CN102644198A - 环保可再生超轻型喷绘灯箱布 - Google Patents
环保可再生超轻型喷绘灯箱布 Download PDFInfo
- Publication number
- CN102644198A CN102644198A CN2012101519115A CN201210151911A CN102644198A CN 102644198 A CN102644198 A CN 102644198A CN 2012101519115 A CN2012101519115 A CN 2012101519115A CN 201210151911 A CN201210151911 A CN 201210151911A CN 102644198 A CN102644198 A CN 102644198A
- Authority
- CN
- China
- Prior art keywords
- cloth
- lamp box
- polyvinyl
- renewable
- microlight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及环保可再生超轻型喷绘灯箱布,由聚乙烯编织布1与其正面的聚乙烯淋膜层2组成的聚乙烯基布、聚乙烯基布正面上的底涂剂层3和分布在底涂剂层3上的吸墨涂层4组成。制备方法为:①采用聚乙烯塑料粒,经拉丝、织布和淋聚乙烯,得聚乙烯基布;②在基布正面涂底涂剂,烘干后涂吸墨涂层;③经分切、复卷及检验得成品。其中吸墨涂层由纯丙乳液、聚氯乙烯乳液、碳酸钙、抑泡消泡剂、硅胶、钛白粉、润湿剂、增白剂、正丁醇、氯化钠与若干氨水按一定重量比配成。本发明提供的环保可再生超轻型喷绘灯箱布,其编织布用聚乙烯制得,且涂层选用纯丙乳液与聚氯乙烯乳液的环保涂料,因此具有质地轻、环保可再生等优势。
Description
技术领域
本发明涉及灯箱布,具体涉及一种环保可再生超轻型喷绘灯箱布。
背景技术
随着商品的日益丰富以及广告装饰业的迅猛发展,喷绘广告灯箱布在广告装饰业中的使用量已越来越大。传统的喷绘灯箱布主要采用两层聚氯乙烯和一层高强度的涤沦网布经三层复合机复合而成。因其中间夹有涤沦网布,而限制了其再生回收,且质量较重,所以急需一种环保可再生超轻型灯箱布来代之。
灯箱布按生产工艺可分为刀刮法灯箱布、压延法灯箱布和贴合法灯箱布。刀刮法灯箱布工艺是将液态聚氯乙烯浆料用若干反刮刀均匀的乔涂于基布的正反两面,然后通过烘干工艺使其完全结合成一个整体,之后冷却成形。其特点是防渗透性、抗拉力、抗剥离能力较强。压延法是将聚氯乙烯粉与液态增塑剂等多种原材料充分搅拌,后经高温热辊的压力作用,与基布粘合成一个整体。其特点是表面平整度较好,且透光均匀,在内打光灯布上较有优势,但受以设备的限制,幅宽一般不超过3米。贴合法灯箱布是将上下两层成型聚氯乙烯膜,通过加热,在热辊的压力下与中间的导光纤维网贴合在一起,冷却成形,此种工艺最大的特点是具备优良喷绘吸墨性和较强的色彩表现力。
发明内容
本发明的目的是提供一种环保可再生、质量轻、打印效果好的喷绘灯箱布。
本发明的目的是通过如下措施来达到的:步骤如下:①采用高密度聚乙烯塑料粒,经塑料扁丝拉丝机组拉丝、喷水织机织布和淋膜机淋低密度聚乙烯,即得聚乙烯基布;②将聚乙烯基布的淋膜层上涂上底涂剂,经烘箱烘干后涂吸墨涂层;③经分切、复卷及检验得成品。
按上述方案,环保可再生超轻型喷绘灯箱布,其特征在于步骤①中所织得塑料编织布重量<100g/m2。
按上述方案,环保可再生超轻型喷绘灯箱布,其特征在于步骤②中所述底涂剂为聚氨酯胶。
按上述方案,环保可再生超轻型喷绘灯箱布,其特征在于步骤②中吸墨涂层由70%纯丙乳液、15%聚氯乙烯乳液、10%碳酸钙、2%抑泡消泡剂、1.5%硅胶、0.9%钛白粉、0.2%润湿剂、0.2%增白剂、0.1%正丁醇、0.1%氯化钠及若干氨水按重量比配成。
