CN102702626A - 过氧化物硫化三元乙丙橡胶水管配方 - Google Patents

过氧化物硫化三元乙丙橡胶水管配方 Download PDF

Info

Publication number
CN102702626A
CN102702626A CN2012102155313A CN201210215531A CN102702626A CN 102702626 A CN102702626 A CN 102702626A CN 2012102155313 A CN2012102155313 A CN 2012102155313A CN 201210215531 A CN201210215531 A CN 201210215531A CN 102702626 A CN102702626 A CN 102702626A
Authority
CN
China
Prior art keywords
parts
formula
epdm
water pipe
diene monomer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102155313A
Other languages
English (en)
Other versions
CN102702626B (zh
Inventor
贾炳顺
贾恩馨
李继兰
赵金明
贾斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN BINHAI NEW DISTRICT DAGANG TIANLI RUBBER HOSE CO Ltd
Original Assignee
TIANJIN BINHAI NEW DISTRICT DAGANG TIANLI RUBBER HOSE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN BINHAI NEW DISTRICT DAGANG TIANLI RUBBER HOSE CO Ltd filed Critical TIANJIN BINHAI NEW DISTRICT DAGANG TIANLI RUBBER HOSE CO Ltd
Priority to CN2012102155313A priority Critical patent/CN102702626B/zh
Publication of CN102702626A publication Critical patent/CN102702626A/zh
Application granted granted Critical
Publication of CN102702626B publication Critical patent/CN102702626B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种过氧化物硫化三元乙丙橡胶水管配方，按重量份包括：三元乙丙橡胶100份；氧化锌4.5～10.5份；防老剂RD 1～6.5份；防老剂MB 0.8～3.6份；防老剂NBC 0.2～3.3份；交联剂TAIC 0.5～8份；交联剂DCP 1.8～5.2份；煅烧陶土15～40份；快压出炭黑N55080～150份；石蜡油51～76份。还包括有硬脂酸：0.5～6.5份。本发明大大提高了产品的耐高温性、耐臭氧性、耐冷却液及耐油性，产品的使用寿命会大大延长，完全可以满足汽车厂的要求，达到国家标准要求。

