CN102634114A - 一种用于负离子和银离子杀菌太阳能纳米内胆组合物及其加工工艺 - Google Patents
一种用于负离子和银离子杀菌太阳能纳米内胆组合物及其加工工艺 Download PDFInfo
- Publication number
- CN102634114A CN102634114A CN2012101069325A CN201210106932A CN102634114A CN 102634114 A CN102634114 A CN 102634114A CN 2012101069325 A CN2012101069325 A CN 2012101069325A CN 201210106932 A CN201210106932 A CN 201210106932A CN 102634114 A CN102634114 A CN 102634114A
- Authority
- CN
- China
- Prior art keywords
- silver
- parts
- sterilization
- inner bag
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种负离子和银离子杀菌太阳能纳米聚丙烯内胆的配方，包括以下重量份的物质：活性炭5～8份；负离子材料5～8份；偶联剂2.5～6份；硝酸银溶液3～8份；载体树脂70～85份。制备方法：将硝酸银溶液浸渍在活性炭和六环石中，采用恒温振荡法制备，经过干燥，煅烧制得渗银活性炭和渗银六环石，再制成纳米级细粉体，然后加入载体树脂、偶联剂、分散剂，进行高速捏合，经双螺杆挤出，制成太阳能纳米聚丙烯内胆。本发明专利采用活性炭和六环石相结合的吸附方式，同时六环石可以释放负离子和远红外线，负离子和银离子共同作用，起到双重杀菌的功效。
Description
技术领域
本发明涉及一种纳米材料，具体涉及一种用于负离子和银离子杀菌太阳能纳米内胆组合物及其加工工艺。
背景技术
随着太阳能行业的逐渐发展壮大，太阳能的用水量也占据人们生活的重要部分，如洗澡生活用水的品质也越来越受到重视。而我国广大农村水质环境与城市差距很大，由于农村用水多为打井取水，普通浅井一般只能取到浅层地下水，且未经过净化处理，含泥沙、腐蚀性氟氯离子较多，据国家环境监测总站发布的监测报告显示：目前全国有3.2亿人用水不安全，这其中有2.6亿人的用水属高氟氯水。
90年代以来，银杀菌材料的研究与开发受到极大重视。杀菌材料中的Ag一般以Ag+吸附细菌。当Ag+微生物细菌接触时，能强烈吸附细菌。细菌赖之起呼吸作用的酶被Ag+催化转变成失去其呼吸作用的微生物，细菌机体结构被破坏，导致其迅速死亡。Ag+杀菌活性相当强，消耗量极少，一般用量为ppm级即可灭菌，对人体无影响。实验表明人体组织Ag＜0.01mg％，多余银可通过消化道很快排除，不会引起人体器官和组织损伤。
Ag+对光不稳定，因此需要用活性炭为载体制备对抗菌活性成分具有缓释作用的无机抗菌剂。但是作为载体的活性炭本身不具有杀菌功能，从而使现有的无机抗菌剂的杀菌能力有限。
发明内容
本发明实施例的目的是针对上述现有技术的缺陷，提供了一种负离子和银离子一同作用，起到双重杀菌功效，杀菌能力更强的负离子和银离子杀菌太阳能纳米内胆及其加工工艺。
