CN102504219A - 超耐候型室外粉末涂料用聚酯树脂的制备方法 - Google Patents

超耐候型室外粉末涂料用聚酯树脂的制备方法 Download PDF

Info

Publication number
CN102504219A
CN102504219A CN201110314280XA CN201110314280A CN102504219A CN 102504219 A CN102504219 A CN 102504219A CN 201110314280X A CN201110314280X A CN 201110314280XA CN 201110314280 A CN201110314280 A CN 201110314280A CN 102504219 A CN102504219 A CN 102504219A
Authority
CN
China
Prior art keywords
polyester resin
powder coating
minutes
outdoor
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201110314280XA
Other languages
English (en)
Other versions
CN102504219B (zh
Inventor
张爱东
葛铁军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Xin Bao Polytron Technologies Inc
Original Assignee
YANGZHOU XINBAO RESIN CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YANGZHOU XINBAO RESIN CO Ltd filed Critical YANGZHOU XINBAO RESIN CO Ltd
Priority to CN 201110314280 priority Critical patent/CN102504219B/zh
Publication of CN102504219A publication Critical patent/CN102504219A/zh
Application granted granted Critical
Publication of CN102504219B publication Critical patent/CN102504219B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

超耐候型室外粉末涂料用聚酯树脂的制备方法，涉及室外粉末涂料生产技术领域，特别是生产涂料用的聚酯树脂的加工工艺技术领域。本发明主要由多元醇与多元酸缩合而成，通过反应生成水的去除而使酯化反应不断进行，从而获得一定聚合度的高分子聚酯树脂。将本发明方法生产的聚酯树脂用于生产室外粉末涂料，可使产品表面具有高光泽和优越的户外耐候性等优点，在耐人工气候老化性试验中，可达到1600h合格。

Description

超耐候型室外粉末涂料用聚酯树脂的制备方法
技术领域
本发明涉及室外粉末涂料生产技术领域，特别是生产涂料用的聚酯树脂的加工工艺技术领域。
背景技术
现有的采用聚酯树脂制成的粉末涂料用于室外使用的物件喷涂时，在自然条件下，一长般耐候性难以满足高标准要求，在耐人工气候老化性试验中，只能达到800h合格，无粉化、起泡、开裂、剥落等异常现象。
发明内容
本发明目的在于提出一种可用于生产耐候性强的室外粉末涂料的聚酯树脂的制备方法。
本发明包括以下步骤：
1）将反应釜温度升至80℃，然后投入新戊二醇、对苯二甲酸、三羟甲基丙烷和单丁基氧化锡；
2）将反应釜温度按2-3℃/15分钟升温速率升至240℃，在240℃下反应100～120分钟； 
3）投入间苯二甲酸后在240℃下反应120～180分钟；
4）在0.090～0.095mPa真空下进行缩聚反应180～240分钟；
5）将反应釜降温至180～200℃加入三苯基膦，反应30±2分钟出料，出料，取得聚酯树脂；
所述反应过程的各原料投料质量比为新戊二醇35～45份、三羟甲基丙烷1～3份、对苯二甲酸10～20份、间苯二甲酸50～70份、单丁基氧化锡0.2～0.5份、三苯基膦1～3份。
 本发明主要由多元醇与多元酸缩合而成，通过反应生成水的去除而使酯化反应不断进行，从而获得一定聚合度的高分子聚酯树脂。将本发明方法生产的聚酯树脂用于生产室外粉末涂料，可使产品表面具有高光泽和优越的户外耐候性等优点，在耐人工气候老化性试验中，可达到1600h合格。
具体实施方式
一、     称量（重量份）：
分别称取新戊二醇35～45份、三羟甲基丙烷1～3份、对苯二甲酸10～20份、间苯二甲酸50～70份、单丁基氧化锡0.2～0.5份、三苯基膦1～3份。
二、制备方法：
1、将反应釜温度升至80℃，然后投入新戊二醇、对苯二甲酸、三羟甲基丙烷和单丁基氧化锡；
2、将反应釜温度按2-3℃/15分钟升温速率升至240℃，在240℃下反应100～120分钟； 
3、检测反应釜中的树脂酸值达到标准后，投入间苯二甲酸后在240℃下反应120～180分钟；
4、检测树脂酸值达到标准后，在0.090～0.095mPa真空下进行缩聚反应180～240分钟；
5、检测树脂酸值达到标准后，将反应釜降温至180～200℃加入三苯基膦，反应30±2分钟出料，出料，取得聚酯树脂。
三、应用：
将本发明方法制成的聚酯树脂作为生产室外粉末涂料，再通过常规喷涂方法制作在工作表面，在耐人工气候老化性试验中，能达到1600h合格。

Claims (1)

1.超耐候型室外粉末涂料用聚酯树脂的制备方法，其特征在于包括以下步骤：
1）将反应釜温度升至80℃，然后投入新戊二醇、对苯二甲酸、三羟甲基丙烷和单丁基氧化锡；
2）将反应釜温度按2-3℃/15分钟升温速率升至240℃，在240℃下反应100～120分钟； 
3）投入间苯二甲酸后在240℃下反应120～180分钟；
4）在0.090～0.095mPa真空下进行缩聚反应180～240分钟；
5）将反应釜降温至180～200℃加入三苯基膦，反应30±2分钟出料，出料，取得聚酯树脂；
所述反应过程的各原料投料质量比为新戊二醇35～45份、三羟甲基丙烷1～3份、对苯二甲酸10～20份、间苯二甲酸50～70份、单丁基氧化锡0.2～0.5份、三苯基膦1～3份。
CN 201110314280 2011-10-17 2011-10-17 超耐候型室外粉末涂料用聚酯树脂的制备方法 Active CN102504219B (zh)