-0.4% of wetting agent, 0.1%-0.4% of antibacterial preservative, 0.1%-0.3% of polyurethane associative thickener, 0.1%-0.6% of acrylic acid thickener, 1%-6% of glycol and 20%-60% of anion mineral powder. The environment-friendly emulsion paint is obtained by mixing the emulsion paint with the anion mineral powders and then uniformly stirring the mixture. The environment-friendly emulsion paint is poison-free, pollution free and beneficial to human health.
Description
Technical field:
The present invention relates to chemical technology field, refer in particular to a kind of environment friendly emulsion paint prescription and making method.
Background technology:
Present people's finishing room all can use lacquer or the coating wall of whitewashing a wall, wherein; Containing formaldehyde etc. in lacquer or the coating has the volatile matter of toxin, and this lacquer or coating can cause very big injury to human body, carries out room air detected result every household formaldehyde content according to the family of expert after to more or less a hundred finishing and surpasses national standard; The highlyest exceed standard 30 times, living in the people who fitted up in the house for a long time all can have by dazzling, pungent, stimulate throat and the strong cognition of surrounding of neuroactive gas; And the smell of this moment is exactly the gas that contains formaldehyde poison gas, and is well-known: formaldehyde is toxic gas and the invisible killer in the room, finishing back, is to cause mouth; Nose, tracheae; The arch-criminal of position diseases such as esophageal-gastric, liver, heart and cancer, the major suspect who causes " white blood disease " especially more has harm to children and old man.The formaldehyde toxic gas is to function of human body in addition, and the big murder by poisoning that fetus is caused in nerve, intelligence, memory, thinking, sexuality and the body reaches the release period in 15 years, as ghost, drifts everywhere, and the ghost lingers on! Cause unclear the dying of illness in the formaldehyde toxic gas of several ten million people arranged global every year! By formaldehyde cause and the disease that causes considerably beyond the sickness rate of AIDS, people are poisoned by it deeply, PARA FORMALDEHYDE PRILLS(91,95) is abhored already.
Summary of the invention:
The objective of the invention is deficiency, and a kind of environment friendly emulsion paint prescription and making method are provided to prior art, its no toxin, pollution-free is useful to HUMAN HEALTH.
For realizing above-mentioned purpose; The present invention adopts following technical scheme; It comprises water, white titanium pigment, water-ground limestone, benzene emulsion, terepthaloyl moietie, germanium ore powder, and the weight percent that its content accounts for total formulation material is respectively: water 10%～30%, white titanium pigment 10%～30%, water-ground limestone 1%～10%, benzene emulsion 20%～38%, wetting agent 0.1%-0.4%, fungicidal preservative 0.1%-0.4%, polyurethane associative thickener 0.1%-0.3%, acrylic acid class thickening material 0.1%-0.6%, terepthaloyl moietie 1%～6%, negative ion ore powder are 20%～60%.
Described negative ion powder is for adopting a kind of the processing in the germanium ore, and negative ion ore powder composition per-cent is respectively: SiO
2Be 20%-70%, B
2O
3Be 4%-12%, Al
2O
3Be 20%-60%, Fe
2O
3For 0.2%-0.6%, MnO are that 0.8%-1.5%, MgO are that 0.1%-0.5%, CaO are 0.2%-0.8%, Na
2O is 1%-4%, Li
2O is 0.4%-1.2%, Rb
2O is that 0.01%-0.04%, F are 0.8%-1.6%, H
2O+ is 2%-6%, TiO
20.01%-0.03%.
The making method of environment friendly emulsion paint, the making method step is:
(1), measures with the water of 10%-30%, the wetting agent of 0.1%-0.4%, the dispersion agent of 0.1%-0.6%, the fungicidal preservative of 0.1%-0.4%, the suds suppressor of 0.05%-0.15%, the white titanium pigment of 10%-40%, the water-ground limestone of 1%-10% high-speed stirring dispersion 10-30 minute by prescription;
(2), measure the water of 10%-30%, the skimmer of 0.1%-0.4%, the film coalescence aid of 1%-4%, the polyurethane associative thickener of 0.1%-0.3%, 20%～60% benzene emulsion, 1%～6% terepthaloyl moietie, the acrylic acid class thickening material of 1%-6% by prescription; Add interior mixing of material of step (1), process rubber-emulsion paint.
