CN105016673A - Anti-falling cement-based glue for tiles for exterior wall - Google Patents
Anti-falling cement-based glue for tiles for exterior wall Download PDFInfo
- Publication number
- CN105016673A CN105016673A CN201510015077.0A CN201510015077A CN105016673A CN 105016673 A CN105016673 A CN 105016673A CN 201510015077 A CN201510015077 A CN 201510015077A CN 105016673 A CN105016673 A CN 105016673A
- Authority
- CN
- China
- Prior art keywords
- glue
- exterior wall
- tiles
- based glue
- cement based
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides anti-falling cement-based glue for tiles for an exterior wall. The glue is prepared from the following components in parts by weight: 40-50 parts of common silicate cement, 45-55 parts of fine aggregate, 3-8 parts of filler, 1-3 parts of redispersible powder, 0.2-1.0 part of cellulose ether, 0.2-0.8 part of a water reducer, 0.3-1.0 part of crack-resisting fiber, 0.05-0.25 part of an anti-sliding compound, 0.05-0.25 part of a porosity regulating compound, and 0.2-1.0 part of a set controlling compound. According to the anti-falling cement-based glue for tiles for the exterior wall provided by the invention, the anti-sliding falling performance of an adhesive for tiles is improved simultaneously from four aspects of improving the binding power, resisting shrinkage crack, resisting slippage and enhancing the weather resistance; the construction properties of the glue for tiles such as water retention, viscosity maintaining and the like can be remarkably improved, the original adhesive strength of the glue for tiles can be effectively enhanced, and the tensile bond strength of the glue for tiles if the glue for tiles is soaked in water, thermally aged and frozen and thawed can be improved to a great extent. The glue for tiles has good adaptability with other additives. The glue for tiles plays good roles of reducing water and increasing strength, reducing the cracking risk and optimizing the gap structure,
Description
Technical field
The invention belongs to building material field, particularly a kind of exterior wall peel type cement based glue for tile.
Background technology
Ceramic tile is as finishing material, and no matter in indoor or exterior finish, application all widely.In exterior wall finishing, adopt the way of bulk ceramic tile lifting decorative aesthetics more, especially apply more in medium-to-high grade public building.But along with developing rapidly of city, increasing of Highrise buildings, smashes automobile after the slippage of outdoor tile big area comes off, to injure the example of passerby by a crashing object also of common occurrence.
Outdoor tile slippage come off be on the one hand due to the area of China's exterior wall monolithic ceramic tile and weight increasing, the application as the heavy ceramic tile of 800 × 800mm on market is very general; Ceramic tile is more and more finer and close on the other hand, and water-intake rate is more and more lower.In traditional cementi method, sand and cement field mix are made simple sand-cement slurry, again this mortar is coated in the wetting ceramic tile back side, thereafter the ceramic tile scribbling mortar is pressed onto on surface of wall wetting in advance, finally raps ceramic tile to ensure that ceramic tile has consistent planeness.When this method pastes exterior wall low water absorption ceramic tile, easily cause ceramic tile hollowing, come off, construction quality is difficult to ensure.
In China, the application of novel ceramic tile bond is also in the starting stage, and the problem that the slippage of External Wall ceramic tile comes off is paid close attention to less.As ZL201110422942.5 proposes a kind of adhesive powder for ceramic tile, but because of Cost Problems, cohesive strength is obviously on the low side, is not suitable for the paving of outdoor tile.Though ZL20111.332087.9 proposes a kind of high-strength ceramic tile tackiness agent, though it has increased substantially the usage quantity of rubber powder, do not consider that the slippage at heavy brick paving initial stage under exterior wall environment comes off problem, application cost is also higher.
In general, also less to the research of the adhesive material of common tile laying at present, less to the come off bonding product of problem of solution outdoor tile slippage.Therefore, along with increasing of outdoor tile application in building trade, a kind of exterior wall peel type cement based glue for tile is researched and developed significant to the development promoting ceramic tile adhesive agent material.
Summary of the invention
Goal of the invention: in order to overcome above-mentioned the deficiencies in the prior art, the object of the present invention is to provide a kind of outdoor tile that is applicable under the environment that bonding initial stage, long-term immersion and the temperature difference are larger, continue the cement based glue for tile ensureing sticking strength, antiskid peel type.