为了实现上述目的本发明采取的技术方案是：一种用于负离子和银离子杀菌太阳能纳米聚丙烯内胆组合物，包括以下重量份的物质：
无机吸附材料5～8份；负离子材料5～8份；载体树脂70～85份；偶联剂2.5～6份；硝酸银溶液3～8份；分散剂1～3份。
所述负离子材料为六环石、电气石、蛋白石或竹炭粉。
所述的无机吸附材料是活性炭、沸石或硅胶。
所述载体树脂为纳米聚丙烯母粒、聚对苯二甲酸乙二醇酯、聚乙烯、聚甲基丙烯酸甲酯、聚氯乙烯、聚偏二氯乙烯、聚碳酸酯、聚酰胺、环氧树脂、聚氨酯、氯化聚乙烯、丙烯腈-丁二烯-苯乙烯共聚物、苯乙烯-丁二烯嵌段共聚物。
所述偶联剂为钛酸酯偶联剂或硅酸酯偶联剂。
所述分散剂为聚乙烯醇或硬脂酸。
本发明还提供一种负离子和银离子杀菌太阳能纳米聚丙烯内胆的加工工艺，包括以下步骤：
将硝酸银溶液浸渍在活性炭和六环石中，采用恒温振荡法制备，经过干燥，煅烧后制得渗银活性炭和渗银六环石，然后制成纳米级细粉体，再加入载体树脂、偶联剂、分散剂，进行高速捏合，经双螺杆挤出，采用中空吹塑方法，挤出物经水槽冷却，空气冷却后制成太阳能纳米聚丙烯内胆。
本发明更优选的技术方案是：一种负离子和银离子杀菌太阳能纳米聚丙烯内胆的加工工艺，包括以下步骤：
将活性炭和六环石放入0.6％-1％的硝酸银溶液中浸间1-1.5小时，经过95℃-105℃干燥2.5-3.5小时，在210℃-230℃煅烧1.5-2.5小时，后制得渗银活性炭和渗银六环石，将渗银活性炭和渗银六环石经过粗磨制成微米级的颗粒，将制成的微米级的颗粒放入纳米颗粒砂磨机中，通过纳米颗粒砂磨机研磨后制成纳米级细粉体，纳米级细粉体经干燥后与载体树脂、偶联剂和分散剂一起在转速460r/min的条件下进行捏合15～20min，最后经双螺杆挤出，采用中空吹塑方法，挤出物经水槽冷却，空气冷却后制成太阳能纳米聚丙烯内胆。
所述纳米级细粉体采用喷雾干燥机进行干燥，喷雾干燥机的进风温度：200-260℃，出风温度：70-90℃，干燥时间：10-20s。
活性炭具有极强的吸附能力，且由于活性炭表面的疏水性和巨大的比表面积，活性炭载银后不仅可以有效地吸附自来水中有机物和部分无机杂质，活性炭上如果吸附银离子不仅去除速度快，而且去除效率大大提高。银离子的杀菌机理与银离子能强烈地吸附微生物细菌有关，微生物细菌被银离子吸附后，赖之起呼吸作用的酶就失去功效，细菌机体结构被毁坏，微生物细菌迅速死亡。银离子表现出较强的氧化能力，破坏细菌细胞的代谢作用，阻止了微生物的繁殖。另外，可以强烈的吸引细菌体内蛋白酶的巯基，并迅速结合，使细菌的基因酶丧失活性，致使细菌死亡。当菌体被杀后，Ag+又游离出来，与其它菌体作用，实行新一轮的杀灭，直到细菌全部杀死为止。
负离子的主要功能有：①恒久的负离子发射功能，调节周围环境的空气质量；②较强的生物波发射功能，促进血液循环，激活人体免疫细胞，防止人体老化和早衰；③持久的抗菌、杀菌性能，能杀灭对人体有害的细菌，又不伤害人体；④优良的除臭性能，脱除异味，保持良好的生活空间；⑤可释放人体需要的多种微量元素，有益于人体健康；⑥优越的界面活性作用，可以节约洗涤剂的用量，而且有助于环境的净化。