(3), by measuring, with processing environment friendly emulsion paint after rubber-emulsion paint and the even stirring of negative ion ore powder with the negative ion ore powder of 1%-6% and the rubber-emulsion paint of 94%-99%.
Beneficial effect of the present invention is: it comprises water, white titanium pigment, water-ground limestone, benzene emulsion, terepthaloyl moietie, germanium ore powder, and the weight percent that its content accounts for total formulation material is respectively: water 10%～30%, white titanium pigment 10%～40%, water-ground limestone 1%～10%, benzene emulsion 20%～60%, wetting agent 0.1%-0.4%, fungicidal preservative 0.1%-0.4%, polyurethane associative thickener 0.1%-0.3%, acrylic acid class thickening material 0.1%-0.6%, terepthaloyl moietie 1%～6%, negative ion ore powder are 20%～60%.Its no toxin, pollution-free is useful to HUMAN HEALTH.
Embodiment:
The present invention adopts following technical scheme; It comprises water, white titanium pigment, water-ground limestone, benzene emulsion, terepthaloyl moietie (antifreezing agent), germanium ore powder, and the weight percent that its content accounts for total formulation material is respectively: water 10%～30%, white titanium pigment 10%～30%, water-ground limestone 1%～10%, benzene emulsion 20%～38%, wetting agent 0.1%-0.4%, fungicidal preservative 0.1%-0.4%, polyurethane associative thickener 0.1%-0.3%, acrylic acid class thickening material 0.1%-0.6%, terepthaloyl moietie 1%～6%, negative ion ore powder are 20%～60%.
Described negative ion powder is for adopting a kind of the processing in the germanium ore, and negative ion ore powder composition per-cent is respectively: SiO
2Be 20%-70%, B
2O
3Be 4%-12%, Al
2O
3Be 20%-60%, Fe
2O
3For 0.2%-0.6%, MnO are that 0.8%-1.5%, MgO are that 0.1%-0.5%, CaO are 0.2%-0.8%, Na
2O is 1%-4%, Li
2O is 0.4%-1.2%, Rb
2O is that 0.01%-0.04%, F are 0.8%-1.6%, H
2O+ is 2%-6%, TiO
20.01%-0.03%.Silicon-dioxide (ore includes composition)
Boron trioxide (ore includes composition), aluminium sesquioxide (ore includes composition), red oxide of iron (ore includes composition), manganese oxide (ore includes composition), Natural manganese dioxide (ore includes composition), quicklime (ore includes composition), sodium dioxide (ore includes composition), titanium dioxide lithium (ore includes composition), titanium dioxide rubidium (ore includes composition), fluorine (ore includes composition), crushing process volatilization 0.41% (ore includes composition), titanium oxide (ore includes composition);
The making method of environment friendly emulsion paint, the making method step is:
(1), by prescription metering with the dispersion agent of the wetting agent 0.1%-0.6% of the water of 10%-30%, 0.1%-0.4%, the fungicidal preservative of 0.1%-0.4%, the suds suppressor of 0.05%-0.15%, the white titanium pigment of 10%-40%, the water-ground limestone of 1%-10%, high-speed stirring was disperseed 10-30 minute;
(2), measure the water of 10%-30%, the skimmer of 0.1%-0.4%, the film coalescence aid of 1%-4%, the polyurethane associative thickener of 0.1%-0.3%, 20%～60% benzene emulsion, 1%～6% terepthaloyl moietie, the acrylic acid class thickening material of 1%-6% by prescription; Add interior mixing of material of step (1), process rubber-emulsion paint.