Technical scheme: the invention provides a kind of exterior wall peel type cement based glue for tile, be made up of the component of following weight part:
As preferably, described ordinary Portland cement is No. 42.5 ordinary Portland cements or No. 52.5 ordinary Portland cements.
Preferred as another kind, described fine aggregate is 40 ~ 80 order quartz sands of mass ratio 1:1 ~ 3 and the mixing of 80 ~ 120 order quartz sands.
Preferred as another kind, described filler is dry powder, and its fineness is 400 ~ 800 orders.
Preferred as another kind, described redispersable latex powder is selected from vinyl acetate and ethylene copolymer rubber powder, vinyl acetate and higher aliphatic vinyl acetate copolymerization rubber powder, vinyl acetate, acrylate and higher aliphatic vinyl acetate terpolymer rubber powder, one or more in vinylformic acid homopolymerization rubber powder.
Preferred as another kind, described ether of cellulose is ethoxyl methyl cellulose ether or hydroxypropyl methyl cellulose ether, and its viscosity is between 100000mPa.s ~ 200000mPa.s.
Preferred as another kind, described water reducer is selected from one in melamine high-efficiency water-reducing agent and polycarboxylate water-reducer or two kinds.
Preferred as another kind, described anti-crack fiber is wood fibre, and its length is 300 μm ~ 800 μm.
Preferred as another kind, described resistant slide compound is the modification polyoxyethylene of mass ratio 1:1 ~ 3 and mixing of starch ethers.
Preferred as another kind, described hole regulating compound is the hydrophobic titanium dioxide silicon defoaming agent of mass ratio 1:3 ~ 4 and mixing of triterpenoid saponin air entrapment agent; It is calcium formiate that described tune coagulates compound.
The preparation method of described exterior wall peel type cement based glue for tile, comprises the following steps:
(1) all kinds of starting material up to specification are selected;
(2) by the weight percent of selected component, each starting material are weighed;
(3) load weighted each component is poured into stirrer, to the order not requirement that material is poured into; Stir 3 ~ 5 minutes, mix, to obtain final product.
The application method of described exterior wall peel type cement based glue for tile, comprises the following steps: in regulation ratio add water stir after can construct.
Beneficial effect: the present invention improves ceramic tile adhesive resistant slide simultaneously and to come off performance from raising cohesive force, resisted shrinkage cracking, resistant slide and lifting weathering resistance four aspect, can significantly improve the workabilities such as glue for tile water conservation, viscosity, the former intensity of bonding of effective lifting glue for tile, after glue for tile immersion can be increased substantially, thermal ageing and freeze thawing back draft cohesive strength and with other additives, there is good adaptability, the effect that this glue for tile has good water reducing and strength increasing, reduces cracking risk, optimizes gap structure.
Specifically, the present invention, relative to prior art, has following outstanding advantage:
(1) this glue for tile has the effect obviously strengthening ceramic tile resistant slide and come off.By mixing full-bodied ether of cellulose, resistant slide compound, the stability of glue for tile, intensity and uniformity coefficient effectively can be improved.Modification polyoxyethylene has high viscosity, water-soluble, thixotroping oilness, greatly can improve force of cohesion, the cohesive force of mortar, have good thickening, thixotropic effects, significantly enhances the resistant slide exfoliation ability of glue for tile.
(2) this glue for tile is under various exposed environments, has good tensile bond strength.By strictly controlling water cement ratio, the appropriate redispersable latex powder of admixture, high-performance water reducing agent, significantly improve glue for tile tensile bond strength.By the pore structure of hole regulating compound regulation and control slurry, adopt the means of drawing afterwards of first disappearing to optimize the gap structure of glue for tile, be conducive to strengthening its tensile bond strength under Different climate condition, improve the weather resistance of glue for tile significantly.
(3) this glue for tile has significant reducing and anti-cracking effect.Adopt snappiness and dispersed excellent wood fibre, can tridimensional network be formed after mixing, enhance anchorage force and the resisting power of system; Decrease Early self-shrinkage, certain restraining effect can be played to syphon hollowing.
Embodiment
Below in conjunction with embodiment, further illustrate the present invention.
