CN102503302A - High-strength ceramic tile tackiness agent - Google Patents
High-strength ceramic tile tackiness agent Download PDFInfo
- Publication number
- CN102503302A CN102503302A CN2011103320879A CN201110332087A CN102503302A CN 102503302 A CN102503302 A CN 102503302A CN 2011103320879 A CN2011103320879 A CN 2011103320879A CN 201110332087 A CN201110332087 A CN 201110332087A CN 102503302 A CN102503302 A CN 102503302A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- vinyl acetate
- orders
- rubber powder
- ordinary portland
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-strength ceramic tile tackiness agent, which comprises components, by weight, of 40.00%-50.00% of ordinary portland cement, 45.00%-55.00% of padding, 0.30%-0.60% of cellulose ether, 0.00%-8.00% of tackiness agent, 0.05%-0.50% of xylogen fiber, 0.10%-0.30% of thixotropic agent and 0.05%-0.20% of water reducing agent. The high-strength ceramic tile tackiness agent is characterized by being firm in bonding, free of tile falling, free of hollowing and the like for general bricks, and also has the characteristics for glass mosaic, the ceramic tile with large area or large weight.
Description
Technical field
The present invention relates to a kind of high strong type ceramic tile adhesive that is used for sticking brick.
Background technology
The annual newly constructed house floor area of building of China is more than 2,000,000,000 square meters, and the ratio of employing tile decorative surface is more than 50%.Therefore, ceramic tile has more and more become one of important architectural constructional materials.Traditional in the past sticking brick method is earlier ceramic tile to be soaked certain hour in water, and then ash concrete and sand are mixed into slurry by a certain percentage, from water, takes out ceramic tile; Slurry is applied to the ceramic tile back side; Paste thickness from the bottom up, pastes ceramic tile on the basic unit at 10mm～15mm.This traditional method still is passable for the bigger ceramic tile of water demand ratio.Along with social development, people require increasingly highly to ceramic tile, and the water regain of ceramic tile is more and more lower, and the method for traditional sticking brick such as then is easy to cause the ceramic tile hollowing, come off at phenomenon, very big potential safety hazard occurs.In order to stop the generation of this situation; Scholars have carried out particular study for the used material of sticking brick; With 28 days original tensile bond strengths of ceramic tile basically all about 1.5MPa, the tensile bond strength after immersion, thermal ageing or freeze-thaw cycle are handled is then about 0.7MPa.The material of this type sticking brick is commonly referred to as ceramic tile adhesive.This type ceramic tile adhesive satisfies C1 type index request among the industry standard JC/T 547-2005 " ceramic wall and floor bricks tackiness agent ", for common ceramic tile stickup or operable.Ceramic tile adhesive for more than the bigger ceramic tile of the bigger ceramic tile of glass Mosaic, area and weight ratio then not too can satisfy actual needs, the performance of ceramic tile adhesive need satisfy among the industry standard JC/T 547-2005 " ceramic wall and floor bricks tackiness agent " the C2 type require just suitable.
Summary of the invention
In order to solve above-mentioned deficiency of the prior art, the present invention provides high strong type ceramic tile adhesive.This high strong type ceramic tile adhesive not only has bonding firmly for common ceramic tile, does not fall brick, characteristics such as hollowing not, and have such characteristics too for glass Mosaic, ceramic tile or the bigger ceramic tile of weight ratio that area is bigger.
The present invention provides a kind of high strong type ceramic tile adhesive, and it comprises following component by weight percentage:
Ordinary Portland cement 40.00%-50.00%;
Filler 45.00%-55.00%;
Ether of cellulose 0.30%-0.60%;
Tackiness agent 3.00%-8.00%;
Lignin fibre 0.05%-0.50%;
Thixotropic agent 0.10%-0.30%;
Water reducer 0.05%-0.20%.
Said ordinary Portland cement is No. 42.5 ordinary Portland cements, 42.5R ordinary Portland cement or No. 52.5 ordinary Portland cements, said filler be in 40 orders～80 order silica sands, 80 orders～120 order silica sands, 40 orders～80 orders washing river sand and the 80 orders～120 orders washing river sand one or more.
Described ether of cellulose is hydroxyethylmethyl-cellulose ether or hydroxypropyl methyl cellulose ether, and viscosity is between 20000mPa.s～50000mPa.s.
