CN102585456A - 一种聚酯用无卤阻燃剂组合物及其应用方法 - Google Patents

一种聚酯用无卤阻燃剂组合物及其应用方法 Download PDF

Info

Publication number
CN102585456A
CN102585456A CN2012100116329A CN201210011632A CN102585456A CN 102585456 A CN102585456 A CN 102585456A CN 2012100116329 A CN2012100116329 A CN 2012100116329A CN 201210011632 A CN201210011632 A CN 201210011632A CN 102585456 A CN102585456 A CN 102585456A
Authority
CN
China
Prior art keywords
pdptp
flame retardant
mpp
mca
polyester
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012100116329A
Other languages
English (en)
Other versions
CN102585456B (zh
Inventor
王彦林
张艳丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beisel Ze F (beijing) Acoustic Technology Co Ltd
Original Assignee
Suzhou University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou University of Science and Technology filed Critical Suzhou University of Science and Technology
Priority to CN201210011632.9A priority Critical patent/CN102585456B/zh
Publication of CN102585456A publication Critical patent/CN102585456A/zh
Application granted granted Critical
Publication of CN102585456B publication Critical patent/CN102585456B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种聚酯用无卤阻燃剂组合物及其应用方法。该阻燃剂由三聚氰胺氰尿酸盐(简称MCA)、三聚氰胺聚磷酸盐(简称MPP)、二乙基次膦酸铝(1240)中的任意一种与PDPTP按任意的重量比复配制得。本发明的阻燃剂，具有多元素协同增效、与材料相容性好、阻燃性能高及环保等优点。