Description

过氧化物硫化三元乙丙橡胶水管配方
技术领域
本发明涉及一种橡胶水管。特别是涉及一种用于汽车的过氧化物硫化三元乙丙橡胶水管配方。
背景技术
汽车胶管是指用于底盘、发动机和车身三大部分，分输油、输气、驱动、控制、刹车、散热器和冷暖七个系统的胶管制品，主要起输油、输水和传递动力的作用。其中，散热器胶管是主要产品之一。汽车散热器胶管是三元乙丙橡胶的主要用途之一。随着汽车工业的发展，作为汽车重要配件之一的散热器胶管，对其要求越来越高、越来越苛刻，过去使用的三元乙丙橡胶散热器胶管采用的是硫磺硫化体系已不能满足汽车散热器胶管的低压缩变形、耐高温、耐冷却液的要求，因此过氧化物硫化散热器胶管应运而生。
发明内容
本发明所要解决的技术问题是，提供一种能够提高产品的耐高温性、耐臭氧性、耐冷却液及耐油性的过氧化物硫化三元乙丙橡胶水管配方。
本发明所采用的技术方案是：一种过氧化物硫化三元乙丙橡胶水管配方，按重量份包括：
三元乙丙橡胶   100份；
氧化锌         4.5～10.5份；
防老剂RD       1～6.5份；
防老剂MB       0.8～3.6份；
防老剂NBC      0.2～3.3份；
交联剂TAIC     0.5～8份；
交联剂DCP      1.8～5.2份；
煅烧陶土       15～40份；
快压出炭黑N550 80～150份；
石蜡油         51～76份。
还包括有硬脂酸：0.5～6.5份。
本发明的过氧化物硫化三元乙丙橡胶水管配方，大大提高了产品的耐高温性、耐臭氧性、耐冷却液及耐油性，产品的使用寿命会大大延长，完全可以满足汽车厂的要求，达到国家标准要求。
具体实施方式
下面结合实施例对本发明的过氧化物硫化三元乙丙橡胶水管配方做出详细说明。
本发明的过氧化物硫化三元乙丙橡胶水管配方，按重量份包括：
三元乙丙橡胶     100份；
氧化锌           4.5～10.5份；
防老剂RD         1～6.5份；
防老剂MB         0.8～3.6份；
防老剂NBC        0.2～3.3份；
交联剂TAIC       0.5～8份；
交联剂DCP        1.8～5.2份；
煅烧陶土         15～40份；
快压出炭黑N550   80～150份；
石蜡油           51～76份。
硬脂酸在硫化体系中起缓冲作用，同时也能减少混炼时的粘辊现象，有助于炭黑分散，也为了在制作的过程中保证挤出加工的顺畅，在上述的配方中还可加入有硬脂酸：0.5～6.5份。
上述的：
1、交联剂TAIC：三烯基甲基三异氰脲酸脂
2、交联剂DCP：过氧化二异丙苯
3、防老剂MB：2-巯基苯并咪唑
4、防老剂RD：2，2，4-三甲基-1，2-二氢化喹啉聚合体
5、防老剂NBC：N,N-二丁基二硫代氨基甲酸镍
下面给出按照上述配方用量的过氧化物硫化三元乙丙橡胶水管配方的三个实例：
实例1：
  序号   名称 重量(g)
  1   三元乙丙橡胶   100
  2   氧化锌   4.5
  3   硬脂酸   3
  4   防老剂RD   3.5
  5   防老剂MB   0.8
  6   防老剂NBC   0.1
  7   交联剂TAIC   3
  8   交联剂DCP   2.8
  9   煅烧陶土   35
  10   快压出炭黑N550   80
  11   石蜡油   60
实例2：
  序号   名称  重量(g)
  1   三元乙丙橡胶   100
  2   氧化锌   8
  3   硬脂酸   3
  4   防老剂RD   2
  5   防老剂MB   1.9
  6   防老剂NBC   1
  7   交联剂TAIC   0.5
  8   交联剂DCP   4.3
  9   煅烧陶土   28
  10   快压出炭黑N550   110
  11   石蜡油   62
实例3
  序号   名称  重量(g)
  1   三元乙丙橡胶   100
  2   氧化锌   4.5
  3   硬脂酸   3
  4   防老剂RD   1
  5   防老剂MB   2.2
  6   防老剂NBC   1.5
  7   交联剂TAIC   3
  8   交联剂DCP   1.8
  9   煅烧陶土   20
  10   快压出炭黑N550   130
  11   石蜡油   65
过氧化物硫化体系与现有的硫磺硫化体系性能对比如下：
Figure BDA00001818282200041
由上表的数据可以得出，过氧化物硫化橡胶与硫磺硫化橡胶相比，不仅耐高温老化性能优异，而且耐冷却液性能、耐油、压缩变形性能也非常好，可以更好地满足目前汽车用散热器水管的要求。

Claims (2)

1.一种过氧化物硫化三元乙丙橡胶水管配方，其特征在于，按重量份包括：
三元乙丙橡胶     100份；
氧化锌           4.5～10.5份；
防老剂RD         1～6.5份；
防老剂MB         0.8～3.6份；
防老剂NBC        0.2～3.3份；
交联剂TAIC       0.5～8份；
交联剂DCP        1.8～5.2份；
煅烧陶土         15～40份；
快压出炭黑N550   80～150份；
石蜡油           51～76份。
2.根据权利要求1所述的过氧化物硫化三元乙丙橡胶水管配方，其特征在于，还包括有硬脂酸：0.5～6.5份。
CN2012102155313A 2012-06-27 2012-06-27 过氧化物硫化三元乙丙橡胶水管组合物 Active CN102702626B (zh)