CN102702474A - 亲水性聚氨酯泡沫 - Google Patents
亲水性聚氨酯泡沫 Download PDFInfo
- Publication number
- CN102702474A CN102702474A CN2012102175514A CN201210217551A CN102702474A CN 102702474 A CN102702474 A CN 102702474A CN 2012102175514 A CN2012102175514 A CN 2012102175514A CN 201210217551 A CN201210217551 A CN 201210217551A CN 102702474 A CN102702474 A CN 102702474A
- Authority
- CN
- China
- Prior art keywords
- hydrophilic
- polyurethane foam
- parts
- polyether
- hydrophilic polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种聚氨酯泡沫，具体涉及一种亲水性聚氨酯泡沫。所述的亲水性泡沫聚氨酯，由如下质量份数的原料制成：亲水聚醚A 50~75；聚醚多元醇B 25~50；TDI 36.5~42；二乙醇胺0.5~1.5；聚氨酯催化剂A-33 0.12~0.3；硅油0.5~1.5；水3；所述的亲水聚醚A为亲水聚醚DEP-28；所述的聚醚多元醇B为聚醚多元醇DEP-3600H。本发明采用亲水性聚醚制作亲水性聚氨酯泡沫，具有制备简单、使用效果好、保湿性强的特点。
Description
技术领域
本发明涉及一种亲水性聚氨酯泡沫，具体涉及一种亲水性聚氨酯泡沫。
背景技术
随着科技的发展，高分子材料已渗透到人们生活的各个领域，并成为人们生活中不可缺少的材料。亲水性高分子材料因其具有优异的吸水、保水功能而被广泛应用于农业、园林、化工、医疗卫生等领域。高分子亲水材料主要是通过主链或侧链上的亲水基团，如羟基、酰胺基、羧基、磺酸基等与水分子相互作用而吸水。主要类型有聚丙烯酸酯类、聚乙烯醇类、醋酸乙烯共聚物类、聚氧化乙烯类、淀粉接枝共聚物类、聚氨酯类等。
通过在聚氨酯分子链中引入亲水基团如氧化乙烯链节，来提高聚氨酯的吸水性。由于氧化乙烯链节不像氧化丙烯链节有疏水基团-CH3，使得聚氨酯分子链的空间位阻大大减小，因此更利于醚氧键-O-的弯曲聚集，以及与水形成氢键；水的进入也使聚氨酯具有溶胀作用，提高了分子链的运动能力，有利于水分子的进入和扩散，从而使含有氧化乙烯链节的聚氨酯具有亲水性。因此，目前一般多采用聚乙二醇或富含氧化乙烯的多元醇为原料来制备亲水性聚氨酯泡沫。
发明内容
本发明的目的是提供一种亲水性聚氨酯泡沫，具有制备简单、使用效果好、保湿性强的特点。
本发明所述的亲水性聚氨酯泡沫，由如下质量份数的原料制成：
其中：
所述的亲水聚醚A为亲水聚醚DEP-28，优选德信联邦化学工业有限公司的产品。
所述的聚醚多元醇B为聚醚多元醇DEP-3600H，优选德信联邦化学工业有限公司的产品。
所述的聚氨酯催化剂A-33，为美国气体A-33。
所述的TDI为甲苯二异氰酸酯，优选亨斯曼TDI-80。
所述的硅油优选迈图L-580。
本发明的有益效果如下：
本发明采用亲水性聚醚制作亲水性聚氨酯泡沫，具有制备简单、使用效果好、保湿性强的特点。
具体实施方式
以下结合实施例对本发明做进一步描述。
实施例中：
所述的亲水聚醚A为德信联邦化学工业有限公司的亲水聚醚DEP-28。
所述的聚醚多元醇B为德信联邦化学工业有限公司的聚醚多元醇DEP-3600H。
所述的TDI为亨斯曼TDI-80。
所述的硅油为迈图L-580。
实施例1
本发明所述的亲水性聚氨酯泡沫，由如下质量份数的原料制成：
制得的泡沫密度30，断裂伸长率为150%。
实施例2
本发明所述的亲水性聚氨酯泡沫，由如下质量份数的原料制成：
制得的泡沫密度32，断裂伸长率为149%。
实施例3
本发明所述的亲水性聚氨酯泡沫，由如下质量份数的原料制成：
制得的泡沫密度31，断裂伸长率为152%。
实施例4
本发明所述的亲水性聚氨酯泡沫，由如下质量份数的原料制成：
制得的泡沫密度33，断裂伸长率为155%。
Claims (1)
1.一种亲水性聚氨酯泡沫，其特征在于由如下重量份数的原料制成：
所述的亲水聚醚A为亲水聚醚DEP-28；
所述的聚醚多元醇B为聚醚多元醇DEP-3600H。