In embodiment:
Fine aggregate is the mixing by extra fine quality ratio of 40 ~ 80 order quartz sands and 80 ~ 120 order quartz sands, and wherein, embodiment 1 to 5 is 40 ~ 80 order quartz sands of mass ratio 1:1 and the mixing of 80 ~ 120 order quartz sands; Embodiment 6 is 40 ~ 80 order quartz sands of mass ratio 1:3 and the mixing of 80 ~ 120 order quartz sands.
Ether of cellulose is Shandong Teng one novel material company limited hydroxypropyl methyl cellulose ether, and wherein, the viscosity of cellulose ether of embodiment 1 to 4 is 150000mPa.s; The viscosity of cellulose ether of embodiment 5 is 100000mPa.s; The viscosity of cellulose ether of embodiment 6 is 200000mPa.s.
Embodiment 1
Exterior wall peel type cement based glue for tile, is mixed by the component of following weight part:
Wherein, filler is dry powder, and fineness is 400 orders; Re-dispersible glue powder is that Wa Ke company produces 5010N vinyl acetate between to for plastic/ethylene type copolymerization rubber powder; Water reducer adopts Jiangsu Su Bote limited-liability company PCA-100P high-performance polycarboxylic acids water reducing agent; The length of wood fibre is 300 μm; Resistant slide compound is the modification polyoxyethylene of mass ratio 1:1 and mixing of starch ethers; Hole regulating compound is the German MUNZING-CHEMIE company P801 defoamer of mass ratio 1:3 and mixing of Changsha Li Qin novel material company limited CorMix 8123 air entrapment agent.
Embodiment 2
Exterior wall peel type cement based glue for tile, is mixed by the component of following weight part:
Wherein, filler is dry powder, and fineness is 400 orders; Re-dispersible glue powder is that Wa Ke company produces 5010N vinyl acetate between to for plastic/ethylene type copolymerization rubber powder; Water reducer adopts Jiangsu Su Bote limited-liability company FF55 melamine high-efficiency water-reducing agent; The length of wood fibre is 300 μm; Resistant slide compound is the modification polyoxyethylene of mass ratio 1:1 and mixing of starch ethers; Hole regulating compound is the employing Germany MUNZING-CHEMIE company P801 defoamer of mass ratio 1:3 and mixing of Changsha Li Qin novel material company limited CorMix 8123 air entrapment agent.
Embodiment 3
Exterior wall peel type cement based glue for tile, is mixed by the component of following weight part:
Wherein, filler is dry powder, and fineness is 400 orders; Re-dispersible glue powder is that Wa Ke company produces 8031 vinyl acetates/higher aliphatic vinyl acetate type copolymerization rubber powder; Water reducer adopts Jiangsu Su Bote limited-liability company PCA-100P high-performance polycarboxylic acids water reducing agent; The length of wood fibre is 300 μm; Resistant slide compound is the modification polyoxyethylene of mass ratio 1:3 and mixing of starch ethers; Hole regulating compound is the German MUNZING-CHEMIE company P801 defoamer of mass ratio 1:4 and mixing of Changsha Li Qin novel material company limited CorMix 8123 air entrapment agent.
Embodiment 4
Exterior wall peel type cement based glue for tile, is mixed by the component of following weight part:
Wherein, filler is dry powder, and fineness is 800 orders; Re-dispersible glue powder is that Wa Ke company produces 8034 ethylene acetate/acrylic acid esters/higher aliphatic vinyl acetate terpolymer rubber powder; Water reducer adopts Jiangsu Su Bote limited-liability company PCA-100P high-performance polycarboxylic acids water reducing agent; The length of wood fibre is 800 μm; Resistant slide compound is the modification polyoxyethylene of mass ratio 1:3 and mixing of starch ethers; Hole regulating compound is the German MUNZING-CHEMIE company P801 defoamer of mass ratio 1:4 and mixing of Changsha Li Qin novel material company limited CorMix 8123 air entrapment agent.