(3), by measuring, with processing environment friendly emulsion paint after rubber-emulsion paint and the even stirring of negative ion ore powder with the negative ion ore powder of 1%-6% and the rubber-emulsion paint of 94%-99%.
The environment friendly emulsion paint constructional method is: surface of wall is handled: remove surface dirt, and grease and loose plaster, replenish in the slit, guarantees the metope cleaning, and drying is smooth; Roller coat is brushed on metope, before the use, please do stirring, dilution: root a tree name situation, add the proper amount of clear water dilution.
Coating process: priming paint one time, twice of finish paint.(in 25～30 ℃ of room temperatures, every interval can cover application in 2 hours, as far as possible, please under moist or cold situation, did not construct).
After the cleaning application is stopped over and application finishes, please in time use the clear water cleaning means.
The application aftertreatment: please will be used for shutter with cutter, the adhesive tape at window place or U.S. line paper cut off, and are strictly on guard against frost.
Environment friendly emulsion paint of the present invention brush is after on the metope, and the negative ion ore powder can produce negative ion, and to people's effect in room, people can feel a kind of pure and fresh sensation, and are useful to HUMAN HEALTH, also environmental protection simultaneously.
Below be the examining report of national building materials inspection center:
Inspection center's numbering: 20111G00033-1
The examining report date of issuance: on March 14th, 2011
The above only is preferred embodiment of the present invention, so all equivalences of doing according to the described structure of patent claim of the present invention, characteristic and principle change or modify, includes in patent claim of the present invention.
Claims (3)
1. environment friendly emulsion paint prescription; It comprises water, white titanium pigment, water-ground limestone, benzene emulsion, terepthaloyl moietie, germanium ore powder, it is characterized in that: the weight percent that its content accounts for total formulation material is respectively: water 10%～30%, white titanium pigment 10%～30%, water-ground limestone 1%～10%, benzene emulsion 20%～38%, wetting agent 0.1%-0.4%, fungicidal preservative 0.1%-0.4%, polyurethane associative thickener 0.1%-0.3%, acrylic acid class thickening material 0.1%-0.6%, terepthaloyl moietie 1%～6%, negative ion ore powder are 20%～60%.
2. a kind of environment friendly emulsion paint prescription according to claim 1 is characterized in that: described negative ion powder is for adopting a kind of the processing in the germanium ore, and negative ion ore powder composition per-cent is respectively: SiO
2Be 20%-70%, B
2O
3Be 4%-12%, Al
2O
3Be 20%-60%, Fe
2O
3For 0.2%-0.6%, MnO are that 0.8%-1.5%, MgO are that 0.1%-0.5%, CaO are 0.2%-0.8%, Na
2O is 1%-4%, Li
2O is 0.4%-1.2%, Rb
2O is that 0.01%-0.04%, F are 0.8%-1.6%, H
2O+ is 2%-6%, TiO
20.01%-0.03%.
3. utilize the making method of the described a kind of environment friendly emulsion paint of claim 1, the making method step is:
(1), measures with the water of 10%-30%, the wetting agent of 0.1%-0.4%, the dispersion agent of 0.1%-0.6%, the fungicidal preservative of 0.1%-0.4%, the suds suppressor of 0.05%-0.15%, the white titanium pigment of 10%-40%, the water-ground limestone of 1%-10% high-speed stirring dispersion 10-30 minute by prescription;
(2), measure the water of 10%-30%, the skimmer of 0.1%-0.4%, the film coalescence aid of 1%-4%, the polyurethane associative thickener of 0.1%-0.3%, 20%～60% benzene emulsion, 1%～6% terepthaloyl moietie, the acrylic acid class thickening material of 1%-6% by prescription; Add interior mixing of material of step (1), process rubber-emulsion paint.
(3), by measuring, with processing environment friendly emulsion paint after rubber-emulsion paint and the even stirring of negative ion ore powder with the negative ion ore powder of 1%-6% and the rubber-emulsion paint of 94%-99%.