Described tackiness agent is one or more in vinyl acetate and ethylene copolymer rubber powder, ethene and vinylchlorid and month silicic acid vinyl acetate terpolymer rubber powder, vinyl acetate and ethene and higher fatty acid vinyl acetate terpolymer rubber powder, vinyl acetate and higher fatty acid vinyl acetate copolymerization rubber powder, vinyl acetate and propenoate and higher fatty acid vinyl acetate terpolymer rubber powder or the vinylformic acid homopolymerization rubber powder.
Said lignin fibre is a wood fibre, and length is at 300 μ m～600 μ m.
Said thixotropic agent is a kind of in calcium-base bentonite thixotropic agent or the sodium bentonite thixotropic agent or two kinds, and said water reducer is a kind of in melamine high-efficiency water-reducing agent or the polycarboxylate water-reducer or two kinds.
Adopt high strong type ceramic tile adhesive provided by the invention not only to have bonding firmly, do not fall brick for common ceramic tile, characteristics such as hollowing not, and have such characteristics too for glass Mosaic, ceramic tile or the bigger ceramic tile of weight ratio that area is bigger.
Embodiment
For further setting forth the present invention, provide embodiment below and explain.
In the present invention; Said ordinary Portland cement is No. 42.5 ordinary Portland cements, 42.5R ordinary Portland cement and 52.5 ordinary Portland cements that Jidong Cement Co., Ltd., Tangshan provides, and said filler is 40 orders～80 order silica sands, 80 orders～120 order silica sands, 40 orders～80 orders washing river sand and 80 orders～120 orders washing river sand that Lingshou stone dam generation hall mining industry source mill provides.
Described ether of cellulose is hydroxyethylmethyl-cellulose ether and the hydroxypropyl methyl cellulose ether that Beijing Long Hu Science and Technology Ltd. provides, and viscosity is respectively at 35000mPa.s～45000mPa.s and 20000mPa.s～30000mPa.s.
Described tackiness agent is vinyl acetate and ethylene copolymer rubber powder and vinyl acetate, higher fatty acid vinyl acetate copolymerization rubber powder and ethene and vinylchlorid and month silicic acid vinyl acetate terpolymer rubber powder that Beijing Long Hu Science and Technology Ltd. provides.
Said thixotropic agent is the calcium-base bentonite thixotropic agent that Beijing Long Hu Science and Technology Ltd. provides, and said water reducer is the melamine high-efficiency water-reducing agent that Beijing Long Hu Science and Technology Ltd. provides.
Based on above-mentioned scope, the present invention provides first embodiment, and concrete weight (KG) proportioning of each component is following:
42.5 ordinary Portland cement 450;
40 orders～80 order silica sands 250;
80 orders～120 order silica sands 300;
Hydroxyethylmethyl-cellulose ether 5;
Vinyl acetate and ethylene copolymer rubber powder 40;
Lignin fibre 2;
Thixotropic agent 1;
Water reducer 2.
Based on above-mentioned scope, the present invention provides second embodiment, and the concrete weight proportion of each component is following:
42.5R ordinary Portland cement 500;
40 orders～80 orders washing river sand 200;
80 orders～120 orders washing river sand 250;
Hydroxypropyl methyl cellulose ether 5;
Vinyl acetate and higher fatty acid vinyl acetate copolymerization rubber powder 35;
Lignin fibre 5;
Thixotropic agent 3;
Water reducer 2.
Based on above-mentioned scope, the present invention provides the 3rd embodiment, and the concrete weight proportion of each component is following:
52.5 ordinary Portland cement 400;
80 orders～120 order silica sands 515;
Hydroxyethylmethyl-cellulose ether 3;
Ethene and vinylchlorid and month silicic acid vinyl acetate terpolymer rubber powder 80;
Lignin fibre 0.5;
Thixotropic agent 1;
Water reducer 0.5.
Based on above-mentioned scope, the present invention provides the 4th embodiment, and the concrete weight proportion of each component is following:
42.5 ordinary Portland cement 478;
40 orders～80 orders washing river sand 200;
80 orders～120 order silica sands 250;
Hydroxyethylmethyl-cellulose ether 6;
Vinyl acetate and ethylene copolymer rubber powder 60;
Lignin fibre 3;
Thixotropic agent 2;
Water reducer 1.
Based on above-mentioned scope, the present invention provides the 5th embodiment, and the concrete weight proportion of each component is following:
42.5 ordinary Portland cement 425;
40 orders～80 order silica sands 200;
80 orders～120 orders washing river sand 295;
Hydroxyethylmethyl-cellulose ether 4;
Ethene and vinylchlorid and month silicic acid vinyl acetate terpolymer rubber powder 70;
Lignin fibre 4;
Thixotropic agent 1;
Water reducer 1.