按上述方案,环保可再生超轻型喷绘灯箱布,其特征在于步骤②中吸墨涂层为环保涂料,其制备方法为在聚氯乙烯乳液中加入抑泡消泡剂,搅拌10min后加硅胶,分散30min后加氨水调PH值至6-7;加纯丙乳液,搅拌10min后依次加碳酸钙、钛白粉、润湿剂;再次搅拌40min后加增白剂、正丁醇与氯化钠,搅拌10min后过滤即得。
按上述方案,环保可再生超轻型喷绘灯箱布,其特征在于抑泡消泡剂为A08(20%)。
按上述方案,环保可再生超轻型喷绘灯箱布,其特征在于硅胶为SD-640。
按上述方案,环保可再生超轻型喷绘灯箱布,其特征在于润湿剂为TN-21(4%)。
环保可再生超轻型喷绘灯箱布,其技术指标为:①能兼容溶剂型、弱溶剂型、UV固化型墨水打印;②打印分辨率高,能达到1440dpi;③打印色密度高,色彩还原好;④吸墨干燥时间为6min,干燥快;⑤灯箱布质地轻,质量<140g/m2;⑥涂层附着牢度>12N/25mm;⑦拉伸负荷:经向>400N,纬向>500N;⑧撕裂负荷:经向>250N,纬向>300N。
环保可再生超轻型喷绘灯箱布,具有以下特点:①中间层采用聚乙烯材料做成的编织布,而非涤沦网布,环保且可回收再利用;②基布正面先淋低密度聚乙烯膜,再涂底涂剂与吸墨涂层,提高涂层平整度;③吸墨涂层选用纯丙乳液与聚氯乙烯乳液的环保涂料,避免造成环境污染;④灯箱布质量<140g/m2,相比于传统灯箱布的400~600g/m2,其质地更轻;⑤强度高、耐低温,适于用作为户外灯箱布;⑥与传统的喷绘灯箱布相比,具有同等的喷墨打印性能。
具体实施方式
下面结合附图对本发明较优实施例进行详细介绍,但是实施例不会构成对本发明的限制。
参见附图1,环保可再生超轻型喷绘灯箱布,包括聚乙烯编织布1与聚乙烯编织布正面的聚乙烯淋膜层2组成的聚乙烯基布、基布正面上的底涂剂层3和分布在底涂剂层3上的吸墨涂层4。
实施例1
⑴采用高密度聚乙烯塑料粒,通过塑料扁丝拉丝机组拉丝与喷水织机织布,即得基布;
⑵在淋膜机上将基布正面淋上一层0.025mm厚的低密度聚乙烯,即得聚乙烯基布;
⑶制备吸墨涂层:在7.5Kg聚氯乙烯乳液中加入1.25Kg A08,搅拌10min后加0.75 Kg SD-640,分散30min后加氨水调PH值至6-7,加37.5Kg纯丙乳液,搅拌10min后依次加5Kg碳酸钙、0.5Kg钛白粉、0.1Kg润湿剂,再次搅拌40min后加0.1Kg TN-21、0.05Kg正丁醇与0.05Kg氯化钠,搅拌10min后过滤即得;
⑷选用印刷凹版涂布,将聚乙烯基布的正面涂上底涂剂聚氯酯胶,经烘箱烘干后涂吸墨涂层;
⑸经分切、复卷及检验得成品。
Claims (8)
1.环保可再生超轻型喷绘灯箱布,其特征在于制备方法包括以下几个步骤:①采用高密度聚乙烯塑料粒,经塑料扁丝拉丝机组拉丝、喷水织机织布和淋膜机淋低密度聚乙烯,得聚乙烯基布;②将聚乙烯基布的正面涂上底涂剂,经烘箱烘干后涂吸墨涂层;③经分切、复卷及检验得成品。
2.如权利要求1所述的环保可再生超轻型喷绘灯箱布,其特征在于步骤①中所述的塑料编织布重量<100g/m2。
3.如权利要求1所述的环保可再生超轻型喷绘灯箱布,其特征在于步骤②中所述的底涂剂为聚氨酯胶。
4.如权利要求1所述的环保可再生超轻型喷绘灯箱布,其特征在于步骤②中所述的吸墨涂层由70%纯丙乳液、15%聚氯乙烯乳液、10%碳酸钙、2%抑泡消泡剂、1.5%硅胶、0.9%钛白粉、0.2%润湿剂、0.2%增白剂、0.1%正丁醇、0.1%氯化钠及若干氨水按重量比配成。
5.如权利要求1和4所述的环保可再生超轻型喷绘灯箱布,其特征在于所述的吸墨涂层的制备方法为在聚氯乙烯乳液中加入抑泡消泡剂,搅拌10min后加硅胶,分散30min后加氨水调PH值至6-7;加纯丙乳液,搅拌10min后依次加碳酸钙、钛白粉、润湿剂;再次搅拌40min后加增白剂、正丁醇与氯化钠,搅拌10min后过滤即得。
6.如权利要求1和4所述环保可再生超轻型喷绘灯箱布,其特征在于所述的抑泡消泡剂为A08(20%)。
7.如权利要求1和4所述环保可再生超轻型喷绘灯箱布,其特征在于所述的硅胶为SD-640。
8.如权利要求1和4所述环保可再生超轻型喷绘灯箱布,其特征在于所述的润湿剂为TN-21(4%)。