Embodiment 5
Exterior wall peel type cement based glue for tile, is mixed by the component of following weight part:
Wherein, filler is dry powder, and fineness is 800 orders; Re-dispersible glue powder is that Wa Ke company produces 5010N vinyl acetate between to for plastic/ethylene type copolymerization rubber powder; Water reducer adopts Jiangsu Su Bote limited-liability company PCA-100P high-performance polycarboxylic acids water reducing agent; The length of wood fibre is 800 μm; Resistant slide compound is the modification polyoxyethylene of mass ratio 1:3 and mixing of starch ethers; Hole regulating compound is the German MUNZING-CHEMIE company P801 defoamer of mass ratio 1:4 and mixing of Changsha Li Qin novel material company limited CorMix 8123 air entrapment agent.
Embodiment 6
Exterior wall peel type cement based glue for tile, is mixed by the component of following weight part:
Wherein, filler is dry powder, and fineness is 800 orders; Re-dispersible glue powder is that Wa Ke company produces 5010N vinyl acetate between to for plastic/ethylene type copolymerization rubber powder; Water reducer adopts Jiangsu Su Bote limited-liability company PCA-100P high-performance polycarboxylic acids water reducing agent; The length of wood fibre is 800 μm; Resistant slide compound is the modification polyoxyethylene of mass ratio 1:3 and mixing of starch ethers; Hole regulating compound is the German MUNZING-CHEMIE company P801 defoamer of mass ratio 1:3.5 and mixing of Changsha Li Qin novel material company limited CorMix 8123 air entrapment agent.
The exterior wall peel type cement based glue for tile obtained by embodiment 1 ~ 6, carry out the tensile bond strength after the former intensity of ceramic tile adhesive stretch-bonded, immersion, thermal ageing, freeze-thaw cycle and slippage simultaneous test, the requirement that its testing method installs JC/T547-2005 " ceramic wall and floor bricks tackiness agent " measures.Test-results is in table 1.
Table 1 ceramic tile adhesive cohesive strength test result
Table 1 data show: adopt exterior wall peel type cement based glue for tile of the present invention can effectively reduce ceramic tile slippage, and all have higher stretching adhesive strength under a variety of experimental conditions.
Claims (10)
1. an exterior wall peel type cement based glue for tile, is characterized in that: be made up of the component of following weight part:
2. a kind of exterior wall peel type cement based glue for tile according to claim 1, is characterized in that: described ordinary Portland cement is No. 42.5 ordinary Portland cements or No. 52.5 ordinary Portland cements.
3. a kind of exterior wall peel type cement based glue for tile according to claim 1, is characterized in that: described fine aggregate is 40 ~ 80 order quartz sands of mass ratio 1:1 ~ 3 and the mixing of 80 ~ 120 order quartz sands.
4. a kind of exterior wall peel type cement based glue for tile according to claim 1, it is characterized in that: described filler is dry powder, its fineness is 400 ~ 800 orders.
5. a kind of exterior wall peel type cement based glue for tile according to claim 1, it is characterized in that: described redispersable latex powder is selected from vinyl acetate and ethylene copolymer rubber powder, vinyl acetate and higher aliphatic vinyl acetate copolymerization rubber powder, vinyl acetate, acrylate and higher aliphatic vinyl acetate terpolymer rubber powder, one or more in vinylformic acid homopolymerization rubber powder.
6. a kind of exterior wall peel type cement based glue for tile according to claim 1, is characterized in that: described ether of cellulose is ethoxyl methyl cellulose ether or hydroxypropyl methyl cellulose ether, and its viscosity is between 100000mPa.s ~ 200000mPa.s.
7. a kind of exterior wall peel type cement based glue for tile according to claim 1, is characterized in that: described water reducer is selected from one in melamine high-efficiency water-reducing agent and polycarboxylate water-reducer or two kinds.
8. a kind of exterior wall peel type cement based glue for tile according to claim 1, it is characterized in that: described anti-crack fiber is wood fibre, its length is 300m ~ 800m.
9. a kind of exterior wall peel type cement based glue for tile according to claim 1, is characterized in that: described resistant slide compound is the modification polyoxyethylene of mass ratio 1:1 ~ 3 and mixing of starch ethers.
10. a kind of exterior wall peel type cement based glue for tile according to claim 1, is characterized in that: described hole regulating compound is the hydrophobic titanium dioxide silicon defoaming agent of mass ratio 1:3 ~ 4 and mixing of triterpenoid saponin air entrapment agent; It is calcium formiate that described tune coagulates compound.