CN102603997A - 一种连续化聚合物聚醚多元醇的生产方法 - Google Patents

一种连续化聚合物聚醚多元醇的生产方法 Download PDF

Info

Publication number
CN102603997A
CN102603997A CN2012100493368A CN201210049336A CN102603997A CN 102603997 A CN102603997 A CN 102603997A CN 2012100493368 A CN2012100493368 A CN 2012100493368A CN 201210049336 A CN201210049336 A CN 201210049336A CN 102603997 A CN102603997 A CN 102603997A
Authority
CN
China
Prior art keywords
polyether polyol
monomer
initiator
serialization
polymerization
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100493368A
Other languages
English (en)
Inventor
汤振英
刘荣
刘德春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANJING KUMHO GPRO CHEMICAL CO Ltd
Original Assignee
NANJING KUMHO GPRO CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANJING KUMHO GPRO CHEMICAL CO Ltd filed Critical NANJING KUMHO GPRO CHEMICAL CO Ltd
Priority to CN2012100493368A priority Critical patent/CN102603997A/zh
Publication of CN102603997A publication Critical patent/CN102603997A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种连续化聚合物聚醚多元醇的生产方法,将聚醚多元醇、聚合单体和引发剂混合后连续的加入到反应器中,在温度为100~130℃、压力为0.3~0.5MP条件下进行聚合反应,然后将聚合后的反应物通入真空脱单系统,脱除未反应的单体和引发剂产物,得到最终产物聚合物聚醚多元醇;其特征在于:所述引发剂为偶氮二异丁酸二甲酯。本发明采用新型引发剂AIBME进入连续化聚合物聚醚多元醇生产工艺,产出的产品稳定性好,单体含量低,反应过程稳定安全环保,产能大大提高。

Description

一种连续化聚合物聚醚多元醇的生产方法
技术领域
本发明涉及一种连续化聚合物聚醚多元醇的生产方法。
背景技术
随着技术的进步及聚合物聚醚多元醇(简称POP)产能的扩大,对于生产的要求也越来越高。聚合物的生产现在已经普遍采用连续化生产方式,这样生产的POP产品质量稳定,且产能大大提高。
传统的引发剂用于连续化POP得生产,由于在脱单过程中会产生剧毒的固体分解物,堵塞管道,从而造成POP单体含量高,且一定时间后必须进行清理管道,造成产能不能释放。
发明内容
发明目的:本发明的目的在于针对现有技术的不足,提供一种高产能的连续化聚合物聚醚多元醇的生产方法。
技术方案:本发明所述的连续化聚合物聚醚多元醇的生产方法,将聚醚多元醇、聚合单体和引发剂混合后连续的加入到反应器中,在温度为100~130℃、压力为0.3~0.5MP条件下进行聚合反应,然后将聚合后的反应物通入真空脱单系统,脱除未反应的单体和引发剂产物,得到最终产物聚合物聚醚多元醇;所述引发剂为偶氮二异丁酸二甲酯。
本发明采用的新型的引发剂偶氮二异丁酸二甲酯(AIBME),其分解物不结晶,不会堵塞管道,提高了产能,降低了POP中的单体含量。
比较优选地,所述引发剂的用量为聚醚多元醇和聚合单体混合物总重量的1~6%。
所述聚醚多元醇与所述聚合单体的重量比为55~80:45~20。
所述聚合单体为苯乙烯单体和丙烯腈单体。
有益效果:本发明采用新型引发剂AIBME进入连续化聚合物聚醚多元醇生产工艺,产出的产品稳定性好,单体含量低,反应过程稳定安全环保,产能大大提高。
具体实施方式
下面对本发明技术方案进行详细说明,但是本发明的保护范围不局限于所述实施例。
实施例1:本发明连续化聚合物聚醚多元醇的生产方法,将聚醚多元醇和聚合单体(苯乙烯单体和丙烯腈单体)按重量比为76:24混合好,再加入聚醚多元醇和聚合单体混合物总重量5%的新型引发剂AIBME,混合均匀后连续的加入到反应器中,反应器的温度保持100℃-130℃,压力在0.3 MP -0.5MP进行聚合反应,物料通过反应器上部的溢流口连续的进入真空系统,真空系统脱除未反应的单体及引发剂,从而得到合格的固含量为45%的聚合物聚醚多元醇。
本实施例聚合物聚醚多元醇(KGP524)合成过程中不同引发剂使用对于产品单体含量的比较:
引发剂 异丙醇/ppm 苯乙烯/ppm 丙烯腈/ppm 总单体/ppm
AIBN 1.66 129.46 18.9 150
AIBME 1.2 42.32 10.8 54.35
实施例2:本发明连续化聚合物聚醚多元醇的生产方法,将聚醚多元醇和聚合单体(苯乙烯单体和丙烯腈单体)按重量比为55:44混合好,再加入聚醚多元醇和聚合单体混合物总重量1%的新型引发剂AIBME,混合均匀后连续的加入到反应器中,反应器的温度保持100℃-130℃,压力在0.3 MP -0.5MP进行聚合反应,物料通过反应器上部的溢流口连续的进入真空系统,真空系统脱除未反应的单体及引发剂,从而得到合格的固含量为40%的聚合物聚醚多元醇。
如上所述,尽管参照特定的优选实施例已经表示和表述了本发明,但其不得解释为对本发明自身的限制。在不脱离所附权利要求定义的本发明的精神和范围前提下,可对其在形式上和细节上作出各种变化。

Claims (4)

1.一种连续化聚合物聚醚多元醇的生产方法,将聚醚多元醇、聚合单体和引发剂混合后连续的加入到反应器中,在温度为100~130℃、压力为0.3~0.5MP条件下进行聚合反应,然后将聚合后的反应物通入真空脱单系统,脱除未反应的单体和引发剂产物,得到最终产物聚合物聚醚多元醇;其特征在于:所述引发剂为偶氮二异丁酸二甲酯。
2.根据权利要求1所述的连续化聚合物聚醚多元醇的生产方法,其特征在于:所述引发剂的用量为聚醚多元醇和聚合单体混合物总重量的1~6%。
3.根据权利要求1所述的连续化聚合物聚醚多元醇的生产方法,其特征在于:所述聚醚多元醇与所述聚合单体的重量比为55~80:45~20。
4.根据权利要求1所述的连续化聚合物聚醚多元醇的生产方法,其特征在于:所述聚合单体为苯乙烯单体和丙烯腈单体。
CN2012100493368A 2012-02-29 2012-02-29 一种连续化聚合物聚醚多元醇的生产方法 Pending CN102603997A (zh)