Description

一种聚酯用无卤阻燃剂组合物及其应用方法
技术领域
本发明涉及一种聚酯用无卤阻燃剂组合物及其应用方法，特别涉及一种聚酯PET和PBT用无卤阻燃剂组合物及其应用方法。
背景技术
广义的有机磷阻燃剂以磷酸酯居多，并多为液体，具有耐热性较差、挥发性大、发烟量大、与聚合物相容性差等缺点。因此急需开发具有热稳定性好、分子量大、与材料相容性好、含磷量高、低烟、无毒等优点的具有C-P键的有机膦阻燃剂，并且由于多元素协同型有机膦阻燃剂优点更多，能赋予材料更好的加工性能，因而设计分子内多元素协同或通过复配实现多元素协同已成为当前阻燃剂技术研究的热点课题。特别是用于聚酯PET和PBT的性价比高的无卤有机膦阻燃剂急待开发。
发明者研究出了一种聚酯用无卤阻燃剂组合物，该阻燃剂组合物结构中含有C-P键，同时又引入了阻燃元素硫、氮或铝，协同阻燃效果好，稳定性高，适应于高温加工，多芳性环结构与高分子材料具有很好的相容性，不降低材料的机械强度。同时该阻燃剂组合物制取方法简单，可以降低成本，具有很好的应用前景。
发明内容
本发明的目的之一在于提供一种聚酯用无卤阻燃剂组合物。该阻燃剂协同阻燃效能高，无卤，能满足环保要求，有很好的应用开发前景。
本发明的另一目的在于提供一种上述阻燃剂组合物在聚酯PET和PBT中的应用方法。
本发明的目的是通过以下技术方案实现的：
一种新型聚酯用无卤阻燃剂组合物，它是由三聚氰胺氰尿酸盐(简称MCA)、三聚氰胺聚磷酸盐(简称MPP)、二乙基次膦酸铝(1240)中的任意一种与聚苯基硫代膦酸DOPO-HQ(简称PDPTP)以任意比例复配制得，且PDPTP、MCA、MPP、1240的重量分数均大于零。但考虑价格的降低和阻燃性能，推荐表1所表述的复配比例。表1为各组分占阻燃剂总重的百分比。
表1复合阻燃剂各配方配比表
Figure BSA00000658064900021
其中PDPTP的结构如下式所示：
Figure BSA00000658064900022
MCA的结构如下式所示：
Figure BSA00000658064900023
MPP的结构如下式所示：
Figure BSA00000658064900024
1240的结构如下式所示：
Figure BSA00000658064900031
如上所述本发明阻燃剂组合物的应用方法，其特征在于，该方法为：
在聚酯PET中分别加入不同比例的PDPTP和MCA或PDPTP和MPP，搅匀，熔融温度下注塑或挤出。
该方法还可以为：
在聚酯PBT中分别加入不同比例的PDPTP和MCA或PDPTP和MPP或PDPTP和1240，搅匀，熔融温度下注塑或挤出。
与现有技术相比，本发明的有益效果在于：
①本发明组分中的PDPTP是一个全新的化合物，为多芳环大分子含磷、硫双阻燃元素的化合物、与高分子材料有很好的相容性，易于分散，不析出，不降低材料的机械强度。
②本发明的阻燃剂不含有卤素，有利于环保，有很好的应用开发前景。
③本发明提供的阻燃剂组合物，含有磷、硫、氮或铝元素，可产生协效阻燃作用，对聚酯PET和PBT具有很好的阻燃效能。
④本发明提供的阻燃剂组合物的制备方法简单，设备投资少，可降低生产成本，应用方便。
具体实施方式
下面给出实施例以对本发明作进一步说明，为了对比复合阻燃剂的效果，也给出了单一组分PDPTP在聚酯中应用的实施例。但需指出的是以下实施例不能理解为对本发明保护范围的限制，本领域的技术熟练人员根据本发明的上述内容对本发明作出的一些非本质的改进和调整仍属于本发明的保护范围。
实施例1在聚酯PET中加入不同比例的PDPTP，搅拌均匀，用挤出机在熔融温度下挤出直径约3mm的样条，用HC900-2型氧指数测定仪测其氧指数，结果见表2。
表2阻燃剂PDPTP用量对PET氧指数的影响
  添加量％   0   10   15   20
  氧指数   21   27   28   29
实施例2在聚脂PET中加入不同比例的PDPTP和MCA，搅拌均匀，用挤出机在熔融温度下挤出直径约3mm的样条，用HC900-2型氧指数测定仪测其氧指数，结果见表3。
表3阻燃剂PDPTP和MCA用量对PET氧指数的影响
Figure BSA00000658064900041
实施例3在聚酯PET中加入不同比例的PDPTP和MPP，搅拌均匀，用挤出机在熔融温度下挤出直径约3mm的样条，用HC900-2型氧指数测定仪测其氧指数，结果见表4。
表4阻燃剂PDPTP和MPP用量对PET氧指数的影响
Figure BSA00000658064900042
实施例4在聚脂PBT中加入不同比例的PDPTP，搅拌均匀，用挤出机在熔融温度下挤出直径约3mm的样条，用HC900-2型氧指数测定仪测其氧指数，结果见表5。
表5阻燃剂PDPTP用量对PBT氧指数的影响
  添加量％   0   10   20   25
  氧指数   21   24   28   32
实施例5在聚酯PBT中加入不同比例的PDPTP和MCA，搅拌均匀，用挤出机在熔融温度下挤出直径约3mm的样条，用HC900-2型氧指数测定仪测其氧指数，结果见表6。
表6阻燃剂PDPTP和MCA用量对PBT氧指数的影响
Figure BSA00000658064900051
实施例6在聚酯PBT中加入不同比例的PDPTP和MPP，搅拌均匀，用挤出机在熔融温度下挤出直径约3mm的样条，用HC900-2型氧指数测定仪测其氧指数，结果见表7。
表7阻燃剂PDPTP和MPP用量对PBT氧指数的影响
Figure BSA00000658064900052
实施例7在聚酯PBT中加入不同比例的PDPTP和1240，搅拌均匀，用挤出机在熔融温度下挤出直径约3mm的样条，用HC900-2型氧指数测定仪测其氧指数，结果见表8。
表8阻燃剂PDPTP和1240用量对PBT氧指数的影响
Figure BSA00000658064900053

Claims (4)

1.一种聚酯用无卤阻燃剂组合物及其应用方法，其特征在于，它是由MCA、MPP和1240中的任意一种与PDPTP以任意比例复配制得。且PDPTP、MCA、MPP、1240的重量分数均大于零。
其中，PDPTP的结构如下式所示：
Figure FSA00000658064800011
MCA的结构如下式所示：
Figure FSA00000658064800012
MPP的结构如下式所示：
1240的结构如下式所示：
Figure FSA00000658064800014
2.根据权利要求1所述的聚酯为：聚对苯二甲酸乙二醇酯(PET)和聚对苯二甲酸丁二醇酯(PBT)。
3.根据权利要求1所述复合阻燃剂的应用方法为：在聚酯PET中分别加入不同比例的PDPTP和MCA或PDPTP和MPP，搅匀，熔融温度下注塑或挤出。
4.根据权利要求1所述复合阻燃剂的应用方法为：在聚酯PBT中分别加入不同比例的PDPTP和MCA或PDPTP和MPP或PDPTP和1240，搅匀，熔融温度下注塑或挤出。
CN201210011632.9A 2012-01-16 2012-01-16 一种聚酯用无卤阻燃剂组合物及其应用方法 Expired - Fee Related CN102585456B (zh)