Based on above-mentioned scope, the present invention provides the 6th embodiment, and the concrete weight proportion of each component is following:
42.5R ordinary Portland cement 440;
40 orders～80 order silica sands 250;
80 orders～120 order silica sands 250;
Hydroxyethylmethyl-cellulose ether 4.5;
Vinyl acetate and higher fatty acid vinyl acetate copolymerization rubber powder 50;
Lignin fibre 3;
Thixotropic agent 1.5;
Water reducer 1.
The above-mentioned high strong type ceramic tile adhesive that the present invention provides detects by relevant regulations among the JC/T 547-2005 " ceramic wall and floor bricks tackiness agent ", and the specific examples detected result is following:
Table 1 instance one, two detected results
| Project | Instance one | Instance two |
| The stretching adhesive strength, MPa | 2.3 | 2.5 |
| Stretching adhesive strength after the immersion, MPa | 1.1 | 1.3 |
| Stretching adhesive strength after the thermal ageing, MPa | 2.7 | 2.9 |
| Stretching adhesive strength behind the freeze-thaw cycle, MPa | 1.2 | 1.5 |
| Open assembly time, 20min stretching adhesive strength, MPa | 1.6 | 2.0 |
Table 2 instance three, four detected results
| Project | Instance three | Instance four |
| The stretching adhesive strength, MPa | 2.3 | 1.8 |
| Stretching adhesive strength after the immersion, MPa | 1.2 | 1.0 |
| Stretching adhesive strength after the thermal ageing, MPa | 2.9 | 1.6 |
| Stretching adhesive strength behind the freeze-thaw cycle, MPa | 1.3 | 1.1 |
| Open assembly time, 20min stretching adhesive strength, MPa | 1.9 | 1.5 |
Table 3 instance five, six detected results
| Project | Instance five | Instance six |
| The stretching adhesive strength, MPa | 1.7 | 1.9 |
| Stretching adhesive strength after the immersion, MPa | 1.3 | 1.2 |
| Stretching adhesive strength after the thermal ageing, MPa | 1.7 | 1.6 |
| Stretching adhesive strength behind the freeze-thaw cycle, MPa | 1.5 | 1.4 |
| Open assembly time, 20min stretching adhesive strength, MPa | 1.4 | 1.6 |
Claims (6)
1. one kind high strong type ceramic tile adhesive is characterized in that: comprise following component by weight percentage:
Ordinary Portland cement 40.00%-50.00%;
Filler 45.00%-55.00%;
Ether of cellulose 0.30%-0.60%;
Tackiness agent 3.00%-8.00%;
Lignin fibre 0.05%-0.50%;
Thixotropic agent 0.10%-0.30%;
Water reducer 0.10%-0.20%.
2. a kind of high strong type ceramic tile adhesive according to claim 1; It is characterized in that: said ordinary Portland cement is No. 42.5 ordinary Portland cements, 42.5R ordinary Portland cement or No. 52.5 ordinary Portland cements, said filler be in 40 orders～80 order silica sands, 80 orders～120 order silica sands, 40 orders～80 orders washing river sand and the 80 orders～120 orders washing river sand one or more.
3. a kind of high strong type ceramic tile adhesive according to claim 1, it is characterized in that: described ether of cellulose is hydroxyethylmethyl-cellulose ether or hydroxypropyl methyl cellulose ether, and viscosity is between 20000mPa.s～50000mPa.s.
4. a kind of high strong type ceramic tile adhesive according to claim 1 is characterized in that: described tackiness agent is one or more in vinyl acetate and ethylene copolymer rubber powder, ethene and vinylchlorid and month silicic acid vinyl acetate terpolymer rubber powder, vinyl acetate and ethene and higher fatty acid vinyl acetate terpolymer rubber powder, vinyl acetate and higher fatty acid vinyl acetate copolymerization rubber powder, vinyl acetate and propenoate and higher fatty acid vinyl acetate terpolymer rubber powder or the vinylformic acid homopolymerization rubber powder.
5. a kind of high strong type ceramic tile adhesive according to claim 1, it is characterized in that: described lignin fibre is a wood fibre, length is at 300 μ m～600 μ m.
6. a kind of high strong type ceramic tile adhesive according to claim 1; It is characterized in that: said thixotropic agent is a kind of in calcium-base bentonite thixotropic agent or the sodium bentonite thixotropic agent or two kinds, and said water reducer is a kind of in melamine high-efficiency water-reducing agent or the polycarboxylate water-reducer or two kinds.