本发明实施例的有益效果是：与现有的技术相比，本发明专利采用活性炭和六环石相结合的吸附方式，同时六环石可以释放负离子，负离子和银离子一同作用，起到双重杀菌的功效。本发明的纳米PP(聚丙烯)内胆在不结水垢和防腐蚀的基础上增加了双重杀菌消毒的作用。六环石释放远红外线，远红外线释放的能量被物体吸收的辐射能传递给物体内的原子、分子等粒子，使这些粒子发生不规则运动，引起物体的升温作用，称为远红外线的一次效应，也称为增温效应。红外线对人体皮肤、皮下组织具有强烈的穿透力。外界红外线辐射人体产生的一次效应可以使皮肤和皮下组织的温度相应增高，促进血液的循环和新陈代谢，促进人的健康。
具体实施方式
下面结合具体实施例对本发明作进一步说明，但不作为对本发明的限定。
实施例1
按照下列重量称取原料(千克)：
活性炭60；六环石70；钛酸酯偶联剂45；硝酸银溶液50；纳米聚丙烯母粒800；
纳米聚丙烯母粒的型号优选：NH01，其生产厂家为余姚双象纳米塑业有限责任公司。
一种负离子和银离子杀菌太阳能纳米聚丙烯内胆的加工工艺：
将60千克活性炭和70千克六环石放入50千克、浓度为0.6％的硝酸银溶液中浸间1小时，经过100℃干燥3小时，在220℃煅烧2小时，后制得渗银活性炭和渗银六环石，将渗银活性炭和渗银六环石经过粗磨制成微米级的颗粒后，将制成的微米级的颗粒放入纳米颗粒砂磨机中，通过纳米颗粒砂磨机研磨后制成纳米级细粉体，纳米级细粉体采用喷雾干燥机进行干燥，纳米级细粉体干燥工艺：进风温度：240℃，出风温度：80℃，干燥时间：15s；干燥后的纳米级细粉体与800千克纳米聚丙烯母粒、45千克钛酸酯偶联剂、20千克聚乙烯醇一起在转速460r/min的条件下进行捏合20min，最后经双螺杆挤出，制成太阳能纳米聚丙烯内胆。
实施例2
按照下列重量称取原料(千克)：
活性炭50；六环石80份；钛酸酯偶联剂25；硝酸银溶液80；纳米聚丙烯母粒850；硬脂酸30。
一种负离子和银离子杀菌太阳能纳米聚丙烯内胆的加工工艺：
将50千克活性炭和80千克六环石放入80千克、质量百分比浓度为1％的硝酸银溶液中浸间1.5小时，经过95-105℃干燥3.5小时，在230℃煅烧1.5小时，后制得渗银活性炭和渗银六环石，将渗银活性炭和渗银六环石经过粗磨制成微米级的颗粒后，将制成的微米级的颗粒放入纳米颗粒砂磨机中，通过纳米颗粒砂磨机研磨后制成纳米级细粉体，纳米级细粉体采用喷雾干燥机进行干燥，纳米级细粉体干燥工艺：进风温度：260℃，出风温度：70℃，干燥时间：10s；干燥后的纳米级细粉体与850千克纳米聚丙烯母粒、25千克钛酸酯偶联剂和30千克硬脂酸一起在转速460r/min的条件想进行捏合15min，最后经双螺杆挤出，制成太阳能纳米聚丙烯内胆。
实施例3
按照下列重量称取原料(千克)：
活性炭80；六环石50；硅酸酯偶联剂60；硝酸银溶液30；纳米聚丙烯母粒700；聚乙烯醇10。
一种负离子和银离子杀菌太阳能纳米聚丙烯内胆的加工工艺：
将80千克活性炭和50千克六环石放入30千克、质量百分比浓度为0.8％的硝酸银溶液中浸间1小时，经过105℃干燥2.5小时，在210℃煅烧2.5小时，后制得渗银活性炭和渗银六环石，将渗银活性炭和渗银六环石经过粗磨制成微米级的颗粒后，将制成的微米级的颗粒放入纳米颗粒砂磨机中，通过纳米颗粒砂磨机研磨后制成纳米级细粉体，纳米级细粉体采用喷雾干燥机进行干燥，纳米级细粉体干燥工艺：进风温度：200℃，出风温度：90℃，干燥时间：20s；干燥后的纳米级细粉体与700千克纳米聚丙烯母粒、60千克硅酸酯偶联剂和10千克聚乙烯醇一起在转速460r/min的条件下进行捏合20min，最后经双螺杆挤出，制成太阳能纳米聚丙烯内胆。
实施例4
按照下列重量称取原料(千克)：
沸石70，蛋白石60；钛酸酯偶联剂45；硝酸银溶液50；聚丙烯750；聚乙烯醇15。
无机吸附材料5～8份；负离子材料5～8份；载体树脂70～85份；偶联剂2.5～6份；硝酸银溶液3～8份；分散剂1～3份。
加工工艺如实施例1。
实施例5
按照下列重量称取原料(千克)：
硅胶70，电气石70；硅酸酯偶联剂25；硝酸银溶液75；聚氯乙烯750；硬脂酸25。
加工工艺如实施例1。
以上所述的实施例，只是本发明较优选的具体实施方式的一种，本领域的技术人员在本发明技术方案范围内进行的通常变化和替换都应包含在本发明的保护范围内。
Claims (9)
1.一种用于负离子和银离子杀菌太阳能纳米聚丙烯内胆组合物，包括以下重量份的物质：
无机吸附材料5～8份；负离子材料5～8份；载体树脂70～85份；偶联剂2.5～6份；硝酸银溶液3～8份；分散剂1～3份。
2.根据权利要求1所述的用于负离子和银离子杀菌太阳能纳米聚丙烯内胆组合物，其特征在于，所述负离子材料为六环石、电气石、蛋白石或竹炭粉。
3.根据权利要求1所述的负离子和银离子杀菌太阳能纳米聚丙烯内胆的配方，其特征在于，所述的无机吸附材料是活性炭、沸石或硅胶。
4.根据权利要求1所述的用于负离子和银离子杀菌太阳能纳米聚丙烯内胆组合物，其特征在于，所述载体树脂为纳米聚丙烯母粒、聚对苯二甲酸乙二醇酯、聚乙烯、聚甲基丙烯酸甲酯、聚氯乙烯、聚偏二氯乙烯、聚碳酸酯、聚酰胺、环氧树脂、聚氨酯、氯化聚乙烯、丙烯腈-丁二烯-苯乙烯共聚物、苯乙烯-丁二烯嵌段共聚物。
5.根据权利要求1所述的用于负离子和银离子杀菌太阳能纳米聚丙烯内胆组合物，其特征在于，所述偶联剂为钛酸酯偶联剂或硅酸酯偶联剂。
6.根据权利要求1所述的用于负离子和银离子杀菌太阳能纳米聚丙烯内胆组合物，其特征在于，所述分散剂为聚乙烯醇或硬脂酸。
7.一种权利要求1-6任一项所述的负离子和银离子杀菌太阳能纳米聚丙烯内胆的加工工艺，包括以下步骤：
将硝酸银溶液浸渍在活性炭和六环石中，采用恒温振荡法制备，经过干燥，煅烧后制得渗银活性炭和渗银六环石，然后制成纳米级细粉体，再加入载体树脂、偶联剂、分散剂，进行高速捏合，经双螺杆挤出，采用中空吹塑方法，挤出物经水槽冷却，空气冷却后制成太阳能纳米聚丙烯内胆。
8.根据权利要求7所述的加工工艺，其特征在于，包括以下步骤：
将活性炭和六环石放入0.6％-1％的硝酸银溶液中浸间1-1.5小时，经过95℃-105℃干燥2.5-3.5小时，在210℃-230℃煅烧1.5-2.5小时，后制得渗银活性炭和渗银六环石，将渗银活性炭和渗银六环石经过粗磨制成微米级的颗粒，将制成的微米级的颗粒放入纳米颗粒砂磨机中，通过纳米颗粒砂磨机研磨后制成纳米级细粉体，纳米级细粉体经干燥后与载体树脂、偶联剂和分散剂一起在转速460r/min的条件下进行捏合15～20min，最后经双螺杆挤出，采用中空吹塑方法，挤出物经水槽冷却，空气冷却后制成太阳能纳米聚丙烯内胆。
9.根据权利要求8所述的加工工艺，其特征在于，所述纳米级细粉体采用喷雾干燥机进行干燥，喷雾干燥机的进风温度：200-260℃，出风温度：70-90℃，干燥时间：10-20s。